Building stones are porous media and they can deteriorate through moisture ingress and secondary damage such as crystallization of soluble salts. Not only is this due to the increasing number of flood events in the past years but also structural damages of houses from activity such as leakage or rising moisture (groundwater) are the main causes. The potential benefit of several nondestructive testing methods to assess water damage in building stone has been studied in a field-scale experiment. Three testing walls made of fired clay brick, sandstone, and spongilite were flooded and their drying behavior monitored using infrared thermography, complex resistivity, ground penetrating radar, and ultrasonics. The results were compared to the average moisture content determined by gravimetric weighing of the specimens. Qualitatively, the results of the different nondestructive testing methods matched well. But in terms of quantitative data, some scatter was observed and the results should be viewed with care. Collecting time-consuming calibration data would help to overcome this problem, but especially when dealing with historic building structures, this is not always possible in practice.
Ultrasound sensors should be embedded into concrete for monitoring concrete properties. These new longitudinal wave sensors with a center frequency of 60 kHz were examined regarding their suitability for ultrasonic measurements in concrete structures in terms of emission characteristics, sensitivity and frequency ränge.
For the measurement of the radiation patterns, the sensors were embedded vertically and horizontally in concrete cylinders. The directivity pattern was measured using a laser vibrometer.
The sensitivity of the sensor was determined in water using different sensors of the same type. It shows changes in the signal amplitude as well as variations in the frequency ränge for different transmitter-receiver combinations.
The attenuation of the concrete affects the achievable resolution of the measurements and thus, the maximum possible spacing of the sensors within a concrete element. Experimental tests helped optimizing the distances with respect to the required resolution and the effort of embedding the sensors. The signal attenuation in the concrete was measured in the frequency ränge of 60 kHz in response to various degrees of reinforcement and grain size. For this purpose, the sensors were cast at different distances in the specimens studied. The recorded Signals were evaluated for their amplitude and frequency spectrum.
The non-destructive assessment of cracks in concrete is a common task for which non-destructive evaluation solutions have been published. Primarily, these tests have been carried out on artificial cracks that have been created by using notches instead of natural cracks. This study evaluates a procedure designed to create reproducible and controlled cracks in concrete. The procedure is based on using expanding mortar in a series of blind holes. This is done in combination with carefully aligned reinforcement to guide the direction of the crack development. The depth of the crack is also controlled by reinforcement. Crack depth varies statistically in the range of the Maximum aggregate size (16 mm) used for concrete.
Muon Tomography of the Interior of a Reinforced Concrete Block: First Experimental Proof of Concept
(2021)
Quality assurance and condition assessment of concrete structures is an important topic world-wide due to the aging infrastructure and increasing traffic demands. Common topics include, but are not limited to, localisation of rebar or tendon ducts, geometrical irregularities, cracks, voids, honeycombing or other flaws. Non-destructive techniques such as ultrasound or radar have found regular, successful practical application but sometimes suffer from limited resolution and accuracy, imaging artefacts or restrictions in detecting certain features. Until the 1980s X-ray transmission was used in case of special demands and showed a much better resolution than other NDT techniques. However, due to safety concerns and cost issues, this method is almost never used anymore. Muon tomography has received much attention recently. Novel detectors for cosmic muons and tomographic imaging algorithms have opened up new fields of application, such as the investigation of freight containers. Muon imaging also has the potential to fill some of the gaps currently existing in concrete NDT. As a first step towards practical use and as a proof of concept we used an existing system to image the interior of a reference reinforced 600 kg concrete block. Even with a yet not optimized setup for this kind of investigation, the muon imaging results are at least of similar quality compared to ultrasonic and radar imaging, potentially even better. The data acquisition takes more time and signals contain more noise, but the images allowed to detect the same important features that are visible in conventional high energy X-ray tomography. In our experiment, we have shown that muon imaging has potential for concrete inspection. The next steps include the development of mobile detectors and optimising acquisition and imaging parameters.
Decades of non-destructive evaluation (NDE) for the quality assurance of concrete bridges revealed the necessity of developing procedures for building reference specimens for different defects. External objects have been widely used in specimen construction to represent defects. However, embedded materials can alter the actual defect characteristics, interrupting the NDE responses. This study proposes new approaches to fabricating reference specimens for reinforced concrete that feature substantial defects, including cracks, delamination, honeycombing and rebar corrosion, without external objects. As a result, realistic responses can be acquired to identify promising NDE methods for characterising actual deteriorations. The procedures were produced with the intent of being reproducible in any laboratory. Destructive and non-destructive testing methods were performed to verify the effectiveness of the processes in creating defects. This study provides research laboratories with techniques for
fabricating reference specimens for characterising defects and assessing the performance of NDE technologies.