The plastic deformation results in irreversible microstructure changes in the steel, which can be considered as the initial stage of the fracture process. However, detecting, monitoring and evaluating, damage states and small defects non-destructively in advance still proves challenging. It was reported in literature the phenomenon of the spontaneous emergence of weak magnetic fields in structural steels and pipelines, which originates due to heterogeneous mechanical and / or thermal stresses. This observation is not associated with induced phase transformations by deformation and appears to be a promising tool for the prior characterization of damage in ferromagnetic steels. To provide a better understanding of the physical bases of the process, the magnetic microstructure of such materials and the change of magnetic domains after undergoing plastic deformation were studied. For this purpose, a colloidal solution with paramagnetic particles in the nanometer scale (ferrofluid) was used, through the Bitter technique, in order to, not only observe a change in size of the magnetic domains of the material, but also changes in their morphology. Ferritic steels with different carbon contents (0.08%; 0.22% and 0.45%) were studied in this work.
The plastic deformation results in irreversible microstructure changes in the steel, which can be considered as the initial stage of the fracture process. However, detecting, monitoring and evaluating, damage states and small defects non-destructively in advance still proves challenging. Dubov reported the phenomenon of the spontaneous emergence of weak magnetic fields in ferritic structural steel and pipelines, which originate due to heterogeneous mechanical and / or thermal stresses. This observation is not associated with induced phase transformations by deformation and appears to be a promising tool for the prior characterization of damage in ferromagnetic steels. To provide a better understanding of the physical bases of the process, the magnetic microstructure of such materials and a change of magnetic domains after undergoing plastic deformation were studied. A colloidal solution with paramagnetic particles in the nanometer range (ferrofluid), which allowed, through the Bitter technique, not only to observe a change in size of the magnetic domains of the material, but also changes in their morphology. Ferritic steels with their concentrations of carbon in its composition (0.12%; 0.17% and 0.45%) were studied in this work.
Creep-fatigue of P92 in service-like tests with combined stress- and strain-controlled dwell times
(2023)
Complex service-like relaxation- and creep-fatigue tests with strain- and stress-controlled dwells and fatigue cycle durations of approx. 2200 s were performed exemplarily on a grade P92 steel at 620 ◦C in this study. The results indicate deviations in the prevailing creep mechanisms of long-term relaxation and creep dwells, affecting subsequent dwells, load shifts, and the macroscopic softening behavior quite differently. In addition, fracture surfaces and longitudinal metallographic sections reveal intergranular crack growth for complex loading with stress-controlled dwells, whereas complex strain-controlled tests enhance oxidation and transgranular crack propagation. These findings substantiate the limited transferability of relaxation-fatigue to creep-fatigue conditions.
The current competitive situation on electricity markets forces power plants into cyclic operation regimes with frequent load shifts and starts/shutdowns. In the present work, the cyclic mechanical behavior of ferritic-martensitic 9-12 % Cr steels under isothermal and thermomechanical loading was investigated for the example of grade P92 material. A continuous softening was observed under all loading conditions. The introduction of hold periods to the applied cycles reduced material lifetime, with most prominent effects at technologically relevant small strain levels. The microstructural characterization reveals a coarsening of the original “martensitic” lath-type microstructure to a structure with polygonal subgrains and reduced dislocation density. The microstructural data forms the input for a physically-based modelling approach, both of which are presented in “Part 2: Microstructural Evolution during Cyclic Loading and its Representation in a Physically-based Micromechanical Model“.
The dataset contains experimental mechanical data from complex service-like creep-fatigue experiments performed isothermally at 620 °C and a low strain amplitude of 0.2 % on tempered martensite-ferritic grade P92 steel. The data sets in text file format provide cyclic deformation (min. and max. stresses) and the total (hysteresis) data of all recorded fatigue cycles for three different creep-fatigue experiments: 1) a standard relaxation fatigue (RF) test with symmetrical dwell times of three minutes introduced at minimum and maximum strain, 2) a fully strain-controlled service-like relaxation (SLR) test combining these three-minute peak strain dwells with a 30-minute dwell in between at zero strain, and 3) a partly stress-controlled service-like creep (SLC) test combining the three-minute peak strain dwells with 30-minute dwells at constant stress.
Further information on data and data acquisition, analysis, and experimental details are given in “Experimental Data from Service-Like Creep-Fatigue Experiments on Grade P92 Steel”, submitted to Data in Brief. Additional analyses of these datasets, as well as experimental findings and discussions are presented in “Creep-Fatigue of P92 in Service-Like Tests with Combined Stress- and Strain-Controlled Dwell Times”, submitted to International Journal of Fatigue.
Die Messung spontaner magnetischer Streufelder ferromagnetischer Materialien wird als neue, Metal Magnetic Memory (MMM) genannte, Methode der zerstörungsfreien Prüfung (ZfP) angesehen, Schädigungen frühzeitig vorherzusagen. Die MMM Methode versucht, die sich gleichzeitig mit der Schadensentwicklung ausbildende lokale magnetische Struktur für die ZfP zu nutzen und zwar schon vor der eigentlichen Rissinitiierung. Das zugehörige Regelwerk ISO 24497 verspricht neben der Detektion von Mikrorissen und Inhomogenitäten des Werkstoffgefüges auch die Bestimmung des (Eigen-) Spannungszustandes. Neue, an der Bundesanstalt für Materialforschung und -prüfung für die ZfP angepasste GMR (Giant Magneto Resistance)-Sensorik erlaubt Magnetfeldmessungen mit einer Ortsauflösung im Mikrometerbereich. Mit höherer Ortsauflösung zeigen sich Unterschiede, jedoch keine Widersprüche zu bisher publizierten Daten. Ihnen wesentlich ist, dass es einige verwertbare Hinweise auf einen Zusammenhang von Restfeldmagnetisierung und Materialeigenschaften gibt.
Evaluation of high spatial resolution imaging of magnetic stray fields for early damage detection
(2017)
The paper discusses the evaluation of elastic and plastic strain states in two low-carbon steels of the same steel group with high spatial resolution GMR (giant magneto resistance) sensors. The residual stress distributions of tungsten inert gas welded plates were determined by means of neutron diffraction as a reference. The normal component of local residual magnetic stray fields arise in the vicinity of the positions of maximum stress. The experiments performed on flat tensile specimen indicate that the boundaries of plastic deformations are a source of stray fields. The spatial variations of magnetic stray fields for both the weld and the tensile samples are in the order of the earths magnetic field.
This article refers to the research article entitled “Creep-Fatigue of P92 in Service-Like Tests with Combined Stress- and Strain-Controlled Dwell Times” [1]. It presents experimental mechanical data from complex service-like creep-fatigue experiments performed isothermally at 620 °C and a low strain amplitude of 0.2 % on tempered martensite-ferritic grade P92 steel. The data sets in text file format provide cyclic deformation (min. and max. stresses) and the total (hysteresis) data of all recorded fatigue cycles for three different creep-fatigue experiments: 1) a standard relaxation fatigue (RF) test with symmetrical dwell times of three minutes introduced at minimum and maximum strain, 2) a fully strain-controlled service-like relaxation (SLR) test combining these three-minute peak strain dwells with a 30-minute dwell in between at zero strain, and 3) a partly stress-controlled service-like creep (SLC) test combining the three-minute peak strain dwells with 30-minute dwells at constant stress. Such service-like (SL) tests with additional long-term stress- and strain-controlled dwell times are non-standard, rare, and expensive, making these data very valuable. They may be used to approximate cyclic softening in the technically relevant range, for the design of complex SL experiments, or for detailed analyses of stress-strain hystereses (e.g., for stress or strain partitioning methods, for the determination of hysteresis energies (work), inelastic strain components, etc.). In addition, the latter analyses may supply important input for advanced parametric lifetime modeling of components under creep-fatigue loading or model calibration parameters.
It is widely known that the magnetic domain structure of stress-sensitive ferromagnetic materials may be altered by external or internal mechanical stresses due to magnetoelastic effects. In this contribution, localized magnetic domain changes arising from inhomogeneous deformation and multiaxial loading conditions are imaged by the Bitter method for the first time. It is demonstrated that these domain changes provide deformation-related information and thus, allow for the visualization of macroscopic strain gradients in fine-grained polycrystalline steels, while keeping a sufficient spatial resolution.
This approach has been developed within the framework of BAM-MI-project “MICRONET”.
Measurement of spontaneous magnetic stray field signals has been reported to be a promising tool for capturing macro-scale information of deformation states, defects and stress concentration zones in a material structure. This paper offers a new method for self-magnetic leakage field detection using a magneto-optical (MO) hand-held microscope. Its sensor has a dynamic field range between ±0.05 and ±2 kA/m and a lateral optical resolution of approx. 10 µm. We examined flat tensile test specimens of metastable austenitic steel AISI 304. Static tensile tests were repeatedly interrupted at various predetermined states of strain and the magnetic information was measured by the MO system. Comparative measurements using a high-precision magnetic field GMR-sensor, verify the outstanding capability of the MO microscope regarding spatial resolution of magnetic fields.