Filtern
Erscheinungsjahr
Dokumenttyp
- Beitrag zu einem Tagungsband (47)
- Zeitschriftenartikel (46)
- Vortrag (40)
- Forschungsdatensatz (12)
- Beitrag zu einem Sammelband (9)
- Forschungsbericht (6)
- Buchkapitel (5)
- Monografie (3)
- Posterpräsentation (3)
Sprache
- Englisch (99)
- Deutsch (68)
- Mehrsprachig (3)
- Portugiesisch (1)
Schlagworte
- Microstructure (16)
- Creep (14)
- TMF (10)
- Aging (9)
- Coarsening (9)
- LCF (8)
- Fatigue (7)
- Transmission electron microscopy (7)
- Aluminium (6)
- S-phase (6)
Organisationseinheit der BAM
- 5 Werkstofftechnik (80)
- 5.2 Metallische Hochtemperaturwerkstoffe (79)
- 5.5 Materialmodellierung (12)
- 9 Komponentensicherheit (10)
- 5.1 Mikrostruktur Design und Degradation (9)
- 8 Zerstörungsfreie Prüfung (8)
- 9.6 Additive Fertigung metallischer Komponenten (6)
- 8.5 Röntgenbildgebung (5)
- 8.0 Abteilungsleitung und andere (3)
- 9.3 Schweißtechnische Fertigungsverfahren (3)
Eingeladener Vortrag
- nein (40)
The uniaxial, torsional and axial-torsional thermomechanical fatigue (TMF) behavior of the near-γ TiAl-alloy TNB-V5 was investigated. TMF tests were performed at 400-800 °C with mechanical strain amplitudes ranging from 0.15% to 0.7%. The tests were conducted thermomechanically in-phase (IP) and out-of-phase (OP).
For the same lifetimes, uniaxial IP tests required the highest strain amplitudes, while OP test conditions were most damaging and needed the lowest strain amplitudes. The Mises equivalent mechanical strain amplitudes of pure torsional tests were found in between uniaxial in-phase and out-of-phase tests for the same lifetimes. The non-proportional multiaxial out-of-phase test showed a lower lifetime at the same equivalent mechanical strain amplitude compared to the other types of tests.
The microstructure has been characterized applying electron microscopy and microstructural parameters such as fraction of twinned grains, grain size, lamellar distance and dislocation density have been quantified.
The elastic properties (Young's modulus, shear modulus) of austenitic stainless steel AISI 316L were investigated between room temperature and 900 °C in an additively manufactured variant (laser powder bed fusion, PBF‑LB/M) and from a conventional process route (hot rolled sheet). The moduli were determined using the dynamic resonance method. The data set includes information on processing parameters, heat treatments, grain size, specimen dimensions and weight, Young’s and shear modulus as well as their measurement uncertainty.
The dataset was generated in an accredited testing lab using calibrated measuring equipment. The calibrations meet the requirements of the test procedure and are metrologically traceable. The dataset was audited as BAM reference data.