Filtern
Dokumenttyp
- Vortrag (17)
- Beitrag zu einem Tagungsband (11)
- Zeitschriftenartikel (6)
- Posterpräsentation (6)
- Forschungsbericht (1)
Schlagworte
- Coarsening (21)
- Degradation (17)
- S-phase (14)
- Alloy 2618A (13)
- Microstructure (13)
- Transmission electron microscopy (12)
- Dark-field transmission electron microscopy (DFTEM) (10)
- Aluminium (9)
- Creep (5)
- Dark-field transmission electron microscopy (5)
- Aluminium alloys (4)
- S-Phase (4)
- 2618A (3)
- Aging (3)
- Aluminium alloy 2618A (3)
- TEM (3)
- Volume fraction (3)
- Al-Cu-Li alloys (2)
- Aluminum (2)
- Aluminum alloy (2)
- Digital material representation (2)
- Material degradation (2)
- Ostwald ripening (2)
- Alloy 2818A (1)
- Alterung (1)
- Aluminium alloy (1)
- Aluminiumlegierung (1)
- Aluminum alloys (1)
- Brinell hardness (1)
- Calibration (1)
- Centrifugal compressor wheel (1)
- Chemo-mechanical coupling (1)
- Damage (1)
- Dark-field transmission electron miscoscopy (1)
- Data storage (1)
- Differential scanning calorimetry (DSC) (1)
- Dislocations (1)
- EN AW-2618A (1)
- Electron microscopy (1)
- FIB Tomography (1)
- Grain Boundary Corrosion (1)
- Hardness (1)
- Internal Sulfidation (1)
- Lebensdauervorhersage (1)
- Lifetime prediction (1)
- Long-term aging (1)
- Materials science (1)
- Mikrostruktur (1)
- Phase-field simulation (1)
- Reheating (1)
- Schädigung (1)
- Transmission electron microscopy (TEM) (1)
- coarsening (1)
- hardness (1)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (17)
The article covers data on the Brinell hardness of the forged precipitation-hardened aluminum alloy EN AW-2618A in the initial T61 condition (i. e. slightly underaged) and after isothermal aging for up to 25,0 0 0 h at aging temperatures between 160 °C and 350 °C. In addition, the hardness was determined on specimens after creep testing at 190 °C and various stresses. The hardness decreases with increasing ag- ing time due to the microstructural evolution of the harden- ing precipitates. The drop occurs faster the higher the aging temperature. Aging under creep load additionally accelerates the hardness decrease.
Aluminiumlegierungen mit besonders hoher Festigkeit werden vor allem in der Luft- und Raumfahrt sowie der Automobilindustrie eingesetzt. Ein Anwendungsbeispiel im Fahrzeugbereich sind Radialverdichterräder von Abgasturboladern. Der hierfür untersuchte Werkstoff ist die Legierung 2618A. Die hohe Festigkeit wird durch Ausscheidungshärtung erreicht. Es scheiden sich hierbei durch eine entsprechende Wärmebehandlung Al-Cu-Mg-Teilchen in die Aluminium-Matrix aus. Diese Teilchen stellen Hindernisse für die Bewegung von Versetzungen dar und haben im Fall der Legierung 2618A stabförmige Geometrie. Durch Einsatz bei Betriebstemperatur von etwa 160 °C bis 190 °C vergröbern die Teilchen im Verlauf der Einsatzzeit (Ostwaldreifung) und die Festigkeit nimmt ab.
Der Zwischenbericht soll einen Überblick über die bisherigen experimentellen und theoretischen Ergebnisse geben. Es konnten Brinell-Härteverläufe nach Auslagerung bei 160 °C, 180 °C und 190 °C bis 8.760 h Auslagerungszeit gemessen werden. Erste TEM (Transmissionselektronenmikroskopie )-Untersuchungen der Mikrostruktur liegen vor. Anhand dieser Untersuchungen wurden erste Simulationen und Berechnungen der AI-Cu-Mg-Teilchengrößenentwicklung (Vergröberung) durchgeführt. Auswirkungen dieser Vergröberung der AlCu-Mg-Teilchen auf die Fließgrenze bei Raumtemperatur wurden berechnet. Weitere Ergebnisse sind Kriechversuche an Proben im Ausgangszustand T61 der Legierung 2618A bei den Temperaturen 160 °C, 180 °C und 190 °C. Um das zyklische visko-plastische Verhalten des Werkstoffes und den Einfluss der Alterung zu untersuchen, wurden LCF-Ermüdungsversuche an verschiedenen Auslagerungszuständen durchgeführt.
The aluminium alloy 2618A is an Al-Cu-Mg alloy which is part of the 2xxx series of age-hardenable alloys. These materials are designed for long-term Operation in transportation and aerospace industries. The desired properties, e.g. creep behavior, hardness, and damage tolerance, are controlled by the distribution of fine precipitates formed within the matrix. However, the strength of the material declines du ring exposition to elevated temperatures due to the overageing of the S-phase precipitates (AI2CuMg) and the conversion of the S-phase into the stable equilibrium S-phase. A quantitative model of the overageing process at application relevant temperatures would be desirable for accurate predictions of component lifetime made from the 2618A alloy.
In diesem Forschungsvorhaben wurde ein Verfahren entwickelt, um die Genauigkeit der Lebensdauerbewertung für Abgasturbolader (ATL)-Verdichterräder aus der ausscheidungs-härtbaren Aluminiumlegierung EN AW-2618A zu verbessern. Dies umfasst insbesondere die Berücksichtigung der Werkstoffalterung, mit der beim Einsatz dieser Bauteile unter entsprechender Betriebsbeanspruchung (Temperatur, Zeit, Spannung) gerechnet werden muss. Zunächst wurde eine solide experimentelle Datenbasis für den untersuchten Werkstoff geschaffen. Dies umfasste sowohl eine mechanische als auch eine mikrostrukturelle Charakterisierung des Ausgangszustands (T61) sowie von ausgelagerten Zuständen bis zu 25.000 h bei betriebsrelevanten Temperaturen (160 °C, 180 °C, 190 °C). Bei den Untersuchungen zur Mikrostruktur wurde der Fokus auf die Entwicklung der Radien der stäbchen-förmigen aushärtenden Phase gelegt, die während der Alterung vergröbern. Der Zusammenhang zwischen Auslagerungstemperatur, -zeit und ggfs. mechanischer Belastung wurde erstmals in diesem Umfang quantifiziert und entsprechende Gesetzmäßigkeiten zur Beschreibung der Vergröberung ermittelt. Vergleichend dazu wurde der Einfluss der Alterung auf die Härte, die Festigkeit, das Kriechverhalten und die Ermüdungslebensdauer (LCF, TMF) bestimmt, so dass eine Korrelation zur Mikrostruktur vorliegt.
Die Ergebnisse der Kriechversuche wurden zur Kalibrierung eines modifizierten Sinus-hyperbolicus-Kriechmodells verwendet. Ein zeit- und temperaturabhängiges Verformungsmodell nach Chaboche, welches die wesentlichen Phänomene der Hochtemperaturverformung und der Wechselplastizität beschreibt, wurde erweitert und berücksichtigt nun die Werkstoffalterung, indem die Festigkeit nicht nur als Funktion der Temperatur, sondern auch des Alterungszustands (d. h. des mittleren Radius der Ausscheidungen) dargestellt wird. Für die Erweiterung des Modells zur Bewertung der Ermüdungslebensdauer wurde analog verfahren. Die berechnete Lebensdauer der im Verlauf des Vorhabens durchgeführten LCF- und TMF-Versuche stimmt gut mit den experimentellen Ergebnissen überein. Lediglich ein LCF-Versuch mit einer Haltezeit von 900 s im Zug weicht deutlich vom Mittelwert ab und zeigt die Grenzen des zeitunabhängigen Schädigungsmodells auf. Versuche mit kürzeren Haltezeiten bis zu 60 s liegen im Streuband, ebenso die verschiedenen Alterungszustände. Eine Schädigungsakkumulation unter Berücksichtigung der fortschreitenden Alterung über der Lebensdauer wurde entwickelt und implementiert. Neben der Berücksichtigung der Alterung in der Verformungs- und Lebensdaueranalyse besteht auch die Möglichkeit, komplexe Belastungszyklen in einem Postprozessing zu bewerten, indem Rainflow-Klassierungen typischer komplexer Belastungszyklen vorgenommen werden.
Die Methodik und die Modelle wurden in die Finite-Elemente-Programme Abaqus und Ansys implementiert und stehen für die rechnerische Bewertung von Bauteilen zur Verfügung.