The accelerated concrete prism test (ACPT-60 °C) facilitates testing of alkali-silica reactivity of aggregates within five months. Manual measurement is usually conducted to determine expansion of test specimen every 28 days. This conventional procedure gives only limited insight to expansion behaviour of ASR-affected prisms. Due to the large time intervals, expansion exceeding the critical value of 0.3 mm/m is likely to be noticed late. Continuous recording resolves this problem and delivers beneficial information on the shape of the expansion curve.
Displacement transducers integrated into a special testing equipment developed at BAM put continuous measurement into practice. Additionally, ultrasonic velocity and acoustic emissions are measured in-situ and provide deeper insights into hydration and crack formation processes during the test.
Aiming for an automated testing method close to the German guideline, the following technical and methodical challenges arise. Changing of the vertical orientation of the prisms with every manual measurement as standardised cannot be implemented. Furthermore, preliminary results already proved true that cooling and heating cycles, as necessarily associated with each manual measurement, can evoke additional expansion. Therefore, interrupted and continuously measured expansions reveal systematic differences, indicating the necessity to adjust the threshold expansion value for automated testing.
Results presented in the paper: Different types of reactive aggregate have been tested applying continuous and manual expansion measurement to the concrete specimens. Development of continuously measured ultrasonic velocity and acoustic emissions of the aggregates tested diverge significantly while the expansion curves vary in shape and maximum strain. Prisms produced from a slowly reacting aggregate do not exhibit noticeable crack formation. It shows that comprehensive measuring helps describing and distinguishing ASR-damage mechanisms.
Models of ASR-induced expansion, available in the open literature, so far are validated with discontinuous data hardly tracing the modelled curve. Continuous measurement improves validation and further model development.
The primary aim of this paper is to analyze the impact of mechanical pre-damage and alkali–silica reaction (ASR) on the fracture mechanical properties of pavement concrete. For this purpose, a four point bending test was applied to large format beams to produce a defined level of cyclic pre-damage. The fatigue-induced concrete degradation process was simultaneously recorded using a testing procedure specifically developed for the purpose. In addition, fatigue-induced cracks on extracted drilling cores were spatially visualized and quantified using micro X-ray 3D-computed tomography (3D-CT). The storage of the small-format test specimens, with and without cyclic pre-damage, in an ASR-conducive environment showed that pre-damage leads to an increase in ASR damage processes. Subsequent structural mechanical investigations on small format specimens with and without pre-damage show that fatigue loading and ASR significantly influence fracture mechanical parameters of the concrete.