Concrete is by far the most common building material in the world. Due to its good durability it is widely used in building envelopes. One major part of the embodied energy in concrete comes from the production of Portland cement that consumes around 3,500 MJ energy per each ton of cement. Globally 2.6 billion tons of Portland cement is produced and the consumption is increasing. Since concrete will be used as main building material also in future construction, it is reasonable to develop concrete building components with lower embodied energy.Using the example of an ultra-high performance concrete (UHPC) façade element, it is demonstrated how the embodied energy can be reduced by application of hydrothermal curing.
The adaption of the set-up for gas permeability measurements for ultra-high performance concrete
(2022)
In the framework of this project, a steam pressure vessel was to be developed from ultra-high perfor-mance concrete (UHPC) to withstand process temperatures of 200 °C and the respective steam pressure of 15,5 bar. To guarantee the long-term water vapour tightness of the system, the permeability of two UHPC mixtures were tested after long-term cyclic autoclaving. As UPHC shows a high density and therefore low permeability, measurements after the RILEM-Recommendation (TC 116-PCD) reached their detection limit. Therefore, the measurement set-up was adapted to measure the permeability of highly dense UHPC more reliably and quickly. This adaption includes measurements in a higher pres-sure range, the change of sample size thickness and the usage of Ar as a medium compared with the RILEM Recommendation. Additionally, the system was equipped with two pressure sensors and Ar-flowmeters to guarantee a continuous record of the experimental parameters. The new system was tested and evaluated by comparing measurements with the RILEM recommended system. Preliminary results show that the adapted system is capable to provide efficient and reliable results of concrete with low permeability.
Several studies show that thermal and hydrothermal treatment can further improve the excellent properties of UHPC in terms of mechanical strength and durability. While for the thermal treatment the increase in strength is attributed to an intensified pozzolanic and hydraulic reaction, for the hydrothermal treatment previous studies accredited it mostly to the formation of tobermorite. In the presented study thermal and hydrothermal treatment of UHPC samples was systematically varied and the phase formation analysed related to the strength development of a reference sample cured for 28 days in water. For the thermal treatment the results show that the strength increase depends on the protection against desiccation and can be ascribed to an improved pozzolanic reaction of the siliceous fillers. To achieve a significant enhancement of strength, a pre-storage time of few days and a long dwell time at elevated temperature/pressure are required. For the hydrothermal treatment already heating the specimens up to 185 °C in saturated steam followed by an immediate cooling leads to a substantial increase in compressive strength. Pre-storage time did not affect the result as far as a minimum of several hours is guaranteed. The improved performance is due to an increase in the pozzolanic and hydraulic reaction. Surprisingly, tobermorite was only found within a very thin layer at the surface of the sample, but not in the bulk. Sulphate and aluminium stemming from the decomposition of the ettringite are bound in the newly formed phases hydroxylellestadite and hydrogarnet.