The material properties of recycled concrete aggregates (RCA) are
correlated to the sorting accuracy of the former demolition waste. Impurities like
wood, clay bricks or gypsum can lead to inferior building material properties. Harmful
substances like heavy metals or organic pollutants should be minimised as well.
Hence the non-concrete materials have to be separated from the concrete material
stream. This can be done during the demolition process by using selective
dismantling techniques. Alternatively a variety sorting and classifying techniques to
purify the crushed concrete can be utilized.
A research project, funded by the Federal Ministry for the Environment, Nature
Conservation and Nuclear Safety, investigated the possibilities of gaining recycled
concrete aggregates of a high quality for the reuse in the production of concrete. The
work focuses especially on how gypsum respectively sulphates in the crushed
concrete can be reduced. Sulphates can impair the setting behaviour of concrete
and also damage set concrete by causing expansion. Therefore the content of
sulphates in RCA is restricted by guidelines and standards in Germany.
Generally, gypsum in construction waste originates from interior fittings like gypsum
walls, floor screeds, plaster boards and also plaster. Most of these materials can be
reconstructed using selective dismantling techniques. This can be achieved either by
manual labour or by using mechanical equipment e.g. to remove floor screeds by
milling. Depending on the specific deconstruction site it can be more effective and/or
more environmentally compatible to remove sulphates by treating the crushed
concrete. Applicable treatments for sulphate reduction include dry processes like
manual sorting of gypsum wall blocks as well as wet treatments e.g. jigging.
In addition this research project an environmental performance evaluation was
undertaken to assess different techniques for reducing sulphates in recycled
concrete aggregates.
Tricalcium-silicate (C3S) or Alite is the most important mineral in Portland cement. Since pure tricalcium-silicate is only stable above temperatures of 1250 °C, its decomposition has to be prevented technically by fast cooling after the sintering process. At room temperature, the decomposition velocity is very slow so that metastable tricalcium-silicate is obtained.
Although the mechanisms of clinker phase formation during burning process of Portland cement in a rotary kiln were solved and improved over the years, in view of possible economic and ecological benefits current projects aim to produce clinker phases from metallurgical slags. Recent studies discovered that the mineral phase which remained after a reducing treatment and separation of formed metallic iron from molten Linz-Donawitz (LD-) slags contained about 60 wt.% Alite despite it was cooled slowly. Because the results could be verified using slags from different origins and varying cooling velocities a chemical stabilisation of the Alite can be assumed. First tests in mortars indicate that workability, hardening and solid state properties are comparable with an ordinary Portland cement. An application of the observed phenomenon in cement production requires enhanced knowledge about formation and stabilisation conditions of Alite during crystallisation from melts in contrast to the sintering reactions in conventional Portland cement production. Therefore, this study focuses on the stabilisation mechanisms of Alite in consolidating melts. Samples from different melting experiments are analysed to determine stabilising factors.