Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (15)
- Beitrag zu einem Tagungsband (8)
- Beitrag zu einem Sammelband (1)
- Vortrag (1)
- Posterpräsentation (1)
Sprache
- Englisch (26) (entfernen)
Schlagworte
- Aluminium phosphate (3)
- Sewage sludge ash (3)
- Thermochemical treatment (3)
- Ash (2)
- Corrosion (2)
- Incinerator ash (2)
- Leaching control mechanisms (2)
- Melting experiments (2)
- Pyrometallurgy (2)
- Refractories (2)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (1)
The recycling of refractory materials in the chemical, metallurgical and glass industry has only had minor relevance until now because of the high performance required from these materials (stability against corrosion, inert when coming into contact with the glass melt, etc.). Refractory lifetimes are limited because of corrosion at higher temperatures. The best furnace lifetimes has been achieved with chromium oxide and chromium oxide corund refractories. Waste from the production and use of refractory material is generated in three main forms: as residues from cutting and grinding, as refractories which have limited or no contact with glass melts, and as refractories with infiltration of sublimation residues or condensates. The waste material is classified as hazardous waste due to its chromium content. In this study, arc furnace technology was used for thermal treatment of the waste materials to enable recycling of refractory materials. (author abst.)
A model regarding the generation of acidity in binary metal fluorides has been proposed and its validity has been examined for several binary fluoride systems with the general compositions MF3/M'F3 and MF2/M'F3. In accordance with this hypothesis, the binary systems (CrF3/AlF3, CrF3/FeF3 and AlF3/VF3) do not show acidities larger than the sum of the acidities of the component fluorides. The hypothesis predicts the generation of Lewis acidity when MF2 is the major component (host) and generation of Brønsted acidity when MF3 acts as the host for the MF2/M'F3. The experimental results (surface acidity and catalytic activity) confirmed the predictions made from this hypothesis for binary combinations MgF2/ M'F3 (M'=Cr, Al, Fe, V). The application of this model is discussed in terms of other parameters: ionic radii and the fluoride affinity of the metal fluorides involved.
The material properties of recycled concrete aggregates (RCA) are
correlated to the sorting accuracy of the former demolition waste. Impurities like
wood, clay bricks or gypsum can lead to inferior building material properties. Harmful
substances like heavy metals or organic pollutants should be minimised as well.
Hence the non-concrete materials have to be separated from the concrete material
stream. This can be done during the demolition process by using selective
dismantling techniques. Alternatively a variety sorting and classifying techniques to
purify the crushed concrete can be utilized.
A research project, funded by the Federal Ministry for the Environment, Nature
Conservation and Nuclear Safety, investigated the possibilities of gaining recycled
concrete aggregates of a high quality for the reuse in the production of concrete. The
work focuses especially on how gypsum respectively sulphates in the crushed
concrete can be reduced. Sulphates can impair the setting behaviour of concrete
and also damage set concrete by causing expansion. Therefore the content of
sulphates in RCA is restricted by guidelines and standards in Germany.
Generally, gypsum in construction waste originates from interior fittings like gypsum
walls, floor screeds, plaster boards and also plaster. Most of these materials can be
reconstructed using selective dismantling techniques. This can be achieved either by
manual labour or by using mechanical equipment e.g. to remove floor screeds by
milling. Depending on the specific deconstruction site it can be more effective and/or
more environmentally compatible to remove sulphates by treating the crushed
concrete. Applicable treatments for sulphate reduction include dry processes like
manual sorting of gypsum wall blocks as well as wet treatments e.g. jigging.
In addition this research project an environmental performance evaluation was
undertaken to assess different techniques for reducing sulphates in recycled
concrete aggregates.
New horizons of the structural characterization of stainless steel slags by X-ray powder diffraction
(2007)
Evidence is provided that the tridymite component observed in the X-ray diffraction patterns of some sewage sludge ashes (SSAs) should not be interpreted as the tridymite modification of SiO2 but as the tridymite form of AlPO4. This proof is based on a combined X-ray Powder Diffraction (XRD), X-ray fluorescence (XRF) and Mossbauer spectroscopy investigation of two SSAs produced at two fluidized bed incineration facilities, located in different municipalities and operated differently. The structural and chemical characterization was carried out on the 'as received' SSA samples as well as on the residues of these two SSAs pretreated by leaching in citric acid. In addition, direct proof is presented that the tridymite form of AlPO4 does crystallize from X-ray amorphous precursors under conditions that mimic the huge heating rate and short retention time (just seconds at T ≈ 850 °C) typical for fluidized bed incinerators.
Basic oxygen furnace slags (BOFS) are by-products of the steelmaking process. Several researchers have studied the production of Portland cement clinker and metallic iron from BOFS via a reductive treatment.
In this study, we applied a carbothermal reduction of BOFS in a technical-scale electric arc furnace and characterised the clinker-like products. Those clinker-like non-metallic products (NMPs) had a chemical and mineralogical composition comparable to clinker for ordinary Portland cement (OPC) and contained large elongated alite crystals as major component. The pure NMPs reacted more slowly and achieved a lower degree of hydration compared with commercial OPC.
If the reactivity of the products can be further increased by employing specific adaptations, it can be used as a full clinker substitute for OPC. Nevertheless, it is also an option to use the material without further modifications as a cement component or concrete addition, which contributes to the strength development in both cases.
Based on recently published research on leaching control mechanisms in electric arc furnace (EAF) slags, it is assumed that a FeO/SiO2 ratio of around one leads to low leached V and Cr concentrations. This ratio influences the mineral phase composition of the slag toward higher amounts of spinel and a lower solubility of calcium silicate phases by suppressing the formation of magnesiowuestite and highly soluble calcium silicate phases. To evaluate this hypothesis, laboratory and scaled up tests in an EAF pilot plant were performed on slag samples characterized by elevated V and Cr leaching and a high FeO/SiO2 ratio. Prior to the melting experiments, the optimum FeO/SiO2 ratio was calculated via FactSageTM. In the melting experiments, the ratio was adjusted by adding quartz sand, which also decreased the basicity (CaO/SiO2) of the slag. As a reference, remelting experiments without quartz sand addition were conducted and additionally, the influence of the cooling rate of the slag was examined. The remelted (without quartz sand) and the remelted modified slags (with quartz sand) were analyzed chemically and mineralogically and the leaching behavior was investigated. The modification of the slags yielded a minimized release of V and Cr, supporting the hypothesis that the FeO/SiO2 ratio influences the mineralogy and the leaching behavior.
Slags from the production of high-alloyed steel contain both chemically bound chromium (mainly as Cr2O3) in the mineral fraction and elemental chromium in the metallic remainders. Thermochemical post treatment of the slag in an electric arc furnace under reducing conditions enables the nearly complete recovery of the total amount of chromium in form of a metallic alloy. The best results were achieved by resistance melting (submerged electrodes) with addition of a reducing agent into the melt. The efficiencies of the reducing agents carbon, aluminium, silicon (as ferrosilicon) and silicon carbide were investigated and compared. As aluminium is the strongest reducing agent, it is less selective and reduces much more SiO2 than Cr2O3. While SiC shows only low reactivity because of its high thermal resistance, carbon and silicon had the highest reducing potentials: More than 97% of the chemically bound chromium can be recovered by application of these reducing agents. Due to the high temperature required for the reduction of the chromium compounds, the reduction of SiO2 as an undesired side reaction cannot be avoided. However, compared with mechanical procedures that are limited to the recovery of the metallic remainders, the total chromium recovery can be significantly increased by the described reductive melting procedure.
Sewage sludge and sewage sludge ashes (SSA) are produced in huge amounts at municipal waste water treatment plants (WWTP) all around the world and have become an issue for many urbanized areas. To deal with this unceasing mass flow in an ecologically and economically responsible way a comprehensive chemical and structural characterization of all types of SSA is needed. X-ray powder diffraction (XRD) is one of the most promising analytical methods for this task. Although, there has been ample chemical evidence showing that many SSA contain aluminium phosphate as a major component up to now no aluminium phosphate or aluminium-rich mixed phosphate phase has been reported to be identified by XRD in a SSA produced at a mono-incineration facility. The outcome of the present com-bined XRD and Mossbauer spectroscopy investigation provides comprehensive evidence closing this gap for the first time.
For the first time evidence is provided that a nanocrystalline and stacking-disordered, chemically stabilized β-cristobalite form of AlPO4 occurs in a sewage sludge ash (SSA). This proof is based on a combined X-ray powder diffraction and X-ray fluorescence investigation of an SSA produced at a large-scale fluidized bed incineration facility serving a catching area with a population of 2 million. The structural and chemical characterization was carried out on 'as received' SSA samples as well as on solid residues remaining after leaching this SSA in sodium hydroxide solution. Thus, it was ascertained that the observed nanocrystalline and stacking-disordered cristobalite-like component belongs to the aluminum phosphate component of this SSA, rather than to its silicon dioxide component. In addition, a direct proof is presented that the chemically stabilized β-cristobalite form of AlPO4 does crystallize from X-ray amorphous precursors under conditions that mimic the huge heating rate and short retention time (just seconds at T ≈ 850°C), typical for fluidized bed incinerators.
Tricalcium-silicate (C3S) or Alite is the most important mineral in Portland cement. Since pure tricalcium-silicate is only stable above temperatures of 1250 °C, its decomposition has to be prevented technically by fast cooling after the sintering process. At room temperature, the decomposition velocity is very slow so that metastable tricalcium-silicate is obtained.
Although the mechanisms of clinker phase formation during burning process of Portland cement in a rotary kiln were solved and improved over the years, in view of possible economic and ecological benefits current projects aim to produce clinker phases from metallurgical slags. Recent studies discovered that the mineral phase which remained after a reducing treatment and separation of formed metallic iron from molten Linz-Donawitz (LD-) slags contained about 60 wt.% Alite despite it was cooled slowly. Because the results could be verified using slags from different origins and varying cooling velocities a chemical stabilisation of the Alite can be assumed. First tests in mortars indicate that workability, hardening and solid state properties are comparable with an ordinary Portland cement. An application of the observed phenomenon in cement production requires enhanced knowledge about formation and stabilisation conditions of Alite during crystallisation from melts in contrast to the sintering reactions in conventional Portland cement production. Therefore, this study focuses on the stabilisation mechanisms of Alite in consolidating melts. Samples from different melting experiments are analysed to determine stabilising factors.
The environmental concerns about availability of fossil fuels and greenhouse gas effect increase and alternative renewable fuels for power plants are gaining significantly of importance. One of the alternative renewable fuels is biomass but it is a difficult fuel because of its diversity and complexity. It can contain high percentages of K and Cl responsible for corrosion together with sand that have additionally an abrasive effect during combustion. Because of permanently extending the surface reaction due to abrasion the corrosion of the materials increases. In particular in power plants, the superheater tubes are exposed to a corrosive abrasive attack that is one of the main sources of concern. The development of new alloys for multilayer surface, which combines corrosive and abrasive resistance is therefore of high importance. Those new technical approaches must be at the same time cost-effective to be an alternative to conventional materials. This paper presents the principle of experimental methods developed for the investigations of high temperature corrosion combined with abrasion in thermochemical processes with high hydrochloric acid concentrations like during biomass combustion. The aim of the presented investigation methods it to test and develop suitable alloys for coatings for the super heater tubes of biomass power plants. First results of abrasion investigations show improved abrasion resistance compared to the multi-component reference material Alloy 625.