Filtern
Dokumenttyp
Schlagworte
- Automated expansion measurement (2)
- 60 °C-Betonversuch (1)
- 60 °C-CPT (1)
- AKR (1)
- ASR (1)
- ASR expansion monitoring (1)
- ASR modelling (1)
- Accelerated concrete prism test (1)
- Accelerated testing (1)
- Alkali silica reaction (1)
- Alkali–silica reaction (1)
- Auslaugung (1)
- Automated testing (1)
- Automatische Dehnungsmessung (1)
- Baustoffe (1)
- Beton (1)
- Building Materials (1)
- Compressive Cyclic loading (1)
- Concrete (1)
- Concrete Prism Test at 60 °C (1)
- Damage analysis (1)
- Datenmanagement (1)
- Digitalisierung (1)
- FAIR-Prinzip (1)
- Fatigue (1)
- High-strength concrete (1)
- Leaching of alkalis (1)
- Materialdaten (1)
- Metadaten (1)
- Microstructure (1)
- Mitigation strategies (1)
- Non destructive testing (1)
- Non-destructive testing (1)
- Ontologie (1)
- Road pavement (1)
- Ultrasonic testing (1)
- Wissengraph (1)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (6) (entfernen)
Alkali-silica reaction (ASR) is a chemical reaction within concrete which can lead over time to cracking and spalling. Due to the complexity of the problem, it still causes damage to concrete constructions worldwide.
The publication aims to illustrate the interdisciplinary research of the German Federal Institute for Materials Research and Testing (BAM) within the last 20 years, considering all aspects of ASR topics from the macro to the micro level. First, methods for characterization and assessment of ASR risks and reaction products used at BAM are explained and classified in the international context. Subsequently the added value of the research approach by combining different, preferably nondestructive, methods across all scales is explained using specific examples from a variety of research projects. Aspects covered range from the development of new test-setups to assess aggregate reactivity, to analysis of microstructure and reaction products using microscopical, spectroscopical and X-ray methods, to the development of a testing methodology for existing concrete pavements including in-depth analysis of the visual damage indicator and the de-icing salt input using innovative testing techniques. Finally, research regarding a novel avoidance strategy that makes use of internal hydrophobization of the concrete mix is presented.
Der 60 °C-Betonversuch ist eine in Deutschland und international verbreitete Methode um die Empfindlichkeit von Gesteinskörnungen und Betonen hinsichtlich einer Alkali-Kieselsäure Reaktion (AKR) zu prüfen. Dieser Beitrag stellt eine neuentwickelte automatisierte Variante der Prüfmethode in einem Minireaktor vor. Dabei werden die Dehnungen von Betonprismen nicht, wie beim konventionellen Test manuell, sondern automatisch in entsprechend ausgerüsteten Prüfbehältern gemessen. Neben einer Reduzierung des Messaufwands bringt die automatisierte Prüfung im Minireaktor weitere Vorteile. Die Dehnungssignale werden, anders als bei der konventionellen Messung, quasi-kontinuierlich aufgezeichnet und bilden das Expansionsverhalten der Prismen detailliert ab. Außerdem bleiben Unterbrechungen der AKR-provozierenden Lagerung aus, die bei der konventionellen Prüfung notwendig sind. Im Beitrag werden die automatisierte und konventionelle Prüfung anhand der Dehnungen von Prismen zweier Gesteinskörnungen verglichen. In Übereinstimmung mit vorhergehenden Untersuchungen sind im Minireaktor gemessene Dehnungen systematisch kleiner als manuell gemessene. Als mögliche Ursache werden Unterschiede im Auslaugverhalten experimentell untersucht. Zur Überprüfung der Einstufung der zwei Gesteinskörnungen erfolgen außerdem Referenzprüfungen in der Nebelkammerlagerung bei 40 °C.
Severe mechanical fatigue conditions for worldwide proliferating windfarms are a Major challenge for high-performance concrete in towers, connecting joints and foundations of wind turbines. High-performance concrete offers potential for the application in offshore windfarms, not only regarding its good mechanical, but also chemical resistivity due to low diffusivity in the highly densified microstructure. For a more reliable fatigue assessment, monitoring based on nondestructive testing can be a valuable complement to design rules. Both approaches demand reliable experimental data, information about scalability and the development of standardized testing methods. This article presents results of an ongoing research program of BAM (Bundesanstalt für Materialforschung und -prüfung), which is a part of a joint national project (WinConFat) funded by the German Federal Ministry for Economic Affairs and Energy. The subproject implemented by BAM examines the fatigue behavior in dependence of size and slenderness for varying concrete strength at different stress levels. Besides fatigue strength, nondestructive testing is carried out additionally.
Methods used are strain measurement and ultrasonic testing. The change of strain, stiffness and ultrasonic pulse velocity in the fatigue process is discussed. Results disclose a deeper insight into the damage process under cyclic loading of high-performance concrete and contribute to improve nondestructive monitoring.
The susceptibility of concrete structures due to alkali–silica reaction (ASR) can be assessed by means of ASR concrete prism testing at 60 °C, according to RILEM AAR 4.1. There, expansion of concrete prisms indicates alkali-reactivity of the examined concrete mix. This work applies in situ expansion measurement to accelerated concrete prism testing. Automated measuring facilitates both storage without the usually necessary interruptions for manual measurement and acquisition of quasi-continuousexpansion data. A comparative experimental programme showed that conventional testing resulted in stronger expansion and leaching of alkalis than automated testing. Experimental simulation of interruptions, typically associated with manual measurements in conventional testing, could prove the influence of these cooling–heating cycles. Two phenomenological approaches, frequently used for describing reaction kinetics of ASR by linking it to expansion results from ASR-testing, were validated with continuous expansion data of three types of aggregate. Experimental expansion depicted s-shaped curves similar to them of the modelling approaches. However, strong swelling recorded in the beginning of the test was not covered by the model curves. Auxiliary measurement of acoustic emissions and ultrasonic velocity helped characterising mechanisms such as hydration and cracking, which also influence prism expansion. The proposed modification of the measurement procedure provides an extended basis to analyse expansion mechanisms. Regarding data for validation of ASR-expansion models, continuous expansion results are preferable to conventional test results.
ln most of the ASR-test procedures, the expansion of concrete or mortar specimens is used as an indicator to assess the ASR-potential of an aggregate or a specific concrete mix. For these tests, the specimens are stored in an ASR-provoking environment, where the reaction is accelerated by elevated temperature and humidity. To measure the length change, the storage must be interrupted for at least a few minutes. Düring the 60 °C Concrete Prism Test (60 °C-CPT), the specimens are cooled down to 20 °C for 24 hours, to ensure the same hygrothermal conditions for every measurement. This limits the number of measurements during the test period and may lead to additional effects, that probably influence the expansion development.
With a recently developed device, it is possible to continuously monitor the expansion ofprisms without interrupting the ASR-provoking storage. Due to the dense database of this automated test, the results can contribute to a better understanding of the ASR-process. This study compares results of the automated and conventional 60 °C-CPT. Tests of different aggregates showed, that the results of the automated and conventional test are consistent, but the expansions during the conventional test are generally higher. Preliminary results led to the conclusion, that the cooling for the measurements leads to additional expansions. Therefore, a modified threshold should be discussed for the automated 60 °C-CPT.
Die sprunghaft zunehmende Wichtigkeit von FAIR- und Open-Data für die Qualitätssicherung, aber auch für die Nachnutzbarkeit von Daten und den Erkenntnisfortschritt führt zu enormem Flandlungsbedarf in Forschung und Entwicklung. Damit verbunden laufen derzeit vielfältige, ambitionierte Aktionen, z. B. bezüglich der Erstellung von Ontologien und Wissensgraphen. Das Knowhow entwickelt sich rasant, die Ansätze zur Implementation entstehen in verschiedenen Fachwelten bzw. mit
unterschiedlichen Zielsetzungen parallel, so dass recht heterogene Herangehensweisen resultieren.
Diese Veröffentlichung fokussiert auf Arbeiten, die derzeit als möglichst ganzheitlicher Ansatz für Materialdaten im Rahmen der Digitalisierungsinitiative „Plattform MaterialDigital" vorangetrieben werden. Die Autoren bearbeiten baustoffbezogene Aspekte im Verbundprojekt „LeBeDigital - Lebenszyklus von Beton". Zielsetzung ist die digitale Beschreibung des Materialverhaltens von Beton über den kompletten Herstellungsprozess eines Fertigteils mit einer Integration von Daten und Modellen innerhalb eines Workflows zur probabilistischen Material- und Prozessoptimierung.
Es wird über die Vorgehensweise und die dabei gewonnenen Erfahrungen berichtet, nicht ohne den Blick auf die oft unterschätzte Komplexität der Thematik zu lenken.