Sewage sludge ashes (SSA) contain up to 13% P and are thus promising raw materials for fertilizer production. However, SSAs also contain heavy metals and the main P-bearing mineral phases whitlockite and aluminium phosphate are poorly bioavailable. We developed and patented a process that produces fertilizers from SSA addressing the above mentioned challenges. SSA is thermo-chemically treated at ~950°C under reducing conditions (reductive: dry sewage sludge) in a rotary kiln together with an alkali compound such as sodium or potassium sulfate, hydroxide or carbonate. Some undesired trace elements such as As, Hg, Pb and Cd are evaporated and separated via off gas treatment system. The poorly soluble phosphates are transformed into calcium alkali phosphates (CaNaPO4 or CaKPO4) that are not water soluble but completely soluble in neutral ammonium citrate solution (NAC). Pot experiments showed that the fertilizer performance of the treated SSA containing calcium alkali phosphates as the single P-bearing mineral phase was comparable to the performance of triple superphosphate. The PNAC-solubility of fertilizer products correlated very well with the resulting contents of calcium alkali phosphates and the P-uptake of plants in pot experiments. The effect of the ratio alkali/P on the PNAC-solubility was investigated by crucible experiments and trial series with a medium scale rotary kiln using different SSAs and alkali phosphates. The effects of operational parameters such as the temperature and the retention time were investigated as well as concurring side reactions of the alkali compounds e.g. with SiO2 present in SSA. The alkali/P ratio must be roughly adjusted at 2 to achieve 100% PNAC-solubility for a common type of SSA. A demonstration trial with an output of 2 t recycling fertilizer was carried out in an industrial rotary kiln (product output 30 kg/h). The PNAC-solubility of the product varied between 60% and 80% during the 4 days campaign showing that the transformation of the mineral P-phases to calcium alkali phosphates was not complete. This was observed although the amount of Na2SO4 additive was dosed according to the results of the pre-investigations. Structure analysis by XRD showed that besides the target compound CaNaSO4 also some Ca3(PO4)2 remained in the SSA as well as some unreacted Na2SO4 additive. Obviously, the conditions in the industrial rotary kiln were not optimal for the process showing that some process aspects have to be reconsidered for the scale-up.
Municipal sewage sludge is a carrier of nutrients most important phosphorus (P) but also contains organic pollutants and heavy metals. A two steps thermal treatment is suggested based on 1. mono-incineration of sewage sludge under destruction of organic pollutants and 2. thermochemical treatment of the resulting ashes to remove heavy metals and increase P-bioavailability. The targeted products are marketable P-fertilisers. The thermochemical treatment was investigated in a gas tight lab-scale rotary furnace. Seven sewage sludge ashes of different origin and composition and one residue from gasification of sewage sludge were mixed with a chlorine donor (e.g. MgCl2) and thermochemically treated under systematic variation of operational parameters. The distributions of the heavy metals between solid and gas phase were determined. The heavy metals concentrations of the treated ashes met the legislative limits in most cases. The products from thermochemical treatment are suited raw materials for P-fertiliser production. Relevant process parameters such as temperature, type and concentration of Cl-donor and retention time were optimised for the thermochemical treatment step.
Municipal sewage sludge is a carrier of nutrients most important phosphorus (P) but also contains organic pollutants and heavy metals. A two steps thermal treatment based on 1. mono-incineration of sewage sludge under destruction of organic pollutants and 2. thermochemical treatment of the resulting ashes to remove heavy metals and increase P-bioavailability is suggested by the authors. The process aims at P-fertilisers production from sewage sludge. Seven sewage sludge ashes of different origin and composition and one residue from gasification of sewage sludge were thermochemically treated. The raw ashes were mixed with a chlorine donor (e.g. MgCl2) and thermally treated in a gas tight lab-scale rotary furnace. The distributions of the heavy metals between solid and gas phase were determined. The heavy metals concentrations of the treated ashes matched the legislative limits in most cases. The products from thermochemical treatment are suited raw materials for P-fertiliser production. Relevant process parameters such as temperature, type and concentration of Cl-donor and retention time were optimised for the thermochemical treatment step.
Phosphorus (P) is an essential element for all living organisms and cannot be replaced. Municipal sewage sludge is a carrier of phosphorus, but also contains organic pollutants and heavy metals. A two-step thermal treatment is suggested, including mono-incineration of sewage sludge and subsequent thermochemical treatment of the ashes. Organic pollutants are completely destroyed by mono-incineration. The resulting sewage sludge ashes contain P, but also heavy metals. P in the ashes exhibits low bioavailability, a disadvantage in farming. Therefore, in a second thermochemical step, P is transferred into mineral phases available for plants, and heavy metals are removed as well. The thermochemical treatment was investigated in a laboratory-scale rotary furnace by treating seven different sewage sludge ashes under systematic variation of operational parameters. Heavy metal removal and the increase of the P-bioavailability were the focus of the investigation. The present experimental study shows that these objectives have been achieved with the proposed process. The P-bioavailability was significantly increased due to the formation of new mineral phases such as chlorapatite, farringtonite and stanfieldite during thermochemical treatment.
Sewage sludge ashes (SSA) contain considerable mass fractions of phosphorus (5-10 w-% P) suitable for fertiliser production. Unfortunately, also most of the heavy metals remain in the ashes. A thermochemical process was developed for the treatment of SSA to i) remove heavy metals and ii) transform phosphates into bio-available mineral phases. The technology was already demonstrated in technical scale (capacity of 300 kg/h) and the company OUTOTEC is currently planning the first industrial plant. In order to manufacture a marketable multi-nutrient fertiliser from the thermochemically treated SSA further wastes and industrial by-products were taken into account. Ammonium sulphate occurs as a by-product of the caprolactam production and was chosen as N-carrier (21 w-% N). Straw ash was tested as potassium carrier (11-15 w-% K). Granulation campaigns were carried out with intensive mixers in lab-, medium-and technical scale. NPS-and NPKS-fertilisers were produced that were characterised by suitable particle size distributions and strength.
Slags from the production of high-alloyed steel contain both chemically bound chromium (mainly as Cr2O3) in the mineral fraction and elemental chromium in the metallic remainders. Thermochemical post treatment of the slag in an electric arc furnace under reducing conditions enables the nearly complete recovery of the total amount of chromium in form of a metallic alloy. The best results were achieved by resistance melting (submerged electrodes) with addition of a reducing agent into the melt. The efficiencies of the reducing agents carbon, aluminium, silicon (as ferrosilicon) and silicon carbide were investigated and compared. As aluminium is the strongest reducing agent, it is less selective and reduces much more SiO2 than Cr2O3. While SiC shows only low reactivity because of its high thermal resistance, carbon and silicon had the highest reducing potentials: More than 97% of the chemically bound chromium can be recovered by application of these reducing agents. Due to the high temperature required for the reduction of the chromium compounds, the reduction of SiO2 as an undesired side reaction cannot be avoided. However, compared with mechanical procedures that are limited to the recovery of the metallic remainders, the total chromium recovery can be significantly increased by the described reductive melting procedure.
Treatment and reusing of hazardous wastes have become significant issues of modern societies. Blast furnace sludge (BFS) and electric arc furnace dust (EAFD) are such typical wastes, because they usually contain high amounts of undesirable elements such as zinc (Zn) and lead (Pb).
These elements can cause operational problems in reusing of BFS and EAFD. In this study, the Ferro Duo GmbH and the Federal Institute for Materials Research and Testing have investigated a novel approach for eliminating and/or recovering Zn and Pb from both wastes. Applied was a selective chlorination and volatilization of Zn and Pb as chlorides at temperatures between 500 °C and 1100 °C. Both product obtained, Zn and Pb in the form of ZnCl2 and PbCl2 and the purified solid mineral compound are attractive materials for further use. Hydrochloric acid and iron(II) chloride were used as chlorination agents. Exceptionally high Zn and Pb removal efficiencies of >99.5 % could be achieved with both chlorination agents, whereby iron(II) chloride exhibited better performance.