Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (17)
Sprache
- Englisch (13)
- Deutsch (3)
- Mehrsprachig (1)
Referierte Publikation
- ja (17) (entfernen)
Schlagworte
- Aluminium phosphate (3)
- Sewage sludge ash (3)
- Arc furnace (2)
- Ash (2)
- Incinerator ash (2)
- Leaching control mechanisms (2)
- Lichtbogenofen (2)
- Melting experiments (2)
- Thermochemical treatment (2)
- AOD slag (1)
Organisationseinheit der BAM
Slags from the production of high-alloyed steel contain both chemically bound chromium (mainly as Cr2O3) in the mineral fraction and elemental chromium in the metallic remainders. Thermochemical post treatment of the slag in an electric arc furnace under reducing conditions enables the nearly complete recovery of the total amount of chromium in form of a metallic alloy. The best results were achieved by resistance melting (submerged electrodes) with addition of a reducing agent into the melt. The efficiencies of the reducing agents carbon, aluminium, silicon (as ferrosilicon) and silicon carbide were investigated and compared. As aluminium is the strongest reducing agent, it is less selective and reduces much more SiO2 than Cr2O3. While SiC shows only low reactivity because of its high thermal resistance, carbon and silicon had the highest reducing potentials: More than 97% of the chemically bound chromium can be recovered by application of these reducing agents. Due to the high temperature required for the reduction of the chromium compounds, the reduction of SiO2 as an undesired side reaction cannot be avoided. However, compared with mechanical procedures that are limited to the recovery of the metallic remainders, the total chromium recovery can be significantly increased by the described reductive melting procedure.
Für die vollständige Rückgewinnung des in Edelstahlschlacken enthaltenen Chroms wird eine reduzierende Schmelzbehandlung im Elektro-Lichtbogenofen vorgeschlagen. Dabei wird das in der Schlacke enthaltene Cr2O3 zum Metall reduziert und in der schmelzflüssigen Phase separiert. Die Effektivität der Reduktion wird entscheidend durch die Fahrweise des Lichtbogenofens bestimmt. Mit optimalen Bedingungen lassen sich mehr als 90 % des enthaltenen Chroms als metallische Legierung zurückgewinnen
Based on recently published research on leaching control mechanisms in electric arc furnace (EAF) slags, it is assumed that a FeO/SiO2 ratio of around one leads to low leached V and Cr concentrations. This ratio influences the mineral phase composition of the slag toward higher amounts of spinel and a lower solubility of calcium silicate phases by suppressing the formation of magnesiowuestite and highly soluble calcium silicate phases. To evaluate this hypothesis, laboratory and scaled up tests in an EAF pilot plant were performed on slag samples characterized by elevated V and Cr leaching and a high FeO/SiO2 ratio. Prior to the melting experiments, the optimum FeO/SiO2 ratio was calculated via FactSageTM. In the melting experiments, the ratio was adjusted by adding quartz sand, which also decreased the basicity (CaO/SiO2) of the slag. As a reference, remelting experiments without quartz sand addition were conducted and additionally, the influence of the cooling rate of the slag was examined. The remelted (without quartz sand) and the remelted modified slags (with quartz sand) were analyzed chemically and mineralogically and the leaching behavior was investigated. The modification of the slags yielded a minimized release of V and Cr, supporting the hypothesis that the FeO/SiO2 ratio influences the mineralogy and the leaching behavior.
A model regarding the generation of acidity in binary metal fluorides has been proposed and its validity has been examined for several binary fluoride systems with the general compositions MF3/M'F3 and MF2/M'F3. In accordance with this hypothesis, the binary systems (CrF3/AlF3, CrF3/FeF3 and AlF3/VF3) do not show acidities larger than the sum of the acidities of the component fluorides. The hypothesis predicts the generation of Lewis acidity when MF2 is the major component (host) and generation of Brønsted acidity when MF3 acts as the host for the MF2/M'F3. The experimental results (surface acidity and catalytic activity) confirmed the predictions made from this hypothesis for binary combinations MgF2/ M'F3 (M'=Cr, Al, Fe, V). The application of this model is discussed in terms of other parameters: ionic radii and the fluoride affinity of the metal fluorides involved.
Based on recently published research on leaching control mechanisms in electric arc furnace (EAF) slags, it is assumed that a FeO/SiO2 ratio of around one leads to low leached V and Cr concentrations. This ratio influences the mineral phase composition of the slag toward higher amounts of spinel and a lower solubility of calcium silicate phases by suppressing the formation of magnesiowuestite and highly soluble calcium silicate phases. To evaluate this hypothesis, laboratory and scaled up tests in an EAF pilot plant were performed on slag samples characterized by elevated V and Cr leaching and a high FeO/SiO2 ratio. Prior to the melting experiments, the optimum FeO/SiO2 ratio was calculated via FactSageTM. In the melting experiments, the ratio was adjusted by adding quartz sand, which also decreased the basicity (CaO/SiO2) of the slag. As a reference, remelting experiments without quartz sand addition were conducted and additionally, the influence of the cooling rate of the slag was examined. The remelted (without quartz sand) and the remelted modified slags (with quartz sand) were analyzed chemically and mineralogically and the leaching behavior was investigated. The modification of the slags yielded a minimized release of V and Cr, supporting the hypothesis that the FeO/SiO2 ratio influences the mineralogy and the leaching behavior.
For the first time evidence is provided that a nanocrystalline and stacking-disordered, chemically stabilized β-cristobalite form of AlPO4 occurs in a sewage sludge ash (SSA). This proof is based on a combined X-ray powder diffraction and X-ray fluorescence investigation of an SSA produced at a large-scale fluidized bed incineration facility serving a catching area with a population of 2 million. The structural and chemical characterization was carried out on 'as received' SSA samples as well as on solid residues remaining after leaching this SSA in sodium hydroxide solution. Thus, it was ascertained that the observed nanocrystalline and stacking-disordered cristobalite-like component belongs to the aluminum phosphate component of this SSA, rather than to its silicon dioxide component. In addition, a direct proof is presented that the chemically stabilized β-cristobalite form of AlPO4 does crystallize from X-ray amorphous precursors under conditions that mimic the huge heating rate and short retention time (just seconds at T ≈ 850°C), typical for fluidized bed incinerators.
Evidence is provided that the tridymite component observed in the X-ray diffraction patterns of some sewage sludge ashes (SSAs) should not be interpreted as the tridymite modification of SiO2 but as the tridymite form of AlPO4. This proof is based on a combined X-ray Powder Diffraction (XRD), X-ray fluorescence (XRF) and Mossbauer spectroscopy investigation of two SSAs produced at two fluidized bed incineration facilities, located in different municipalities and operated differently. The structural and chemical characterization was carried out on the 'as received' SSA samples as well as on the residues of these two SSAs pretreated by leaching in citric acid. In addition, direct proof is presented that the tridymite form of AlPO4 does crystallize from X-ray amorphous precursors under conditions that mimic the huge heating rate and short retention time (just seconds at T ≈ 850 °C) typical for fluidized bed incinerators.
Sewage sludge and sewage sludge ashes (SSA) are produced in huge amounts at municipal waste water treatment plants (WWTP) all around the world and have become an issue for many urbanized areas. To deal with this unceasing mass flow in an ecologically and economically responsible way a comprehensive chemical and structural characterization of all types of SSA is needed. X-ray powder diffraction (XRD) is one of the most promising analytical methods for this task. Although, there has been ample chemical evidence showing that many SSA contain aluminium phosphate as a major component up to now no aluminium phosphate or aluminium-rich mixed phosphate phase has been reported to be identified by XRD in a SSA produced at a mono-incineration facility. The outcome of the present com-bined XRD and Mossbauer spectroscopy investigation provides comprehensive evidence closing this gap for the first time.
This paper reports the first successful synthesis and the structural characterization of nanocrystalline and stacking-disordered β-cristobalite AlPO4 that is chemically stabilized down to room temperature and free of crystalline impurity phases. Several batches of the title compound were synthesized and thoroughly characterized by X-ray powder diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy, selected area electron diffraction, energy dispersive X-ray spectroscopy mapping in SEM, solid-state 31P nuclear magnetic resonance (31P-NMR) spectroscopy including the TRAPDOR method, differential thermal analysis (DTA), gas-sorption methods, optical Emission spectroscopy, X-ray fluorescence spectroscopy, and ion chromatography. Parameters that are critical for the synthesis were identified and optimized. The synthesis procedure yields reproducible results and is well documented. A high-quality XRD pattern of the title compound is presented, which was collected with monochromatic copper radiation at room temperature in a wide 2θ range of 5°–100°.