Filtern
Dokumenttyp
- Beitrag zu einem Tagungsband (13)
- Vortrag (6)
- Zeitschriftenartikel (4)
- Forschungsdatensatz (2)
- Dissertation (1)
- Posterpräsentation (1)
Schlagworte
- Laminography (5)
- Brennfleckmessung (4)
- Non-destructive testing (4)
- Photon counting detectors (4)
- Radiography (4)
- Carbon fiber reinforced polymers (3)
- Computed tomography (3)
- Dual-energy (3)
- Normung (3)
- Photon counting detector (3)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (6)
Im Rahmen des EMPIR-Projektes NanoXSpot (Nanometre X-Ray Focal Spot Measurement) werden rückführbare Messverfahren zur Bestimmung der Brennfleckgröße und -form von Röntgenröhren mit Submikrometerauflösung (100 nm – 20 µm) entwickelt, die die Grundlage für die Erarbeitung eines Standardentwurfes bilden. Der Standardentwurf wird bei CEN TC 138 (Non-destructive testing) WG 1 (Radiographic testing) eingereicht und mit ISO und ASTM harmonisiert. Zur Untersuchung der entwickelten Methoden (Brennfleck-CT, Fit-Prozedur für Strichgruppenkörper) und des im Projekt NanoXSpot neu entworfenen Testkörpers, NxS, wurde ein Ringversuch durchgeführt. Dabei wurde sowohl der angestrebte Überlappungsbereich mit EN 12543 Teil 5 (Messung der effektiven Brennfleckgröße von Mini- und Mikrofokus-Röntgenröhren) und ASTM E 2903 (Standard Test Method for Measurement of the Effective Focal Spot Size of Mini and Micro Focus X-ray Tubes) für Brennflecke >5 µm als auch Brennflecke <5 µm untersucht. Im Mittelpunkt standen dabei Stabilität und Wiederholbarkeit der entwickelten Methoden zur Bestimmung der Brennfleckgröße. In diesem Beitrag werden die Ergebnisse des durchgeführten Ringversuches vorgestellt und diskutiert, um Schlussfolgerungen und Empfehlungen für die Vorbereitung eines erweiterten Ringversuchs mit Partnern und Stakeholdern abzuleiten.
The objective of this work is to find a method that describes the degree of damage from an impact experiment. This experiment was performed on Composite Pressure Vessels (CPV) in order to find the correlation of impact damage to the residual burst pressure. Computed Tomography (CT) approach was used to capture the before and after impact condition of the CPVs. The Wasserstein function was used to calculate how much the after impact image has differed from the original one. In the end, a good correlation was obtained to the residual burst pressure.
Defect recognition in CFRP components using various NDT methods within a smart manufacturing process
(2018)
The manufacturing process of carbon fiber reinforced polymer (CFRP) components is gaining a more and more significant role when looking at the increasing amount of CFRPs used in industries today. The monitoring of the manufacturing process and hence the reliability of the manufactured products, is one of the major challenges we need to face in the near future. Common defects which arise during manufacturing process are e.g. porosity and voids which may lead to delaminations during operation and under load. To find irregularities and classify them as possible defects in an early stage of the manufacturing process is of high importance for the safety and reliability of the finished products, as well as of significant impact from an economical point of view. In this study we compare various NDT methods which were applied to similar CFRP laminate samples in order to detect and characterize regions of defective volume. Besides ultrasound, thermography and eddy current, different X-ray methods like radiography, laminography and computed tomography are used to investigate the samples. These methods are compared with the intention to evaluate their capability to reliably detect and characterize defective volume. Beyond the detection and evaluation of defects, we also investigate possibilities to combine various NDT methods within a smart manufacturing process in which the decision which method shall be applied is inherent within the process. Is it possible to design an in-line or at-line testing process which can recognize defects reliably and reduce testing time and costs? This study aims to show up opportunities of designing a smart NDT process synchronized to the production based on the concepts of smart production (Industry 4.0). A set of defective CFRP laminate samples and different NDT methods were used to demonstrate how effective defects are recognized and how communication between interconnected NDT sensors and the manufacturing process could be organized.
Photon counting detectors (PCD) offer new possibilities for x-ray micro computed tomography (CT) in the field of non-destructive testing. For large and/or dense objects with high atomic numbers the problem of scattered radiation and beam hardening severely influences the image quality. This work shows that using an energy discriminating PCD based on CdTe allows to address these problems by intrinsically reducing both the influence of scattering and beam hardening.
Based on 2D-radiographic measurements it is shown that by energy thresholding the influence of scattered radiation can be reduced by up to in case of a PCD compared to a conventional energy-integrating detector (EID).
To demonstrate the capabilities of a PCD in reducing beam hardening, cupping artefacts are analyzed quantitatively. The PCD results show that the higher the energy threshold is set, the lower the cupping effect emerges. But since numerous beam hardening correction algorithms exist, the results of the PCD are compared to EID results corrected by common techniques. Nevertheless, the highest energy thresholds yield lower cupping artefacts than any of the applied correction algorithms.
As an example of a potential industrial CT application, a turbine blade is investigated by CT. The inner structure of the turbine blade allows for comparing the image quality between PCD and EID in terms of absolute contrast, as well as normalized signal-to-noise and contrast-to-noise ratio. Where the absolute contrast can be improved by raising the energy thresholds of the PCD, it is found that due to lower statistics the normalized contrast-to-noise-ratio could not be improved compared to the EID. These results might change to the contrary when discarding pre-filtering of the x-ray spectra and thus allowing more low-energy photons to reach the detectors.
Despite still being in the early phase in technological progress, PCDs already allow to improve CT image quality compared to conventional detectors in terms of scatter and beam hardening reduction.
A composite material is a combination of two or more materials with very different mechanical, thermal and electrical properties. The various forms of composite materials, due to their high material properties, are widely used as structural materials in the aviation, space, marine, automobile, and sports industries. However, some defects like voids, delamination, or inhomogeneous fiber distribution that form during the fabricating processes of composites can seriously affect the mechanical properties of the composite material. In this study, several imaging NDE techniques such as: thermography, high frequency eddy current, ultrasonic, x-ray radiography, x-ray laminography, and high resolution x-ray CT were conducted to characterize the microstructure of carbon fiber composites. Then, a 3D analysis was implemented by the destructive technique of serial sectioning for the same sample tested by the NDE methods. To better analyze the results of this work and extract a clear volume image for all features and defects contained in the composite material, an intensive comparison was conducted among hundreds of 3D-NDE and multi serial sections’ scan images showing the microstructure variation.
The progress in X-ray detector electronics (sensitivity and speed) allows meanwhile fast single photon detection by a matrix detector. Combined photon counting and energy discrimination is implemented in the electronic circuit of each detector pixel. The company XCounter developed detectors based on CdTe single crystals, which can be tiled to larger areas and have a pixel size of 100ìm. The largest area available in beginning of 2014 is 50x75 mm². These detectors have very promising properties, which make them very suitable for NDT applications:
1. A CdTe attenuation layer of 750 µm thickness allows efficient X-ray detection up to ca. 300 keV. In counting mode only photon noise is important; no other detector noise sources need to be considered. There is no Offset signal without radiation.
2. Each of the detector pixels has two energy thresholds. These can be used for dual energy imaging for materials separation. Also the suppression of scattered radiation by energy thresholding will improve the image contrast sensitivity. First experiments will be presented which demonstrate the advantages of this new detector technology over the conventional charge integrating detectors.
A challenge is the development of a modified detector calibration procedure, which becomes critical at longer exposure times.
Eigenschaften und Einsatzgebiete photonenzählender und energieauflösender Röntgenmatrixdetektoren
(2015)
The new standard ‘ISO 17636-2:2013: Non-destructive testing of welds — Radiographic testing — Part 2: X- and gamma-ray techniques with digital detectors’, defines the practice for radiographic inspection of welded pipes for manufacturing and in-service inspection. It is applied in Europe for inspections of pipe welds in nuclear power plants as well as in chemical plants and allows a faster inspection with digital detector arrays (DDA) than with film. Nevertheless, it does not allow the evaluation of the depth and shape of volumetric and planar indications. In 2001 a planar tomography scanner, TomoCAR, was introduced for mechanized radiographic testing (RT) inspection and non-destructive measurement of cross sections. The project TomoWELD is based on a new concept of the scan geometry, an enhanced GPU based reconstruction, and the application of a new generation of photon counting DDAs based on CdTe crystal CMOS hybrids. The new detector permits the selection of energy thresholds to obtain an optimum energy range and reduction of the influence of scattered radiation. The concept and first measurements are presented. Flaw depth and shape of volumetric and planar irregularities can be determined.
Since a few years the direct detection of X-ray photons into electrical signals is possible by usage of highly absorbing photo conducting materials (e.g. CdTe) as detection layer of an underlying CMOS semiconductor X-ray detector. Even NDT energies up to 400 keV are possible today, as well. The image sharpness and absorption efficiency is improved by the replacement of the unsharp scintillation layer (as used at indirect detecting detectors) by a photo conducting layer of much higher thickness. If the read-out speed is high enough (ca. 50 – 100 ns dead time) single X-ray photons can be counted and their energy measured. Read-out noise and dark image correction can be avoided. By setting energy thresholds selected energy ranges of the X-ray spectrum can be detected or suppressed. This allows material discrimination by dual-energy techniques or the reduction of image contributions of scattered radiation, which results in an enhanced contrast sensitivity. To use these advantages in an effective way, a special calibration procedure has to be developed, which considers also time dependent processes in the detection layer. This contribution presents some of these new properties of direct detecting digital detector arrays (DDAs) and shows first results on testing fiber reinforced composites as well as first approaches to dual energy imaging.