The recycling of refractory materials in the chemical, metallurgical and glass industry has only had minor relevance until now because of the high performance required from these materials (stability against corrosion, inert when coming into contact with the glass melt, etc.). Refractory lifetimes are limited because of corrosion at higher temperatures. The best furnace lifetimes has been achieved with chromium oxide and chromium oxide corund refractories. Waste from the production and use of refractory material is generated in three main forms: as residues from cutting and grinding, as refractories which have limited or no contact with glass melts, and as refractories with infiltration of sublimation residues or condensates. The waste material is classified as hazardous waste due to its chromium content. In this study, arc furnace technology was used for thermal treatment of the waste materials to enable recycling of refractory materials. (author abst.)
A model regarding the generation of acidity in binary metal fluorides has been proposed and its validity has been examined for several binary fluoride systems with the general compositions MF3/M'F3 and MF2/M'F3. In accordance with this hypothesis, the binary systems (CrF3/AlF3, CrF3/FeF3 and AlF3/VF3) do not show acidities larger than the sum of the acidities of the component fluorides. The hypothesis predicts the generation of Lewis acidity when MF2 is the major component (host) and generation of Brønsted acidity when MF3 acts as the host for the MF2/M'F3. The experimental results (surface acidity and catalytic activity) confirmed the predictions made from this hypothesis for binary combinations MgF2/ M'F3 (M'=Cr, Al, Fe, V). The application of this model is discussed in terms of other parameters: ionic radii and the fluoride affinity of the metal fluorides involved.
New horizons of the structural characterization of stainless steel slags by X-ray powder diffraction
(2007)
Für die vollständige Rückgewinnung des in Edelstahlschlacken enthaltenen Chroms wird eine reduzierende Schmelzbehandlung im Elektro-Lichtbogenofen vorgeschlagen. Dabei wird das in der Schlacke enthaltene Cr2O3 zum Metall reduziert und in der schmelzflüssigen Phase separiert. Die Effektivität der Reduktion wird entscheidend durch die Fahrweise des Lichtbogenofens bestimmt. Mit optimalen Bedingungen lassen sich mehr als 90 % des enthaltenen Chroms als metallische Legierung zurückgewinnen
Evidence is provided that the tridymite component observed in the X-ray diffraction patterns of some sewage sludge ashes (SSAs) should not be interpreted as the tridymite modification of SiO2 but as the tridymite form of AlPO4. This proof is based on a combined X-ray Powder Diffraction (XRD), X-ray fluorescence (XRF) and Mossbauer spectroscopy investigation of two SSAs produced at two fluidized bed incineration facilities, located in different municipalities and operated differently. The structural and chemical characterization was carried out on the 'as received' SSA samples as well as on the residues of these two SSAs pretreated by leaching in citric acid. In addition, direct proof is presented that the tridymite form of AlPO4 does crystallize from X-ray amorphous precursors under conditions that mimic the huge heating rate and short retention time (just seconds at T ≈ 850 °C) typical for fluidized bed incinerators.
Basic oxygen furnace slags (BOFS) are by-products of the steelmaking process. Several researchers have studied the production of Portland cement clinker and metallic iron from BOFS via a reductive treatment.
In this study, we applied a carbothermal reduction of BOFS in a technical-scale electric arc furnace and characterised the clinker-like products. Those clinker-like non-metallic products (NMPs) had a chemical and mineralogical composition comparable to clinker for ordinary Portland cement (OPC) and contained large elongated alite crystals as major component. The pure NMPs reacted more slowly and achieved a lower degree of hydration compared with commercial OPC.
If the reactivity of the products can be further increased by employing specific adaptations, it can be used as a full clinker substitute for OPC. Nevertheless, it is also an option to use the material without further modifications as a cement component or concrete addition, which contributes to the strength development in both cases.
Based on recently published research on leaching control mechanisms in electric arc furnace (EAF) slags, it is assumed that a FeO/SiO2 ratio of around one leads to low leached V and Cr concentrations. This ratio influences the mineral phase composition of the slag toward higher amounts of spinel and a lower solubility of calcium silicate phases by suppressing the formation of magnesiowuestite and highly soluble calcium silicate phases. To evaluate this hypothesis, laboratory and scaled up tests in an EAF pilot plant were performed on slag samples characterized by elevated V and Cr leaching and a high FeO/SiO2 ratio. Prior to the melting experiments, the optimum FeO/SiO2 ratio was calculated via FactSageTM. In the melting experiments, the ratio was adjusted by adding quartz sand, which also decreased the basicity (CaO/SiO2) of the slag. As a reference, remelting experiments without quartz sand addition were conducted and additionally, the influence of the cooling rate of the slag was examined. The remelted (without quartz sand) and the remelted modified slags (with quartz sand) were analyzed chemically and mineralogically and the leaching behavior was investigated. The modification of the slags yielded a minimized release of V and Cr, supporting the hypothesis that the FeO/SiO2 ratio influences the mineralogy and the leaching behavior.
Stahlwerksschlacken besitzen keine ausgeprägte Hydraulizität. Deshalb haben sie bislang als Kompositmaterial im Zement noch keine Verbreitung gefunden. Stattdessen werden LD-Konverter- und Elektroofen-Schlacken insbesondere im Straßenbau in ungebundenen Tragschichten, aber auch in bituminös gebundenen Trag- und Deckschichten eingesetzt. Das Ziel einer zentralen Forschungsaufgabe bei der Loesche GmbH war und ist die Modifizierung dieser Schlacken, um daraus Produkte mit hohen Gebrauchswerteigenschaften zu generieren. Durch die Modifikationen soll hydraulisch hochreaktives Material bei gleichzeitiger Rückgewinnung des Metallinhaltes erzeugt werden.