Sewage sludge ash (SSA) based P-fertilisers were produced by thermochemical treatment of SSA with Cl-donors at approximately 1000 °C. During this thermochemical process heavy metals are separated as heavy metal chlorides via the gas phase. Chromium cannot be separated under normal conditions. The risk of the development of toxic Cr(VI) during the thermochemical process was investigated. X-ray Absorption Spectroscopy measurements showed that SSA and thermochemically treated SSA with CaCl2, MgCl2 and NaCl contain Cr(III) compounds only. In contrast, treating SSA with elevated quantities of Na2CO3, to enhance the plant-availability of the phosphate phases of the fertiliser, developed approximately 10–15% Cr(VI). Furthermore, Raman microspectroscopy showed that using Mg-carbonate reduces the risk of a Cr(VI) development during thermochemical treatment. Additionally, leaching tests showed that only a Crwater solubility >10% is an indicator for Cr(VI) in SSA based P-fertilisers.
The amount of sewage sludge produced worldwide is expected to further increase due to rising efforts in wastewater treatment. There is a growing concern against its direct use as fertilizer due to contamination of the sludge with heavy metals and organic pollutants. Incinerating the sludge degrades organic compounds almost completely and concentrates heavy metals and phosphorus. However, the sewage sludge ash (SSA) is almost completely disposed of and with it all resources are removed from the economic cycle. Comprehensive knowledge of the composition of SSA is crucial to assess the resource recovery potentials. We conducted a survey of all SSA emerging in Germany and determined the respective mass fractions of 57 elements over a period of one year. The median content of phosphorus was 7.9%, indicating an important recovery potential. Important trace elements were Zn (2.5 g/kg), Mn (1.3 g/kg), and Cu (0.9 g/kg). Mass fractions of technology metals such as V, Cr, Ga, Nb, and rare earths were comparatively low. Considering the possible use of SSA as secondary raw material for fertilizer production it should be noted that its Cd and U content (2.7 mg/kg and 4.9 mg/kg respectively) is significantly lower than that of rock phosphate based mineral fertilizers.
This study focuses on the question whether heat treated sewage sludge ashes are more favourable as fertilizers than untreated sewage sludge ashes (USSA) and whether their fertilization effects are comparable with commercial triple superphosphate (TSP). In a pot experiment, maize was fertilized either with one of three heat treated and Na-, Ca- and Si-compounds amended sewage sludge ashes (two glown phosphates, steel mill slag + sewage sludge ash) or USSA or TSP as control. Fertilization with USSA did not increase the biomass yield and the P uptake of maize in comparison to the P0 treatment (7.25 resp. 8.35 g dry matter/pot). Fertilization with heat treated sewage sludge ashes and TSP resulted in significantly higher yields and plant P uptakes which are on average eight times higher than treatment with USSA and P0 control. Biomass yields and P uptake of maize after fertilization with heat treated sewage sludge ashes are not significantly different from those after TSP fertilization. The main P compound in USSA is Ca3(PO4)2. By heat treatment and amendment with different sodium, calcium, sulphur and silicon containing additives or steel mill converter slag, Ca3(PO4)2 is converted to Ca- and Na-silico-phosphates, which have a higher water solubility than Ca3(PO4)2. This increased solubility is responsible for the high plant availability of this phosphates.