Nanocrystalline hydroxyapatite (HAp) prepared by a precipitation route was investigated. The X-ray diffraction (XRD) powder patterns of the elongated nanocrystals with a typical diameter of about 10 nm and length of 30-50 nm (by transmission electron microscopy (TEM)) revealed the presence of HAp with significantly broadened XRD reflections. However, Ca deficiency was found, as the Ca/P ratio was 1.5 only (so-called calcium-deficient hydroxyapatite (CDHA)), and not 1.67. This Ca deficiency of nanocrystalline HAp is explained using NMR. It is shown unambiguously that (i) the nanocrystals consist of a crystalline core and a (disordered) surface region with a relative phosphate content of about 1:1, (ii) the crystalline core is HAp, and (iii) the surface region is dominated by hydrogen phosphate anions (with no hydroxyapatite-like structural motif) and structural water (hydrate). From the relative phosphate content and taking into account the crystal shape, the thickness of the surface layer along the main crystal axis could be estimated to be about 1 nm, and the average chemical composition of the surface layer has been determined. Finally, a Ca/P ratio of 1.52 was estimated from the NMR data that compares well with the value of 1.51 from chemical analysis. The important consequences are that the surface of nanocrystalline HAp has nothing in common with the bulk composition and that the chemistry of such materials (e.g. the binding of protein molecules to phosphate surfaces) must be reconsidered.
This paper reports the first successful synthesis and the structural characterization of nanocrystalline and stacking-disordered β-cristobalite AlPO4 that is chemically stabilized down to room temperature and free of crystalline impurity phases. Several batches of the title compound were synthesized and thoroughly characterized by X-ray powder diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy, selected area electron diffraction, energy dispersive X-ray spectroscopy mapping in SEM, solid-state 31P nuclear magnetic resonance (31P-NMR) spectroscopy including the TRAPDOR method, differential thermal analysis (DTA), gas-sorption methods, optical Emission spectroscopy, X-ray fluorescence spectroscopy, and ion chromatography. Parameters that are critical for the synthesis were identified and optimized. The synthesis procedure yields reproducible results and is well documented. A high-quality XRD pattern of the title compound is presented, which was collected with monochromatic copper radiation at room temperature in a wide 2θ range of 5°–100°.
Two different radical polymerization techniques have been applied to covalently graft vinylformamide (VFA) onto silica particles. Grafting by the polymerization of VFA using an immobilized azo initiator on silica has been found less effective, because monomer conversion is limited in non-aqueous solvents and grafting yields are low in water. Radical copolymerization of VFA with vinyltriethoxysilane (VTS)-functionalized silica particles is suitable to produce poly(vinylformamide) (PVFA) silica hybrid particles in respectable yield. The VFA/VTS-silica ratio determines the degree of grafting. The PVFA-VTS-co-grafted silica particles can be acidically hydrolyzed into poly(vinylamine)-grafted silica particles. Molecular structures of the surface groups and grafted polymer chains have been confirmed by means of solid state 13C{1H} cross-polarization magic-angle spinning (CP MAS) NMR spectroscopy. Zeta potential measurements show the altering of the former silica particles surface charges arising from the introduction of basic groups on the surface.