X-ray powder diffraction (XRD) patterns of the high-temperature (HT) cristobalite form of SiO2 and its isoelectronic AlPO4 analogue are essentially influenced by the dynamic disorder of these crystal structures. The nature of this disorder and of the phase transition between the α- and β-form has been the subject of intensive research during the last four decades [1]. By 1989 it became possible to stabilize the HT-form of cristobalite SiO2 at room temperature in laboratory and engineering ceramic industries by applying solid solution forming techniques [2]. However, for the HT-form of cristobalite AlPO4 nothing similar has been known until 2014 when it was discovered that nanocrystalline and stacking-disordered β-cristobalite AlPO4 is the major component of the fly ash of a large incineration facility operated by the waste water treatment authorities of Frankfurt/M. [3]. Previous comprehensive investigations of this fly ash failed to interpret its complex XRD pattern – presumably mainly due to the lack of a matching experimental digital pattern in the Powder Diffraction Database. The present paper reports on a synthesis route that facilitates the crystallization of nanocrystalline and stacking-disordered β-cristobalite AlPO4 that is free of crystalline impurity phases and long-term stable at ambient. Its room temperature XRD pattern is presented with parameters traced back to certified reference materials.
[1] Yuan F. and Huang L., Phys. Rev, B, 2012, 85, 134114. [2] Perrotta J.A., Grubbs D.K., Martin E.S., Dando N.R., McKinstry H.A. and Huang C.-Y., J. Am. Ceram. Soc., 1989, 72, 441. [3] Peplinski B., Adam C., Adamczyk B., Müller R., Michaelis M., Krahl Th. and Emmerling F., Powder Diffraction Journal, 2015, 30, 2, Supp. 1, S31.
A model system was used to simulate the properties of tribofilms which form during automotive braking. The model system was prepared by ball milling of a blend of 70 vol.% iron oxides, 15 vol.% molybdenum disulfide and 15 vol.% graphite. The resulting mixture was characterized by X-ray powder diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and various transmission electron microscopic (TEM) methods, including energy dispersive X-ray spectroscopy (EDXS), high resolution investigations (HRTEM) with corresponding simulation of the HRTEM images, diffraction methods such as scanning nano-beam electron diffraction (SNBED) and selected area electron diffraction (SAED). It could be shown that the ball milling caused a reduction of the grain size of the initial components to the nanometer range. Sometimes even amorphization or partial break-down of the crystal structure was observed for MoS2 and graphite. Moreover, chemical reactions lead to a formation of surface coverings of the nanoparticles by amorphous material, molybdenum oxides, and iron sulfates as derived from XPS.