Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (30)
- Beitrag zu einem Tagungsband (5)
- Posterpräsentation (3)
- Vortrag (2)
- Beitrag zu einem Sammelband (1)
- Sonstiges (1)
- Forschungsdatensatz (1)
Schlagworte
- Mechanochemistry (4)
- Spectral induced polarization (4)
- Nuclear magnetic resonance (3)
- Reference material (3)
- BET specific surface area (2)
- Biomaterials (2)
- Concrete and screed (2)
- Electrochemistry (2)
- Embedded humidity sensors (2)
- Lanthanide (2)
Organisationseinheit der BAM
- 6 Materialchemie (24)
- 6.3 Strukturanalytik (23)
- 1 Analytische Chemie; Referenzmaterialien (6)
- 8 Zerstörungsfreie Prüfung (4)
- 6.0 Abteilungsleitung und andere (3)
- 1.2 Biophotonik (2)
- 1.5 Proteinanalytik (2)
- 1.6 Anorganische Referenzmaterialien (2)
- 1.8 Umweltanalytik (2)
- 8.2 Zerstörungsfreie Prüfmethoden für das Bauwesen (2)
Eingeladener Vortrag
- nein (2)
Zeolitic imidazolate framework (ZIF) hybrid fluorescent nanoparticles and ZIF antibody conjugates have been synthesized, characterized, and employed in lateral-flow immunoassay (LFIA). The bright fluorescence of the conjugates and the possibility to tailor their mobility gives a huge potential for diagnostic assays. An enzyme-linked immunosorbent assay (ELISA) with horseradish peroxidase (HRP) as label, proved the integrity, stability, and dispersibility of the antibody conjugates, LC-MS/MS provided evidence that a covalent link was established between these metal-organic frameworks and lysine residues in IgG antibodies.
Stone deterioration is the result of a complex interaction of external physical, chemical and biological forces with the mineralogical-petrophysical properties of the stone. With a better understanding of how these properties are linked to material behavior and durability, more effective measures for stone conservation can be developed. Studying these interactions in tuff is particularly complex due to the naturally high heterogeneity of tuff rocks.
The first aim of a current research project is to combine the results of recent and older studies on tuff deterioration. Furthermore, the literature overview is complemented by our own investigation of Weibern and Ettringen tuff, with a focus on pore structure characteristics.
Die feuchte Wundbehandlung ist ein elementarer Bestandteil zeitgemäßer Wundversorgung. Bereits im 19. Jahrhundert wandte F. Hebra in Wien kontinuierliche Wasserbäder bei brandverletzten Patienten erfolgreich an. G. D. Winter zeigte 1962 erstmals experimentell am Schwein, dass es unter einem Okklusivverband innerhalb kürzerer Zeit zu einer vollständigeren Epithelisierung kommt als bei Luftexposition. Bei der Entwicklung von liposomalen Hydrogelen mit wundheilenden Eigenschaften kann somit das Verhalten der Wasserabgabe an die Haut bzw. das Abdampfverhalten von Wasser - bis hin zum Eintrocknen des Gels - ein qualitätsrelevanter Parameter sein. In diesem Rahmen wurde die Anwendungsbreite der Wasserdampfsorption auf halbfeste pharmazeutische Zubereitungen erweitert, um das Abdampfverhalten näher zu untersuchen und quantifizieren zu können.
Für die Untersuchungen wurden drei unterschiedlich hergestellte bzw. gelagerte wundheilende Gele verwendet.
Dazu wurden Wasserdampfsorptionmessungen an Hydrogelen unterschiedlicher Chargen durchgeführt. Die eingewogenen Proben wurden mit 2 unterschiedlichen DVS-Varianten vermessen:
1. bei einer konstanten Feuchte von 50% relativer Feuchte (r. F.)
2. mit einem vorgegebenen definierten Feuchteprofil (zunächst abnehmende Feuchte von 95% bis 0% r. F. in 5%-Schritten und danach analoger Wiederanstieg auf das Ausgangsniveau).
Eine vergleichbare Oberfläche wurde unter Verwendung einer definierten Tropfengröße (Spritze) erreicht. Jeweils durchgeführte Doppelbestimmungen zeigen die gute Reproduzierbarkeit der Messungen.
Zur Charakterisierung des Abdampfverhaltens wurden die Wasserdampfadsorptionsmessungen bezüglich des prozentualen Masseverlustes (m in %) und der Dynamik (dm/dt in %·min-1) ausgewertet. Zwei sehr ähnlich hergestellte Gele wiesen ein fast identisches Abdampfverhalten auf, der Masseverlust des dritten Gels war verlangsamt. Insbesondere bei den Versuchen unter konstanter relativer Feuchte zeigte Gel 3 eine deutlich abweichende Dynamik des Masseverlustes. Bei definiertem Feuchteprofil traten analoge Unterschiede auf.
Es konnten mit Hilfe der DVS-Methode gelspezifische Unterschiede bezüglich des Abdampfverhaltens des Wassers infolge einer veränderten Mikrostruktur der untersuchten Gele nachgewiesen werden. Auf der Grundlage dieser Informationen ist es möglich, maßgeschneiderte Hydrogele mit einem definierten Abdampfverhalten herzustellen und dadurch die Produkteigenschaften wundheilender Hydrogele zu verbessern.
Rare-earth based luminescent materials are key functional components for the rational design of light-conversion smart devices. Stable Eu3+-doped strontium fluoride (SrF2) nanoparticles were prepared at room temperature in ethylene glycol. Their luminescence depends on the Eu content and changes after heat treatment. The crystallinity of heat-treated material increases in comparison with as-synthesized samples. Particles were investigated in solution using X-ray diffraction, small-angle X-ray scattering, and X-ray spectroscopy. After heat treatment, the size of the disordered nanoparticles increases together with a change of their local structure. Interstitial fluoride ions can be localized near Eu3+ ions. Therefore, non-radiative relaxation from other mechanisms is decreased. Knowledge about the cation distribution is key information for understanding the luminescence properties of any material.
A facile and efficient methodology is described for the solvothermal synthesis of size-tunable, stable, and uniform NiCu core–shell nanoparticles (NPs) for application in catalysis. The diameter of the NPs is tuned in a range from 6 nm to 30 nm and to adjust the Ni:Cu ratio from 30:1 to 1:1. Furthermore, the influence of different reaction parameters on the final NPs is studied. The NPs are structurally characterized by a method combination of transmission electron microscopy, anomalous small-angle X-ray scattering, X-ray absorption fine structure, and X-ray photoelectron spectroscopy. Using these analytical methods, it is possible to elucidate a core–shell–shell structure of all particles and their chemical composition. In all cases, a depletion from the core to the shell is observed, with the core consisting of NiCu alloy, surrounded by an inner Ni-rich shell and an outer NiO shell. The SiO2-supported NiCu core–shell NPs show pronounced selectivity of >99% for CO in the catalytic reduction of CO2 to CO using hydrogen as reactant (reverse water–gas shift reaction) independent of size and Ni:Cu ratio.
In order to identify the best porous materials for the cryogenic physisorption of hydrogen, high-throughput calculations are performed starting, i.e., from the collected information in crystallographic databases. However, these calculations, like molecular simulations, require specific training and significant computational cost. Herein, a relatively simple procedure is proposed to estimate and compare hydrogen uptakes at 77 K and pressure values from 40 bar starting from the porous properties of MOF materials, without involving simulation tools. This procedure uses definitions for adsorption and considers the adsorbed phase as an incompressible fluid whose pressure-density change is that for the liquid phase at 19 K. For the 7000 structures from the CoRE MOF database, the average error of the predictions is only of 1% from reference values at 100 bar, with an SD of ±8%. This accuracy is lower than that from simulation tools, but involving lower computational cost and training.
Lanthanides doped coordination polymers (CPs) with different binding motifs were synthesized to investigate the influence of the different fluorine positions in the structure on the decay time τ of the excited states. Fluorine can be integrated into the network mechanochemically via a fluorinated organic linker, here barium tetrafluoroterephthalate Ba(p-BDC-F4)2 or directly via a metal-fluorine bond (barium terephthalate fluoride BaF(p-BDC)0.5). The CP with a metal-fluorine bond shows the highest lifetime of the excited states of lanthanides (Eu3+, Tb3+ or Eu3+& Tb3+). The excitation of the lanthanides can be performed directly via the excitation wavelength typical for lanthanides and via the excitation wavelength of the linker. This enabled the simultaneous excitation of Eu3+ and Tb3+ in one CP. In the emission spectra (λem = 393 nm) of the mixed doped CPs (Eu3+ and Tb3+) the bands of both lanthanides can be observed. The integration into the crystal lattice and the homogeneous distribution of the lanthanides in the CPs is shown by X-ray diffraction, TEM, STEM-EDS measurements and the long decay times.
Zeolite synthesis was studied using two silica rich filtration residues (FR 1 and FR 2) as Si-source
and sodium aluminate in a direct synthesis at 60°C at strong alkaline conditions (8 M - 16 M NaOH).
In addition to these one-pot syntheses, a two-step process was investigated. Here, an alkaline digestion
of FR at 60°C was followed by gel precipitation with sodium aluminate and gel crystallization
under usual conditions of 80°C - 90°C. The results show that the substitution of chemical
reagent sodium silicate by a waste material like FR as Si-source is possible but requires fine tuning
of the reaction conditions as zeolite crystallization is a process under kinetic control. The
solubility behaviour and impurities of the inserted filtration residues strongly influenced the
course of reaction. Thus zeolites like hydrosodalite or intermediate zeolite between cancrinite
and sodalite, or zeolite NaA or Z-21 in cocrystallization with hydrosodalite could be observed in
the one pot syntheses already in a short time interval between 1 - 4 h depending on the alkalinity.
The two step process yield to zeolites NaA and NaX in very good quality. The reaction process of FR
in both reaction methods was characterized by chemical analyses, X-ray powder diffraction,
Fourier transform infrared spectroscopy as well as scanning electron microscopy. Surface area
and water content of selected products were further characterized by the BET-method and by
thermogravimetry. Summing up the results, we can show that zeolite formation from filtration residues
is possible by several reaction procedures as model cases for a re-use of industrial waste
materials. Beside the importance for environmental protection, the reactions are of interest for
zeolite chemistry as the re-use of FR is possible under economically conditions of low energy consumption
at 60°C and short reaction periods.
The pore structure of lightweight granules made from masonry rubble was studied in order to better understand their engineering properties. Thermally and hydrothermally hardened granules were tested. Analysis by ESEM, mercury porosimetry and sorption methods yield important insight into their microstructure. The thermal granules are characterised by partly melted vitreous areas and large internal macropores that are connected via narrow throats. They show a marginal specific surface area along with a hydrophobic behaviour. In contrast, the hydrothermal granules have an accessible mesoporous system containing plate-like and ink-bottle pores. The shape of their water isotherms depending on the granules CaO content is sensitive to the morphology of calcium silicate hydrate phases (CSH). The hysteresis changes from a narrow loop that closes at low pressures, which can be attributed to coarser more crystalline CSH, to a large triangular-shaped loop along with a low pressure hysteresis, which is characteristic for fine fibre-like CSH with ink-bottle and plate-like pore morphologies. Granules with fibre-like CSH have the higher specific surfaces areas but those with more crystalline CSH show stronger physisorption of water molecules.
The CCQM-K136 key comparison for determination of the porosity properties of aluminum oxide has been organized jointly by the surface and micro/nano analysis working groups of CCQM to test the abilities of the metrology institutes to measure the porosity properties (specific adsorption, BET specific surface area, specific pore volume and pore diameter) of nanoporous Al2O3.
Ural Scientific Research Institute for Metrology (UNIIM) acted as the coordinating laboratory for this comparison with BAM Federal Institute for Materials Research and Testing (BAM) as co-coordinating laboratory. Five NMIs and one DI participated in this key comparison. All participants used a gas adsorption method, here nitrogen adsorption at 77.3 K, for analysis according to the international standards ISO 15901-2 and 9277.
Die Herstellung hydrothermal erhärteter Granulate ist eine Möglichkeit zur Wiederverwertung von ziegelhaltigem Mauerwerkbruch, der derzeit aufgrund der heterogenen Zusammensetzung und hoher Feinanteile ein besonders hohes Verwertungsdefizit aufweist. Dabei ist die hydrothermale Erhärtung in einem Autoklav bei 200 °C und 1.6 MPa in gesättigter Wasserdampfatmosphäre eine Alternative mit geringerem Energieverbrauch im Vergleich zur thermischen Herstellung von Leichtgranulaten aus mineralischen Abfällen (Blähgranulate) oder Tonen und Schiefer (kommerzieller Blähton bzw. Blähschiefer), die bei Temperaturen von 1200-1300 °C im Drehrohrofen erfolgt.
Die Festigkeit der Hydrothermalgranulate entwickelt sich bei diesem Prozess durch die Ausbildung von Calciumsilicathydrat-Phasen (CSH), die durch die Reaktion zwischen Quarzpartikeln und hydratisiertem Kalk entstehen. Die so erzeugten Hydrothermalgranulate haben Rohdichten zwischen 1500 kg/m3 und 2000 kg/m3. Damit und auch durch andere Eigenschaften unterscheiden sie sich von den thermisch erhärteten Blähgranulaten bzw. Blähtonen. Ursache dafür ist letztendlich eine sehr unterschiedliche Gefüge- und Porenstruktur. Im vorliegenden Beitrag wird hauptsächlich über die Ergebnisse der Mikrostrukturuntersuchungen an Hydrothermalgranulaten zusammen mit ihren technologischen Eigenschaften, wie Kornfestigkeit, Rohdichte und Wasseraufnahme, berichtet.
Established maximum levels for the mycotoxin zearalenone (ZEN) in edible oil require monitoring by reliable analytical methods. Therefore, an automated SPE-HPLC online system based on dynamic covalent hydrazine chemistry has been developed. The SPE step comprises a reversible hydrazone formation by ZEN and a hydrazine moiety covalently attached to a solid phase. Seven hydrazine materials with different properties regarding the resin backbone, pore size, particle size, specific surface area, and loading have been evaluated. As a result, a hydrazine-functionalized silica gel was chosen. The final automated online method was validated and applied to the analysis of three maize germ oil samples including a provisionally certified reference material. Important performance criteria for the recovery (70–120 %) and precision (RSDr <25 %) as set by the Commission Regulation EC 401/2006 were fulfilled: The mean recovery was 78 % and RSDr did not exceed 8 %. The results of the SPE-HPLC online method were further compared to results obtained by liquid&–liquid extraction with stable isotope dilution analysis LC-MS/MS and found to be in good agreement. The developed SPE-HPLC online system with fluorescence detection allows a reliable, accurate, and sensitive quantification (limit of quantification, 30 µg/kg) of ZEN in edible oils while significantly reducing the workload. To our knowledge, this is the first report on an automated SPE-HPLC method based on a covalent SPE approach.
Zeolitic Imidazolate Frameworks (ZIFs) are crystalline materials
that comprise of metal nodes and Imidazole derivatives as
linkers. ZIF-67 is often used in polymer composite materials
e. g. for gas separation membranes. Post-synthesis treatment of
ZIF-67 crystals with ultrasound leads to unforeseen plasticity
that resulted in sintered ZIF-67 and ZIF-67 nano-flakes.
Consequently, ultrasound increases the external surface area of
ZIF-67 which might improve e.g. blending with polymers in
composite materials. These new morphologies of ZIF-67 were
characterized by transmission electron, scanning electron, and
atomic force microscopy. The ultrasound treatment of ZIF-67
did not result in the formation of an amorphous framework or
a meta-stable crystal structure as indicated by powder x-ray
diffraction. In addition, ultra-sonicated ZIF-67 retained the high
gas adsorption capacity and pore size compared to synthesized
ZIF-67. The morphological changes are hard to detect with
standard analytical methods that are usually utilized for MOF
characterization. These findings also suggest that sonochemical
treatment of ZIFs leads to structural effects beyond increasing
the amount of nucleation clusters during sono-chemical synthesis,
which is currently not addressed in the field.
Water vapor sorption surface areas and sorption energies of untreated
and thermally modified Norway spruce [Picea abies (L.) Karst.], sycamore maple (Acer pseudoplatanus L.) and European ash (Fraxinus excelcior L.) were investigated by means of dynamic vapor sorption (DVS) measurements and excess surface work (ESW) evaluation method, respectively. Adsorption and desorption experiments in the hygroscopic range and desorption tests from water saturation were conducted.
Thermodynamically, ESW is the sum of the surface free energy and the isothermal isobaric work of sorption. From the amount adsorbed in the first Minimum a specific surface area similar to the BET surface area can be obtained. The results show that untreated spruce has a significantly higher specific water vapor Sorption surface and sorption energy compared to both hardwoods maple and ash. Thermal modification of the woods leads to a significant reduction of water vapor Sorption surface and sorption energy. The determined surface area and energy are higher in desorption direction than in adsorption direction, whereby the highest values in Desorption direction from water saturation, especially for maple and ash, were obtained.
The surface areas calculated by means of the ESW method are similar to the surface areas calculated by means of the BET method, particularly in adsorption direction.
A series of Ca-based coordination polymers were prepared mechanochemically by milling Ca(OH)2 with phthalic acid (H2oBDC), isophthalic acid (H2mBDC), and terephthalic acid (H2pBDC). The hydrated compounds [Ca(oBDC)(H2O)], [Ca(mBDC)(H2O)3.4], and [Ca(pBDC)(H2O)3] were prepared for the first time via mechanochemical routes. The refined structures were validated by extended X-ray absorption data. The new dehydrated compound [Ca(oBDC)] (1-H2O), obtained after the thermal post-treatment of 1 in a reversible phase transition process, was determined ab initio based on the powder X-ray diffraction (PXRD) data. The materials were thoroughly characterized using elemental analysis, thermal analysis, and spectroscopic methods: magic-angle spinning NMR and attenuated total reflection-infrared spectroscopy. The specific surface areas and sorption properties of the hydrated and dehydrated samples were determined using the isotherms of gas sorption and dynamic vapor sorption measurements.
Four cement-based and four calcium-sulphate-based screed types are investigated. The samples have a diameter of 300 mm and a height of 35 or 70 mm. Up to ten humidity sensors are embedded directly during the concreting of the screed samples. Thus, the humidity over the sample height is monitored during hardening, hydration, evaporation, and oven drying. Furthermore, the screed samples are weighted during every measurement to determine the total mass and the corresponding moisture loss.
To define the pore system precisely, mercury intrusion porosimetry as well as gas adsorption is performed. According to the data, the entire pore volume distribution is known. The measured pore diameters range from 0.8 nm to 100 μm and the total porosity of the examined screeds ranges between 11 % and 22 %.
Based on these measurement data, moisture transport, pore saturation as well as sorption isotherms and their hysteresis may be calculated quantitatively as described by Strangfeld et al.
Relaxation phenomena observed in the electrical low-frequency range (approximately 1 mHz-10 kHz) of natural porous media like sandstones is often assumed to be directly related to the dominant (modal) pore throat sizes measured, for instance, with mercury intrusion porosimetry. Attempts to establish a universally valid relationship between pore size and peak Spectral Induced Polarization (SIP) relaxation time have failed, considering sandstones from very different origins and featuring great variations in textural and chemical compositions as well as in geometrical pore space properties. In addition working with characteristic relaxation times determined in Cole-Cole or Debye decomposition fits to build the relationship have not been successful. In particular, samples with narrow pore throats are often characterized by long SIP relaxation times corresponding to long “characteristic length scales” in these media, assuming that the diffusion coefficients along the electrical double layer were constant. Based on these observations, three different types of SIP relaxation can be distinguished. We present a new way of assessing complex pore spaces of very different sandstones in a multi-methodical approach to combine the benefits of mercury intrusion porosimetry, micro-computed tomography, and nuclear magnetic resonance. In this way, we achieve much deeper insight into the pore space due to the different resolutions and sensitivities of the applied methods to both pore constrictions (throats) and wide pores (pore bodies). We experimentally quantify pore aspect ratios and volume distributions within the two pore regions. We clearly observe systematic differences between three SIP relaxation types identified previously and can attribute the SIP peak relaxation times to measured characteristic length scales within our materials. We highlight selected results for a total of nine sandstones. It seems that SIP relaxation behavior depends on the size difference of the narrow pore throats to the wide pore bodies, which increases from SIP Type 1 to Type 3.