Sewage sludge and sewage sludge ashes (SSA) are produced in huge amounts at municipal waste water treatment plants (WWTP) all around the world and have become an issue for many urbanized areas. To deal with this unceasing mass flow in an ecologically and economically responsible way a comprehensive chemical and structural characterization of all types of SSA is needed. X-ray powder diffraction (XRD) is one of the most promising analytical methods for this task. Although, there has been ample chemical evidence showing that many SSA contain aluminium phosphate as a major component up to now no aluminium phosphate or aluminium-rich mixed phosphate phase has been reported to be identified by XRD in a SSA produced at a mono-incineration facility. The outcome of the present com-bined XRD and Mossbauer spectroscopy investigation provides comprehensive evidence closing this gap for the first time.
Slags from the production of high-alloyed steel contain both chemically bound chromium (mainly as Cr2O3) in the mineral fraction and elemental chromium in the metallic remainders. Thermochemical post treatment of the slag in an electric arc furnace under reducing conditions enables the nearly complete recovery of the total amount of chromium in form of a metallic alloy. The best results were achieved by resistance melting (submerged electrodes) with addition of a reducing agent into the melt. The efficiencies of the reducing agents carbon, aluminium, silicon (as ferrosilicon) and silicon carbide were investigated and compared. As aluminium is the strongest reducing agent, it is less selective and reduces much more SiO2 than Cr2O3. While SiC shows only low reactivity because of its high thermal resistance, carbon and silicon had the highest reducing potentials: More than 97% of the chemically bound chromium can be recovered by application of these reducing agents. Due to the high temperature required for the reduction of the chromium compounds, the reduction of SiO2 as an undesired side reaction cannot be avoided. However, compared with mechanical procedures that are limited to the recovery of the metallic remainders, the total chromium recovery can be significantly increased by the described reductive melting procedure.
Based on recently published research on leaching control mechanisms in electric arc furnace (EAF) slags, it is assumed that a FeO/SiO2 ratio of around one leads to low leached V and Cr concentrations. This ratio influences the mineral phase composition of the slag toward higher amounts of spinel and a lower solubility of calcium silicate phases by suppressing the formation of magnesiowuestite and highly soluble calcium silicate phases. To evaluate this hypothesis, laboratory and scaled up tests in an EAF pilot plant were performed on slag samples characterized by elevated V and Cr leaching and a high FeO/SiO2 ratio. Prior to the melting experiments, the optimum FeO/SiO2 ratio was calculated via FactSageTM. In the melting experiments, the ratio was adjusted by adding quartz sand, which also decreased the basicity (CaO/SiO2) of the slag. As a reference, remelting experiments without quartz sand addition were conducted and additionally, the influence of the cooling rate of the slag was examined. The remelted (without quartz sand) and the remelted modified slags (with quartz sand) were analyzed chemically and mineralogically and the leaching behavior was investigated. The modification of the slags yielded a minimized release of V and Cr, supporting the hypothesis that the FeO/SiO2 ratio influences the mineralogy and the leaching behavior.
Basic oxygen furnace slags (BOFS) are by-products of the steelmaking process. Several researchers have studied the production of Portland cement clinker and metallic iron from BOFS via a reductive treatment.
In this study, we applied a carbothermal reduction of BOFS in a technical-scale electric arc furnace and characterised the clinker-like products. Those clinker-like non-metallic products (NMPs) had a chemical and mineralogical composition comparable to clinker for ordinary Portland cement (OPC) and contained large elongated alite crystals as major component. The pure NMPs reacted more slowly and achieved a lower degree of hydration compared with commercial OPC.
If the reactivity of the products can be further increased by employing specific adaptations, it can be used as a full clinker substitute for OPC. Nevertheless, it is also an option to use the material without further modifications as a cement component or concrete addition, which contributes to the strength development in both cases.
Based on recently published research on leaching control mechanisms in electric arc furnace (EAF) slags, it is assumed that a FeO/SiO2 ratio of around one leads to low leached V and Cr concentrations. This ratio influences the mineral phase composition of the slag toward higher amounts of spinel and a lower solubility of calcium silicate phases by suppressing the formation of magnesiowuestite and highly soluble calcium silicate phases. To evaluate this hypothesis, laboratory and scaled up tests in an EAF pilot plant were performed on slag samples characterized by elevated V and Cr leaching and a high FeO/SiO2 ratio. Prior to the melting experiments, the optimum FeO/SiO2 ratio was calculated via FactSageTM. In the melting experiments, the ratio was adjusted by adding quartz sand, which also decreased the basicity (CaO/SiO2) of the slag. As a reference, remelting experiments without quartz sand addition were conducted and additionally, the influence of the cooling rate of the slag was examined. The remelted (without quartz sand) and the remelted modified slags (with quartz sand) were analyzed chemically and mineralogically and the leaching behavior was investigated. The modification of the slags yielded a minimized release of V and Cr, supporting the hypothesis that the FeO/SiO2 ratio influences the mineralogy and the leaching behavior.
Fused cement clinker can be produced from molten basic oxygen furnace slag (BOFS) by way of a reductive thermochemical treatment. During the thermochemical treatment, oxidic iron is reduced to metallic iron and separated. The resulting low-iron slag has a chemical and mineralogical composition similar to ordinary Portland cement (OPC) clinker. In this study, the hydraulic reactivity of the fused clinker from BOFS with and without gypsum was investigated using isothermal calorimetry, differential scanning calorimetry, in situ X-ray diffraction and powder X-ray diffraction. Furthermore, a synthetic fused clinker without foreign ions and fused clinker produced by a mixture of both materials was studied. The hydraulic reaction of the fused clinker from BOFS was considerably slower than that of OPC. However, the reaction can be accelerated by adding gypsum as a sulfate carrier. Furthermore, the results showed an increased reaction rate with decreasing content of foreign ions such as Fe, P or Mn.