Filtern
Dokumenttyp
- Beitrag zu einem Tagungsband (8)
- Zeitschriftenartikel (5)
- Vortrag (1)
- Posterpräsentation (1)
Schlagworte
- UHPC (4)
- Hydrothermal treatment (3)
- Alkali-silica reaction (2)
- Building Materials (2)
- Concrete (2)
- Damage analysis (2)
- Hydroxylellestadite (2)
- Microstructure (2)
- Tobermorite (2)
- X-ray diffraction (XRD) (2)
- Accelerated testing (1)
- Alite (1)
- Alkali silica reaction (1)
- BOFS (1)
- Brown coal fly ash (1)
- Building and Construction (1)
- Compressive strength (1)
- Concrete motorway pavements (1)
- Durability (1)
- Ettringit (1)
- Ettringite (1)
- Fast measurement (1)
- General Materials Science (1)
- Heat treatment (1)
- Hydration products (1)
- Hydrogarnet (1)
- Hydrogranat (1)
- Hydrothermale Behandlung (1)
- Hydroxyellestadit (1)
- In-situ XRD (1)
- Internal sulfate resistance (1)
- Kristalline CSH-Phase (1)
- LD-Schlacke (1)
- Materials characterisation (1)
- Mechanical strength (1)
- Mitigation strategies (1)
- Non-destructive testing (1)
- Performance test (1)
- Phase composition (1)
- Phase development (1)
- Portland Cement (1)
- Preparation of thin sections (1)
- Raman microscopy (1)
- Road pavement (1)
- Sample holder (1)
- Spatial analyses (1)
- Steelmaking slag (1)
- Test methods (1)
- Thermal analysis (1)
- Thermal treatment (1)
- Tobermorit (1)
- Tricalcium-silicate (1)
- Tricalciumsilikat (1)
- Ultra-High Performance Concrete (UHPC) (1)
- Ultra-high performance concrete (1)
- Ultrahigh-performance concrete (UHPC) (1)
- Wärmebehandlung (1)
- X-ray diffraction (1)
- X-ray diffractometry (1)
- XRD (1)
- Zement (1)
- Zonation (1)
- autoclaving (1)
- heat treatment (1)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (1)
A further improvement of the excellent properties of UHPC can be realized with thermal Treatment. Like for normal concrete, it accelerates the hardening and prevents shrinkage after the treatment. Additionally, an increase in strength can be achieved. Aim of this study was the optimisation of the thermal Treatment conditions of UHPC for very different Treatment methods; heat Treatment at 90 °C for unprotected and sealed samples, hot water bath at 90 °C and hydrothermal Treatment at 185 °C/1.1 MPa. The pre-storage time and the dwell time were systematically varied for each method to gain a higher strength. The compressive strength depends on the manner of Treatment at which higher water accessibility leads to higher strengths. The Phase composition changes considerably with different Treatment tempereatures. Finally, it can activate unhydrated binder components forming additional C-S-H, leading to higher strength.
Die Klinkerphasenbildung durch Sinterung in Drehrohröfen bei der Herstellung von Portlandzementklinker (PZK) ist gründlich erforscht und optimiert. Im Hinblick auf mögliche ökonomische und ökologische Vorteile befassen sich aktuelle Forschungsvorhaben darüber hinaus mit der Herstellung von Klinkermineralen aus Stahlwerksschlacken, die eine vergleichbare chemische Zusammensetzung aufweisen.
Neuste Untersuchungen zeigen, dass nach der reduzierenden Behandlung schmelzflüssiger Linz-Donawitz-(LD)-Schlacken und Abscheidung des gebildeten metallischen Eisens eine mineralische Schlacke entsteht, die unabhängig von ihren Abkühlbedingungen ca. 50–60 Gew.% des wichtigsten Klinkerminerals Alit (C3S) enthält und eine hohe hydraulische Reaktivität aufweist.
Die Stabilität des Alits auch nach langsamer Abkühlung deutet auf eine Stabilisierung des Minerals durch Nebenelemente aus den LD-Schlacken hin. Ein sinkender Anteil an LD-Schlacke durch Zusatz synthetischer Schlackemischung, die sich hinsichtlich ihrer Hauptkomponenten wie eine ausreduzierte LD-Schlacke zusammensetzt, führt zu einem Rückgang des Alitgehaltes und dem Zerfall der Schlacke beim Erstarren.
By the combination of an optimized granulometry, a reduced water cement ratio and the use of superplasticizers ultra-high performance concrete achieves a compressive strength of over 150 N/mm2 and a high resistance regarding acids and water-soluble salts. In different Research projects the effect of an autoclavation on the mechanical strength and the phase composition was analyzed. In systematic studies, the concrete mix and the process parameters were varied.
The results show that autoclavation leads to an improved pozzolanic and hydraulic reaction and significantly improves the mechanical strength compared to a conventional thermal treatment. If a minimum time-span for hydration is ensured, the achievable strength level is not dependent on the prestorage time. However, the duration of the autoclaving is significant. After the Maximum strength is reached there is only a very slight decrease, even if unrealistically long autoclaving times are applied.
UHPC (engl. ultra-high-performance concrete) bietet außergewöhnliche Eigenschaften, die sich durch eine optimierte Wärmebehandlung weiter verbessern lassen. Wie bei normalen Beton beschleunigt eine Wärmebehandlung den Aushärteprozess und reduziert das Schrumpfen. Durch Ausbildung eines dichteren Gefüges wird weiterhin die Druckfestigkeit und die Resistenz gegenüber Umwelteinflüssen erhöht.
Die Art der Wärmebehandlung wird durch die Parameter: Temperatur, Druck, Wasserdampfsättigung und Dauer definiert und hat einen entscheiden Einfluss auf die Phasenentwicklung und damit auf die makro- und mikroskopischen Eigenschaften des UHPCs. Auch die Dauer und Art der Vorlagerung des UHPCs vor der thermischen Behandlung sind von Bedeutung.
Ziel der vorgestellten Untersuchung war der Vergleich und die Optimierung verschiedener Wärmebehandlungsarten mit Blick auf die Druckfestigkeits- und Phasenentwicklung. Dafür wurden UHPC-Zylinder und Prismen hergestellt und ungeschützt bzw. in Folie eingeschweißt bei 90 °C im Ofen, im Heißwasserbad, sowie alternativ bei 185 °C und 1.1 MPa im Autoklaven wärmebehandelt. Zusätzlich wurde die Vorlagerungs- und die Behandlungszeit systematisch variiert.
Die Ergebnisse zeigen, dass eine praxisnahe Wärmebehandlung im Ofen (kurze Vorlagerungs- und Behandlungszeit, Verdunstungsschutz durch Einschweißen in Folie) zwar zu einer stark erhöhten Frühfestigkeit führt, aber die Langzeitfestigkeit wird nicht signifikant erhöht. Erst längere Behandlungszeiten verbunden mit intensiviertem Schutz gegen das Austrocknen führen darüber hinaus zu deutlich erhöhten Langzeitfestigkeiten. Nach der Autoklavierung dagegen wurden Festigkeitszuwächse von bis zu 30 % gemessen.
Die röntgenographisch nachgewiesene Phasenentwicklung wird in beiden Behandlungsarten durch die Limitierung des zur Verfügung stehenden Wassers bestimmt. Bei der Wärmebehandlung im Ofen wird das durch den Ettringitzerfall freigesetzte Wasser für die puzzolanische Reaktion der Mikrosilika verbraucht, reicht aber für eine weitere Reaktion der Klinkerphasen nicht aus. Bei der hydrothermalen Behandlung dagegen zeigen die Veränderungen im Phasenbestand sowohl eine Intensivierung der puzzolanischen als auch der hydraulischen Reaktion. Der für autoklavierte Baustoffe charakteristische Tobermorit konnte jedoch nicht im Probeninneren, sondern nur als Belag auf der Probenoberfläche nachgewiesen werden. Ursächlich hierfür ist vermutlich wiederum das zu geringe Wasserangebot im Gefüge des UHPC.
Fused cement clinker can be produced from molten basic oxygen furnace slag (BOFS) by way of a reductive thermochemical treatment. During the thermochemical treatment, oxidic iron is reduced to metallic iron and separated. The resulting low-iron slag has a chemical and mineralogical composition similar to ordinary Portland cement (OPC) clinker. In this study, the hydraulic reactivity of the fused clinker from BOFS with and without gypsum was investigated using isothermal calorimetry, differential scanning calorimetry, in situ X-ray diffraction and powder X-ray diffraction. Furthermore, a synthetic fused clinker without foreign ions and fused clinker produced by a mixture of both materials was studied. The hydraulic reaction of the fused clinker from BOFS was considerably slower than that of OPC. However, the reaction can be accelerated by adding gypsum as a sulfate carrier. Furthermore, the results showed an increased reaction rate with decreasing content of foreign ions such as Fe, P or Mn.