Filtern
Erscheinungsjahr
- 2017 (7) (entfernen)
Dokumenttyp
- Zeitschriftenartikel (3)
- Beitrag zu einem Tagungsband (3)
- Vortrag (1)
Sprache
- Englisch (7) (entfernen)
Schlagworte
- Alkali-silica reaction (3)
- Building Materials (2)
- Ultra-High Performance Concrete (UHPC) (2)
- X-ray diffraction (XRD) (2)
- Accelerated concrete prism test (1)
- Acoustic emissions analysis (1)
- Autoclaving (1)
- Climate simulation concrete prism test (1)
- Concrete (1)
- Concrete pavement (1)
- Continuous monitoring (1)
- Expansion modelling (1)
- External alkalis (1)
- Fatigue loading (1)
- Fire (1)
- Fracture energy (1)
- HPC (1)
- HSC (1)
- Heat treatment (1)
- Laser-induced breakdown spectroscopy (1)
- Microcracks (1)
- Moisture clog (1)
- Moisture transport (1)
- Monitoring of damage (1)
- NDT (1)
- NMR (1)
- Pavement concrete (1)
- Polysaccharides (1)
- Rheology (1)
- Spalling (1)
- Sphingan (1)
- Stabilising agents (1)
- Starch (1)
- Tensile strength (1)
- Ultrasonic velocity (1)
- X-ray CT (1)
- autoclaving (1)
- heat treatment (1)
Eingeladener Vortrag
- nein (1)
Unilateral thermal exposure of concrete building components induces moisture transport processes that have a significant influence on the spalling behaviour of dense high-strength concrete (HSC). These transport processes are based on evaporation and condensation mechanisms of liquid and gaseous water in the pores as well as the chemically bound water within the concrete. The low permeability of HSC and the formation of a saturated zone within building components (also known as a moisture clog) leads to high water-vapour pressures, which contributes to explosive spalling. The formation of these pressures has already been verified by means of pore-pressure measurement techniques. In addition, the redistribution of the moisture within concrete specimens subject to unilateral thermal exposure has been demonstrated on fractured surfaces. Investigations by means of the nuclear magnetic resonance (NMR) relaxometry technique and neutron radiography have shown one-dimensional changes in moisture distribution during thermal exposure.
However, none of these methods has been able to depict the moisture distribution in three dimensions (3D), so the link between pore size, concrete micro-structure and moisture content is missing. The research project presented in this paper aims to fill this gap by developing a new multi-level test methodology to characterise non-destructively the temporal course of spatial moisture distribution during unilateral thermal exposure. The procedure used during this programme included the collection of X-ray 3D-computed tomography (CT) measurements using a miniaturised specimen subjected to in-situ thermal exposure and the comparison of those CT results with the results of one-dimensional NMR-relaxometry before and after the heating process.
In the first step, a mobile heating device was developed, built and tested. To simulate a unilaterally-heated construction component, a cylindrical specimen made of HSC (Ø = 40 mm, L = 100 mm) was cast into an impermeable glass ceramic shell. The ceramic shell ensured a one-dimensional moisture flux and limited the thermal expansion of the concrete. An additional high-temperature wool (HTW) insulating shell ensured a one-dimensional heat flux. The heating device, which operated using infrared radiation (IR), allowed the unilateral heating of the specimens up to 300 °C using variable heating regimes.
In the second step, the mobile heating device was integrated into the CT-scanner, which enabled the collection of measurements before, during and after heating. By subtraction of successive 3D-CT images, X-ray attenuation differences could be resolved three-dimensionally in the specimen and interpreted as changes in the moisture content.
Initial results show that this test methodology can monitor the 3D changes of moisture content inside the specimen during thermal exposure. It enables the researcher to visualise areas with moisture accumulation as well as dehydrated areas inside the specimen. Comparative one-dimensional NMR-relaxometry measurements confirm the results of the CT image analysis.
The accelerated concrete prism test (ACPT-60 °C) facilitates testing of alkali-silica reactivity of aggregates within five months. Manual measurement is usually conducted to determine expansion of test specimen every 28 days. This conventional procedure gives only limited insight to expansion behaviour of ASR-affected prisms. Due to the large time intervals, expansion exceeding the critical value of 0.3 mm/m is likely to be noticed late. Continuous recording resolves this problem and delivers beneficial information on the shape of the expansion curve.
Displacement transducers integrated into a special testing equipment developed at BAM put continuous measurement into practice. Additionally, ultrasonic velocity and acoustic emissions are measured in-situ and provide deeper insights into hydration and crack formation processes during the test.
Aiming for an automated testing method close to the German guideline, the following technical and methodical challenges arise. Changing of the vertical orientation of the prisms with every manual measurement as standardised cannot be implemented. Furthermore, preliminary results already proved true that cooling and heating cycles, as necessarily associated with each manual measurement, can evoke additional expansion. Therefore, interrupted and continuously measured expansions reveal systematic differences, indicating the necessity to adjust the threshold expansion value for automated testing.
Results presented in the paper: Different types of reactive aggregate have been tested applying continuous and manual expansion measurement to the concrete specimens. Development of continuously measured ultrasonic velocity and acoustic emissions of the aggregates tested diverge significantly while the expansion curves vary in shape and maximum strain. Prisms produced from a slowly reacting aggregate do not exhibit noticeable crack formation. It shows that comprehensive measuring helps describing and distinguishing ASR-damage mechanisms.
Models of ASR-induced expansion, available in the open literature, so far are validated with discontinuous data hardly tracing the modelled curve. Continuous measurement improves validation and further model development.
A further improvement of the excellent properties of UHPC can be realized with thermal Treatment. Like for normal concrete, it accelerates the hardening and prevents shrinkage after the treatment. Additionally, an increase in strength can be achieved. Aim of this study was the optimisation of the thermal Treatment conditions of UHPC for very different Treatment methods; heat Treatment at 90 °C for unprotected and sealed samples, hot water bath at 90 °C and hydrothermal Treatment at 185 °C/1.1 MPa. The pre-storage time and the dwell time were systematically varied for each method to gain a higher strength. The compressive strength depends on the manner of Treatment at which higher water accessibility leads to higher strengths. The Phase composition changes considerably with different Treatment tempereatures. Finally, it can activate unhydrated binder components forming additional C-S-H, leading to higher strength.
In concrete elements, simultaneously subjected to cyclic loadings and external alkalis, the risk for damage caused by or under participation of an alkali-silica reaction (ASR) is particularly high. This is of particular concern for concrete pavements due to the increasing heavy vehicle traffic and the application of sodium chloride (NaCl) de-icer during winter. Since 2004, the climate simulation concrete prism test (CS-CPT) has been used successfully to evaluate job mixtures for pavements by considering the impact of alkali-containing de-icers. However, the role of mechanical predamage on ASR is largely unclear. In a joint research project, the CS-CPT has been used to investigate the influence of preexisting microcracks on ASR. It was evident that an ASR initiated earlier in the predamaged concrete prisms due to the more rapid ingress of NaCl solution through the microcracks.
A further improvement of the excellent properties of UHPC can be realized with thermal Treatment. Like for normal concrete, it accelerates the hardening and prevents shrinkage after the treatment. Additionally, an increase in strength can be achieved. Aim of this study was the optimisation of the thermal Treatment conditions of UHPC for very different Treatment methods; heat Treatment at 90 °C for unprotected and sealed samples, hot water bath at 90 °C and hydrothermal Treatment at 185 °C/1.1 MPa. The pre-storage time and the dwell time were systematically varied for each method to gain a higher strength. The compressive strength depends on the manner of Treatment at which higher water accessibility leads to higher strengths. The Phase composition changes considerably with different Treatment tempereatures. Finally, it can activate unhydrated binder components forming additional C-S-H, leading to higher strength.
The primary aim of this paper is to analyze the impact of mechanical pre-damage and alkali–silica reaction (ASR) on the fracture mechanical properties of pavement concrete. For this purpose, a four point bending test was applied to large format beams to produce a defined level of cyclic pre-damage. The fatigue-induced concrete degradation process was simultaneously recorded using a testing procedure specifically developed for the purpose. In addition, fatigue-induced cracks on extracted drilling cores were spatially visualized and quantified using micro X-ray 3D-computed tomography (3D-CT). The storage of the small-format test specimens, with and without cyclic pre-damage, in an ASR-conducive environment showed that pre-damage leads to an increase in ASR damage processes. Subsequent structural mechanical investigations on small format specimens with and without pre-damage show that fatigue loading and ASR significantly influence fracture mechanical parameters of the concrete.
Polysaccharides are incorporated into cement based Systems in order to modify the rheological properties. Typically, cellulose ethers, sphingan gums, guar gum or starch ethers are applied. Depending upon their chemistry, molecular architecture, and adsorption tendency, polysaccharides interact differently with the entire cementitious system. Some stabilising agents like diutan gum mainly affect the cementitious paste; other stabilising agents like starch tend to interact with the sand fraction and even with the coarse aggregates. Cellulose and guar gum shows more diverse performances.
Typically stabilising admixtures like polysaccharides are used, when sophisticated rheological properties are adjusted. Therefore, polysaccharides are often used in combination with superplasticisers, which are added to reduce the yield stress of concrete. This can cause interactions, particularly when the stabilising Agent shows a strong tendency to adsorb on particle surfaces. Adsorptive stabilising agents may reduce the amount of adsorbed superplasticisers, thus affecting both viscosity and yield stress, while non-adsorptive stabilising agents mainly affect the plastic viscosity independently of the superplasticiser. Due to the strong influence of superplasticisers on the yield stress, influences of the stabilising agent on the yield stress retreat into the background, so that their major effect is an increase of the plastic viscosity.
The paper provides a comprehensive overview of how different polysaccharide superplasticisers affect cementitious flowable systems and points out the challenges of the combined use of polysaccharides and superplasticisers. Based on rheometric experiments and observations of the hydration process, time dependent effects on the workability as well as of the hydration of cement are presented and discussed.