Filtern
Erscheinungsjahr
- 2023 (3) (entfernen)
Dokumenttyp
Sprache
- Englisch (3)
Referierte Publikation
- ja (3)
Schlagworte
- AAS (1)
- GD-OES (1)
- HR-CS-MAS (1)
- High-resolution continuum source molecular absorption spectrometry (1)
- Li-ion battery (1)
- MICAP-MS (1)
- Steel (1)
- Trace Analysis (1)
- VO (1)
- Vanadium (1)
- battery aging mechanism (1)
- current collector corrosion (1)
- depth profiles (1)
Organisationseinheit der BAM
- 1 Analytische Chemie; Referenzmaterialien (3)
- 1.6 Anorganische Referenzmaterialien (3)
- 3 Gefahrgutumschließungen; Energiespeicher (1)
- 3.1 Sicherheit von Gefahrgutverpackungen und Batterien (1)
- 5 Werkstofftechnik (1)
- 5.1 Mikrostruktur Design und Degradation (1)
- S Qualitätsinfrastruktur (1)
- S.1 Qualität im Prüfwesen (1)
This work aimed to evaluate high-resolution continuum source molecular absorption spectrometry (HR-CS MAS), traditionally used to determine non-metals, for the determination of a new element, metal, vanadium. VO was selected as a target molecule because it is relatively stable and was expected to be spontaneously generated in a flame or a graphite furnace (GF). The high-resolution overview spectra of the molecule were obtained in a wide range of 480–630 nm, and absorption due to the X4Σ−–C4Σ− electronic transition was registered. A unique instrumental setup, comprising a prototype Modular Simultaneous Echelle Spectrograph (MOSES) and a commercial HR-CS MAS apparatus, was applied in the research. Finally, the spectral area centered at 550.6230 nm was selected for analysis. A method was developed to determine V in solutions of catalysts of heavy petroleum oil hydroprocessing using a commercial HR-CS spectrometer in a flame version. Although sensitivity was relatively poor (characteristic concentration 380 mg L−1), an extremely low noise enabled reaching a satisfactory detection limit (20 mg L−1 in solution, i.e. 0.1% m:m in the catalyst). For the first time vanadium was determined using ordinary air-acetylene flame. The obtained results were consistent with the results of atomic absorption spectrometry with N2O-C2H2 flame. Unfortunately, only a small population of VO molecules could have been generated in GF measurements. Furthermore, the observed VO molecules appeared only at unfavorably high temperatures. The work shows the potential of HR-CS MAS as a scientific tool for investigating the mechanism of processes occurring in the GF. This work can inspire other research of new analytes for HR-CS MAS.
We investigated the performance of nitrogen microwave inductively coupled atmospheric-pressure plasma mass spectrometry (MICAP-MS) under matrix effects and its applicability to trace element analysis in steels. Influences of different gas flows and ion optics on the matrix tolerance are studied, indicating that nebulizer gas flow has the most significant impact. Optimization of ion optics improves matrix tolerance for light elements due to the reduction of the inelastic collisional scattering effect. With optimized operating conditions, MICAP-MS achieves an internal standard intensity recovery of over 90% at an Fe concentration of 500 mg L−1. Even at an Fe concentration of 1 g L−1, the recovery remains above 80%. Three certified reference materials – non-alloy, low-alloy and high-alloy steel – were analyzed using MICAP-MS. The determined mass concentrations of the trace and minor components show metrological compatibility to the reference values. No significant differences are observed between the results obtained with aqueous and matrix-matched calibration, demonstrating the strong matrix tolerance of MICAP-MS, and its promising applicability to steel analysis.
In this work, we employed glow discharge optical emission spectrometry (GD-OES) depth profiling as a fast and semi-quantitative method to investigate the aluminum (Al) current collector degradation in commercial lithium cobalt oxide (LCO) pouch cells with no Al2O3 pretreatment. After battery aging, a heterogeneous deposit was found on the surface of the cathode. Gray hotspot areas within an extensive pale white region were formed. Consistent with energy dispersive X-ray (EDX) analysis of micro-cross sections milled via targeted focused ion beam (FIB), an Al-containing layer of approximately 3 µm can be observed using GD-OES. We attribute one main cause of this layer is the degradation of the Al current collector. The nonuniform growth of this layer was investigated by performing GD-OES depth profiling at different in-plane positions. We found that the gray area has a higher mass concentration of Al, probably in metallic form, whereas the white area was probably covered more homogeneously with Al2O3, resulting from the inhomogeneous distribution of the pitting positions on the current collector. Compared to FIB-EDX, GD-OES enables a faster and more convenient depth profile analysis, which allows the more productive characterization of lithium-ion batteries (LIBs), and consequently benefits the development of preferable battery materials.