Filtern
Erscheinungsjahr
Dokumenttyp
- Beitrag zu einem Tagungsband (48)
- Zeitschriftenartikel (47)
- Vortrag (41)
- Forschungsdatensatz (12)
- Beitrag zu einem Sammelband (9)
- Forschungsbericht (6)
- Buchkapitel (5)
- Monografie (3)
- Posterpräsentation (3)
Sprache
- Englisch (102)
- Deutsch (68)
- Mehrsprachig (3)
- Portugiesisch (1)
Schlagworte
- Microstructure (16)
- Creep (14)
- TMF (10)
- Aging (9)
- Coarsening (9)
- LCF (8)
- Fatigue (7)
- Transmission electron microscopy (7)
- Aluminium (6)
- Ontology (6)
Organisationseinheit der BAM
- 5 Werkstofftechnik (83)
- 5.2 Metallische Hochtemperaturwerkstoffe (82)
- 5.5 Materialmodellierung (13)
- 9 Komponentensicherheit (11)
- 5.1 Mikrostruktur Design und Degradation (10)
- 8 Zerstörungsfreie Prüfung (9)
- 9.6 Additive Fertigung metallischer Komponenten (7)
- 8.5 Röntgenbildgebung (6)
- 8.0 Abteilungsleitung und andere (3)
- 9.3 Schweißtechnische Fertigungsverfahren (3)
- 9.4 Integrität von Schweißverbindungen (3)
- VP Vizepräsident (3)
- VP.1 eScience (3)
- 4 Material und Umwelt (2)
- 1 Analytische Chemie; Referenzmaterialien (1)
- 1.3 Instrumentelle Analytik (1)
- 3 Gefahrgutumschließungen; Energiespeicher (1)
- 3.4 Sicherheit von Lagerbehältern (1)
- 4.2 Material-Mikrobiom Wechselwirkungen (1)
- 4.3 Schadstofftransfer und Umwelttechnologien (1)
- 5.0 Abteilungsleitung und andere (1)
- 5.3 Polymere Verbundwerkstoffe (1)
- 5.4 Multimateriale Fertigungsprozesse (1)
- 5.6 Glas (1)
- 6 Materialchemie (1)
- 6.4 Materialinformatik (1)
- 7 Bauwerkssicherheit (1)
- 7.7 Modellierung und Simulation (1)
- 8.4 Akustische und elektromagnetische Verfahren (1)
- S Qualitätsinfrastruktur (1)
- S.0 Abteilungsleitung und andere (1)
Eingeladener Vortrag
- nein (41)
In diesem Forschungsvorhaben erfolgte eine Überprüfung der Übertragbarkeit der Werkstoff- und Rechenmodelle für die Lebensdauervorhersage von ATL-Heißteilen unter TMF-Beanspruchung auf eine andere Werkstoffklasse als im Vorgängervorhaben, d.h. auf das austenitische Gusseisen EN-GJSA-XNiSiCr35-5-2 (Ni-Resist D-5S). Zunächst wurde dafür eine experimentelle Datenbasis geschaffen, da diese vor Beginn des Vorhabens nicht ausreichend war. Dazu wurden Zug-, Kriech-, LCF- und TMF-Versuche durchgeführt, die der Kalibrierung der Modelle dienten. Das Spannungs-Verformungs-Verhalten und die Lebensdauer in den LCF- und TMF-Versuchen werden durch das Modell auch für den neuen Werkstoff überwiegend gut beschrieben. LCF-Versuche mit Haltezeit bei 900 °C sowie IP-TMFVersuche mit einer Obertemperatur von 900 °C werden weniger gut vorhergesagt, da sich der Schädigungsmechanismus ändert. Eine Verifikation des Modells erfolgte mit Hilfe eines Bauteilversuchs an einem Abgassammler. Die überwiegende Anzahl der experimentell ermittelten Rissorte wurden von dem Modell vorhergesagt.
Ein wesentliches Ziel des Vorhabens war, den Einfluss von HCF-Schwingungen auf die TMF-Lebensdauer vertieft experimentell zu untersuchen und das bereits bestehende Lebensdauermodell auf HCF-Überlagerung zu erweitern. Es wurde ein bruchmechanisch motivierter Ansatz entwickelt, in dem die Lebensdauerminderung durch die im TMF-Zyklus überlagerten HCF-Schwingungen abgebildet wird. Mit diesem Ansatz lassen sich die Lebensdauern sowohl für den Werkstoff SiMo 4.05 als auch für den Ni-Resist in guter Übereinstimmung mit dem Experiment Vorhersagen.
Das Ziel des Forschungsvorhabens ist erreicht worden.
Die warmfeste austenitische Gusseisenlegierung EN-GJSA-XNiSiCr35-5-2 (häufig auch als Ni-Resist D-5S bezeichnet) wurde hinsichtlich ihres mechanischen Verhaltens bei hoher Temperatur charakterisiert. Dazu wurden (isotherme) niederzyklische (LCF-) und (nicht-isotherme) thermomechanische Ermüdungsversuche (TMF) zwischen Raumtemperatur und 900 °C durchgeführt. Diese Ergebnisse dienten (zusammen mit weiteren Versuchsdaten) der Kalibrierung werkstoffmechanischer Modelle. Bei den höchsten Prüftemperaturen wurde Schädigung in Form von Kriechen beobachtet und metallographisch dokumentiert.
Simulation of the θ′ Precipitation Process with Interfacial Anisotropy Effects in Al-Cu Alloys
(2021)
The effects of anisotropic interfacial properties and heterogeneous elasticity on the growth and ripening of plate-like θ′-phase (Al2Cu) in Al-1.69 at.% Cu alloy are studied. Multi-phase-field simulations are conducted and discussed in comparison with aging experiments. The precipitate/matrix interface is considered to be anisotropic in terms of its energy and mobility. We find that the additional incorporation of an anisotropic interfacial mobility in conjunction with the elastic anisotropy result in substantially larger aspect ratios of the precipitates closer to the experimental observations. The anisotropy of the interfacial energy shows comparably small effect on the precipitate’s aspect ratio but changes the interface’s shape at the rim. The effect of the chemo-mechanical coupling, i.e., the composition dependence of the elastic constants, is studied as well. We show that the inverse ripening phenomenon, recently evidenced for δ’ precipitates in Al-Li alloys (Park et al. Sci. Rep. 2019, 9, 3981), does not establish for the θ′ precipitates. This is because of the anisotropic stress fields built around the θ′ precipitates, stemming from the precipitate’s shape and the interaction among different variants of the θ′ precipitate, that disturb the chemo-mechanical effects. These results show that the chemo-mechanical effects on the precipitation ripening strongly depend on the degree of sphericity and elastic isotropy of the precipitate and matrix phases.
MoSi alloys containing up to 1 wt.% Si were fabricated by powder-metallurgical processing and their lattice parameters, elastic constants, densities, grain sizes, strengths, ductilities, and fracture toughness values were measured. The yield strength was insensitive to the grain size, i.e., a HallPetch relationship was not observed. Generally, Si additions caused pronounced solid solution strengthening. However, for small Si concentrations (≤0.1 wt.%) solid solution softening was observed at room temperature and below. With increasing Si concentration, the room temperature ductility and fracture toughness dropped precipitously. This is attributed to the increase in strength and a transition from transgranular to intergranular fracture.
Die Messung spontaner magnetischer Streufelder ferromagnetischer Materialien wird als neue, Metal Magnetic Memory (MMM) genannte, Methode der zerstörungsfreien Prüfung (ZfP) angesehen, Schädigungen frühzeitig vorherzusagen. Die MMM Methode versucht, die sich gleichzeitig mit der Schadensentwicklung ausbildende lokale magnetische Struktur für die ZfP zu nutzen und zwar schon vor der eigentlichen Rissinitiierung. Das zugehörige Regelwerk ISO 24497 verspricht neben der Detektion von Mikrorissen und Inhomogenitäten des Werkstoffgefüges auch die Bestimmung des (Eigen-) Spannungszustandes. Neue, an der Bundesanstalt für Materialforschung und -prüfung für die ZfP angepasste GMR (Giant Magneto Resistance)-Sensorik erlaubt Magnetfeldmessungen mit einer Ortsauflösung im Mikrometerbereich. Mit höherer Ortsauflösung zeigen sich Unterschiede, jedoch keine Widersprüche zu bisher publizierten Daten. Ihnen wesentlich ist, dass es einige verwertbare Hinweise auf einen Zusammenhang von Restfeldmagnetisierung und Materialeigenschaften gibt.
Measurement of spontaneous magnetic stray field signals has been reported to be a promising tool for capturing macro-scale information of deformation states, defects and stress concentration zones in a material structure. This paper offers a new method for self-magnetic leakage field detection using a magneto-optical (MO) hand-held microscope. Its sensor has a dynamic field range between ±0.05 and ±2 kA/m and a lateral optical resolution of approx. 10 µm. We examined flat tensile test specimens of metastable austenitic steel AISI 304. Static tensile tests were repeatedly interrupted at various predetermined states of strain and the magnetic information was measured by the MO system. Comparative measurements using a high-precision magnetic field GMR-sensor, verify the outstanding capability of the MO microscope regarding spatial resolution of magnetic fields.
Evaluation of high spatial resolution imaging of magnetic stray fields for early damage detection
(2017)
The paper discusses the evaluation of elastic and plastic strain states in two low-carbon steels of the same steel group with high spatial resolution GMR (giant magneto resistance) sensors. The residual stress distributions of tungsten inert gas welded plates were determined by means of neutron diffraction as a reference. The normal component of local residual magnetic stray fields arise in the vicinity of the positions of maximum stress. The experiments performed on flat tensile specimen indicate that the boundaries of plastic deformations are a source of stray fields. The spatial variations of magnetic stray fields for both the weld and the tensile samples are in the order of the earths magnetic field.
It is widely accepted that the magnetic state of a ferromagnetic material may be irreversibly altered by mechanical loading due to magnetoelastic effects. A novel standardized nondestructive testing (NDT) technique uses weak magnetic stray fields, which are assumed to arise from inhomogeneous deformation, for structural health monitoring (i.e., for detection and assessment of damage). However, the mechanical and microstructural complexity of damage has hitherto only been insufficiently considered. The aim of this study is to discuss the phenomenon of inhomogeneous “self-magnetization” of a polycrystalline ferromagnetic material under inhomogeneous deformation experimentally and with stronger material-mechanical focus. To this end, notched specimens were elastically and plastically deformed. Surface magnetic states were measured by a three-axis giant magnetoresistant (GMR) sensor and were compared with strain field (digital image correlation) and optical topography measurements. It is demonstrated that the stray fields do not solely form due to magnetoelastic effects. Instead, inhomogeneous plastic deformation causes topography, which is one of the main origins for the magnetic stray field formation. Additionally, if not considered, topography may falsify the magnetic signals due to variable lift-off values. The correlation of magnetic vector components with mechanical tensors, particularly for multiaxial stress/strain states and inhomogeneous elastic-plastic deformations remains an issue.