Al-Mg-Si alloys are known to be highly susceptible to solidification cracking except when using an appropriate filler metal (e.g., 4343 or 5356), although the amount of dilution required to avoid cracking has never been a well-defined quantity. The aim of the present study is to determine a relationship between filler metal dilution, local strain rate conditions, and cracking susceptibility. Making use of the controlled tensile weldability (CTW) test and local strain extensometer measurements, a boundary has been established between crack and non-crack conditions for different local strain rates and dilution amounts, holding all other welding parameters constant. This boundary, presented in the form of critical strain rate-dilution map, defines the critical amount of 4043 filler metal required to avoid solidification cracking when arc welding 6060 aluminium, depending upon local strain rate.
Earlier work has established that a critical amount of 4043 filler is required to avoid solidification cracking when arc-welding 6060 aluminium, depending upon local strain conditions. For example, when the mushy zone behind the weld pool experiences a tensile strain from combined thermal and shrinkage stresses, the possibility exists for crack initiation. For a greater rate of strain, it has been determined that a greater 4043 dilution (i.e. higher weld metal silicon content) is required to avoid crack initiation. Making use of the Controlled Tensile Weldability (CTW) test and local strain extensometer measurements, a boundary has been established between crack and no-crack conditions for different local strain rates and filler dilutions, holding all other welding parameters constant. Using this established boundary as a line of reference, additional parameters have now been examined and their influence on cracking has been characterized. These parameter influences have included studies of weld travel speed, weld pool contaminants (Fe, O, and H), and grain refiner additions (TiAl3 + Boron). Each parameter has been independently varied and its effect on cracking susceptibility quantified in terms of a critical strain rate required to initiate cracking for a given 4043 filler dilution.
A perspective will be given that outlines important considerations in evaluating and predicting weldability. An examination will be made of the local conditions necessary for solidifications crack initiation and growth in a weld. This will be done in light of two prominent thermo-mechanical approaches involving critical strain and critical strain rate. Critical conditions will be identified based upon values available in the literature. Methods used to measure strain and strain rate will be compared. The interpretation of crack lenght measurements commonly used to quantify weldability will be questioned, based upon our current understanding of the problem. Complications and problem areas needing better definition will be identified and discussed, including strain distribution in the mushy zone, segregation at grain boundaries, effect of impurities, and effect of cooling rate on solidification path. Finally, a suggestion will be made for a new approach to weld development using in-situ strain rate measurements and new composition-strain rate maps that define the boundary between crack an no-crack conditions.
Aluminium alloy 6060 is typical of a family of Al-Mg-Si extrusion alloys, which are considered weldable only
when using an appropriate filler alloy such as 4043 (Al-5Si) or 5356 (Al-5Mg). This study concerns the
thermal analysis and solidification path determination of aluminium alloy 6060 diluted with variable amounts
of 4043. Casting of controlled mixtures of alloys 6060 and 4043 was used to simulate different weld dilutions
in order to facilitate thermal analysis. Thermal analysis and metallography were applied in order to reveal
solidification reactions and phases, and allow calculation of solid fraction versus temperature curves.
Although the liquidus temperature was little affected, different phases formed with increased 4043 dilution,
with a trend toward lower temperature reactions and a larger fraction interdendritic constituent.