Based on recently published research on leaching control mechanisms in electric arc furnace (EAF) slags, it is assumed that a FeO/SiO2 ratio of around one leads to low leached V and Cr concentrations. This ratio influences the mineral phase composition of the slag toward higher amounts of spinel and a lower solubility of calcium silicate phases by suppressing the formation of magnesiowuestite and highly soluble calcium silicate phases. To evaluate this hypothesis, laboratory and scaled up tests in an EAF pilot plant were performed on slag samples characterized by elevated V and Cr leaching and a high FeO/SiO2 ratio. Prior to the melting experiments, the optimum FeO/SiO2 ratio was calculated via FactSageTM. In the melting experiments, the ratio was adjusted by adding quartz sand, which also decreased the basicity (CaO/SiO2) of the slag. As a reference, remelting experiments without quartz sand addition were conducted and additionally, the influence of the cooling rate of the slag was examined. The remelted (without quartz sand) and the remelted modified slags (with quartz sand) were analyzed chemically and mineralogically and the leaching behavior was investigated. The modification of the slags yielded a minimized release of V and Cr, supporting the hypothesis that the FeO/SiO2 ratio influences the mineralogy and the leaching behavior.
Based on recently published research on leaching control mechanisms in electric arc furnace (EAF) slags, it is assumed that a FeO/SiO2 ratio of around one leads to low leached V and Cr concentrations. This ratio influences the mineral phase composition of the slag toward higher amounts of spinel and a lower solubility of calcium silicate phases by suppressing the formation of magnesiowuestite and highly soluble calcium silicate phases. To evaluate this hypothesis, laboratory and scaled up tests in an EAF pilot plant were performed on slag samples characterized by elevated V and Cr leaching and a high FeO/SiO2 ratio. Prior to the melting experiments, the optimum FeO/SiO2 ratio was calculated via FactSageTM. In the melting experiments, the ratio was adjusted by adding quartz sand, which also decreased the basicity (CaO/SiO2) of the slag. As a reference, remelting experiments without quartz sand addition were conducted and additionally, the influence of the cooling rate of the slag was examined. The remelted (without quartz sand) and the remelted modified slags (with quartz sand) were analyzed chemically and mineralogically and the leaching behavior was investigated. The modification of the slags yielded a minimized release of V and Cr, supporting the hypothesis that the FeO/SiO2 ratio influences the mineralogy and the leaching behavior.
Since the recycling of tantalum bearing post-consumer waste is practically not existent, metallurgical residues are the most important feed for the tantalum recycling. Most tin ores naturally contain significant quantities of refractory metals. During the smelting process in primary tin production these elements are enriched in the slag phase. This slag is a highly valuable raw material for tantalum production due to its considerable concentration of tantalum and its functioning as an additional slag former in further pyrometallurgical treatment.
In this paper the first process stage of an existing pyrometallurgical process for tantalum recovery, mainly from low grade pyrometallurgical residues, is discussed. Smelting trials were carried out in a pilot-scale electric arc furnace to analyse the effect of feeding on the activity of carbon as a reducing agent. Therefore, blowing petroleum coke through an iron lance and the manual adding of coke into the melting bath were tested. During the pyrometallurgical treatment elements with a high affinity to carbon were reduced to their carbide form and enriched in the molten iron-based metal phase. The objective of the process was to reduce the oxidic tantalum completely and to enrich it into the metal phase. Furthermore, the transfer of unwanted elements such as titanium into the metal phase was aimed to be avoided.
Spoon test specimens were taken from the liquid mineral melt to follow the evolution of the reduction process. The cooled down solidified melting bath was investigated by using the XRD and EDX method to characterise the slag system and to identify relevant mineral phases.
Gegenstand dieser Arbeit ist die Untersuchung eines bestehenden pyrometallurgischen Prozesses zur Rückgewinnung von Tantal und Niob aus metallurgischen Reststoffen mit vorwiegend niedriger Wertstoffkonzentration.
Zur näheren Erforschung der im vorliegenden Stoffsystem ablaufenden Reduktionsprozesse wurden in einem Elektrolichtbogenofen Schmelzversuche im Pilotmaßstab durchgeführt. Als Reduktionsmittel diente Koks, welcher mithilfe einer Argon-gespülten Eisenlanze in die flüssige mineralische Schmelze eingebracht wurde. Während der Reduktionsbehandlung werden Refraktärmetalle wie Tantal und Niob in ihre Carbide überführt und anschließend in der erschmolzenen eisenbasierten Metallphase am Boden des Reaktors angereichert. Neben Tantal und Niob gelangt auch ein Teil des im Einsatzmaterial enthaltenen Titans als unerwünschtes Begleitelement in die Metallphase.
Sein Großteil verbleibt jedoch als Oxid in der Schlacke und wird dort hauptsächlich im Mineral Perowskit (CaTiO3) gebunden. Die erstarrten Schlackeproben wurden mit verschiedenen Methoden wie Röntgenfluoreszensanalyse, Röntgenbeugung und Rasterelektronenmikroskopie mit gekoppelter energiedispersiver Röntgenanalyse untersucht, um die Bildung tantalhaltiger Mineralphasen zu verschiedenen Stadien des Reduktionsprozesses zu verfolgen.
Die hier gewonnenen Erkenntnisse zeigen, dass weniger die durch das Einblasen von Koks verursachte Reduktionsreaktion, sondern das Absinken der tantalreichen Eisentröpfchen in der flüssigen mineralischen Schmelze, gefolgt von ihrer Anreicherung in die Metallphase, für die Kinetik ausschlaggebend ist.
Die Klinkerphasenbildung durch Sinterung in Drehrohröfen bei der Herstellung von Portlandzementklinker (PZK) ist gründlich erforscht und optimiert. Im Hinblick auf mögliche ökonomische und ökologische Vorteile befassen sich aktuelle Forschungsvorhaben darüber hinaus mit der Herstellung von Klinkermineralen aus Stahlwerksschlacken, die eine vergleichbare chemische Zusammensetzung aufweisen.
Neuste Untersuchungen zeigen, dass nach der reduzierenden Behandlung schmelzflüssiger Linz-Donawitz-(LD)-Schlacken und Abscheidung des gebildeten metallischen Eisens eine mineralische Schlacke entsteht, die unabhängig von ihren Abkühlbedingungen ca. 50–60 Gew.% des wichtigsten Klinkerminerals Alit (C3S) enthält und eine hohe hydraulische Reaktivität aufweist.
Die Stabilität des Alits auch nach langsamer Abkühlung deutet auf eine Stabilisierung des Minerals durch Nebenelemente aus den LD-Schlacken hin. Ein sinkender Anteil an LD-Schlacke durch Zusatz synthetischer Schlackemischung, die sich hinsichtlich ihrer Hauptkomponenten wie eine ausreduzierte LD-Schlacke zusammensetzt, führt zu einem Rückgang des Alitgehaltes und dem Zerfall der Schlacke beim Erstarren.