Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (12)
- Beitrag zu einem Tagungsband (10)
- Beitrag zu einem Sammelband (8)
- Vortrag (2)
Sprache
- Englisch (32) (entfernen)
Schlagworte
- Ductile cast iron (4)
- Dynamic crack resistance curve (3)
- Fracture mechanics (3)
- Bruchmechanik (2)
- Fatigue (2)
- Fatigue crack propagation (2)
- Finite element analysis (2)
- Key curve (2)
- Microstructure (2)
- Railway axles (2)
Eingeladener Vortrag
- nein (2)
Fatigue testing in the VHCF ränge requires testing machines with increased frequencies. However, application of energy-saving resonance testing leads to a linkage between test frequency and specimen Parameters. The frequency ränge and the available forces of the testing machine are limiting possible specimen dimensions.
Electrodynamic shakers combine test frequencies up to 4000 Hz with forces in the kN range. Thus, a relatively wide range of tests is possible which allows studying the influence of specimen size on VHCF behaviour.
Electrodynamic shakers as well as the respective Computer control Systems and Vibration measurement techniques are well established in scientific and technical applications. We present results of a first study of VHCF testing on electrodynamic shakers conducted at BAM. Test frequency, specimen size and stress levels have been varied. One goal is to balance the needs of materials testing with the Standard test Systems of environmental Simulation to provide a powerful and flexible tool for very high cycle fatigue testing. Further investigation to optimize the technique is required.
Dynamic fracture mechanics characteristics are required for design and safety proof of advanced
ductile cast iron (DCI) components. In this paper, the analytical compliance ratio
(CR) and numerical finite element (FE) key curve methods were investigated for dynamic Rcurve
testing. Two DCI materials, a purely ferritic and a ferritic one with 18 % of pearlite,
were tested at room temperature (RT) and -40 °C. The special focus is on the impact of the
materials damage and fracture behaviour on performance and limitations of the investigated
methods.
Systematic metallographic and fractographic microstructural analyses were performed accompanying
the test program. Summarizing systematics of the specific damage behaviour
and fracture mechanisms were developed taking microstructure, loading rate, specimen geometry
and test temperature into account.
There has been a change from ductile to brittle fracture mechanism observed at -40 °C with
ferritic DCI and even at RT with ferritic-pearlitic DCI. The ferritic-pearlitic DCI did not show Rcurve
behaviour at -40 °C and only single Juc values could be determined. Furthermore, with
ferritic-pearlitic DCI, random pearlite shares in the ligament caused the relation between
loading rate, force-deflection record and crack extension not to remain uniquely defined.
Therefore, the FE key curve method proofed not to be applicable since the FE model was
based on homogeneous isotropic material and ductile failure mode only. The analytical CR
key curve method worked well only with selected combinations of microstructure, specimen
geometry and temperature.
In summary it has to be concluded that a robust, accurate and sufficiently simple dynamic
key curve method that was suited for application in quality control of industrial relevant DCI
qualities cannot be provided currently.
A two-dimensional analysis of the Charpy V-notch specimen subjected to impact loading, according to the standard DIN EN 10045-1, is carried out, using a transient explicit dynamic finite element program. An elastic-viscoplastic, temperature dependent, constitutive relation for a porous plastic solid based on the Gurson damage model is developed. Ductile fracture of the matrix material will be described by the nucleation and subsequent growth of voids to coalescence. An updated Lagrange–Jaumann formulation is employed accounting for large strain and rotation. The discretization is based on four-node plane strain solid elements with one Gauss point. The equations of motion are integrated numerically by an explicit integration algorithm utilising a lumped mass matrix. The predictions of the numerical analysis in terms of force deflection response, crack resistance behaviour and deformation energy absorbtion are compared with results from Charpy tests which were carried out according to the low-blow technique.
The safety assessment of railway axles is based on a two-stage approach: fatigue strength design and regular inspections which, in terms of a general safety philosophy refer to safe-life and damage tolerance concepts. Starting with a recent failure case, a broken axle of a German high speed train, a discussion is presented on issues of both safety levels. These include ideas for finite life design, the treatment of in-service effects on the fatigue strength due to flying ballast damage and corrosion pits, the effect of corrosion on fatigue crack initiation and propagation, potential effects of non-metallic inclusions in steels, the way to detect them by quality control measures and reliability aspects of non-destructive testing with respect to the detection of fatigue cracks. Proposals are made how the safety level could be further improved.
On July 9, 2008 a high speed train derailed in Cologne main Station, Germany at a low speed because an axle was broken. Fortunately, the derailment happened at a low speed so that nobody was injured. The reason for the broken axle was investigated and it turned out that most likely large inclusions located shortly undemeath the surface in a T-transition were the origin of the final crack. Basing on that result, a systematic investigation on existing safety assessments of railway axles was performed. This results in an analysis of the production process of axles and in a critical review of existing of existing assessments. Improvements and future developments are outlined.
The paper gives an overview on safe life and damage tolerance methods applied to railway axles. It describes failure scenarios due to fatigue crack initiation and propagation. Besides common aspects of design, specific features such as corrosion and impact damage from flying ballast are discussed which may reduce the fatigue strength of axles during service. Potential effects of non-metallic inclusions from the steel manufacturing process are addressed in the context of the very high number of loading cycles railway axles are designed for. With respect to damage tolerance general lines of fracture mechanics residual lifetime analyses are introduced. More specific discussion is provided on aspects such as the threshold value of fatigue crack propagation and reliability aspects of non-destructive inspection.
Welding is one of the most common methods in industrial practice for joining components. Its main advantages are high speed in manufacturing combined with low costs and, usually, a high degree of flexibility, integrity and reliability. Nevertheless, welding is a highly complex metallurgical process and, therefore, weldments are susceptible to material discontinuities, flaws and residual stresses which may lead to structural failure and life time reduction. As a consequence weldments are an important field of fracture mechanics methods although its application is more complex than for homogeneous or non-welded structures. The aim of the paper is to provide an overview on the current state of fracture mechanics application to weldments. It starts by discussing the specific features which any fracture mechanics analysis of weldments has to take into account. Then, the experimental determination of fracture toughness, fatigue crack propagation and tensile properties of weldments is addressed. Finally, the analytical determination of the crack driving force in components and structural integrity assessment approaches for weldments are presented.