Filtern
Dokumenttyp
- Beitrag zu einem Tagungsband (23)
- Vortrag (2)
- Zeitschriftenartikel (1)
- Buchkapitel (1)
- Posterpräsentation (1)
Referierte Publikation
- nein (28) (entfernen)
Schlagworte
- UHPC (6)
- Durability (3)
- Hydrothermal treatment (3)
- Microstructure (3)
- Zement (3)
- Zonation (3)
- Architectural Concrete (2)
- Beton (2)
- Degradation (2)
- Digitalisierung (2)
- Einzelfaserdurchzugsversuch (2)
- Facade Elements (2)
- Fasermodifikation (2)
- Fatigue (2)
- Fibres (2)
- Grenzflächenaktive Verbindung (2)
- Lichtmikroskopie (2)
- Oberflächenfunktionalisierung (2)
- Röntgen-3D-Computertomographie (2)
- Self-Cleaning Properties (2)
- Shrinkage (2)
- Thermal treatment (2)
- Windkanal (2)
- Zementgebundene Baustoffe (2)
- 60 °C-CPT (1)
- AKR (1)
- ASR (1)
- ASR expansion monitoring (1)
- Adhesive Pull-Strength (1)
- Alite (1)
- Alkali-Kieselsäure-Reaktion (1)
- Alkali-Silica Reaction (1)
- Alkali-silica reaction (1)
- Anwendungsbeispiele (1)
- Autoclaved aerated concrete (1)
- Automated testing (1)
- Betonfahrbahndecke (1)
- Betonstahl (1)
- Betontechnik (1)
- Bindemittel (1)
- Brown coal fly ash (1)
- Cementitious materials (1)
- Composition (1)
- Compressive Cyclic loading (1)
- Computed tomography (1)
- Concrete (1)
- Concrete motorway pavements (1)
- Cyclic loading (1)
- Datenmanagement (1)
- Desiccation (1)
- Eigenschaften (1)
- Ettringit (1)
- Ettringite (1)
- FAIR-Prinzip (1)
- Flexural testing (1)
- Fluid transport (1)
- Flüssigkeitstransport (1)
- Functionalization (1)
- Heat treatment (1)
- Herstellungsprozesse (1)
- High-strength concrete (1)
- Hydrogranat (1)
- Hydrothermale Behandlung (1)
- Hydroxyellestadit (1)
- Hydroxylellestadite (1)
- In-situ XRD (1)
- Internal sulfate resistance (1)
- Kristalline CSH-Phase (1)
- LD-Schlacke (1)
- LIBS (1)
- MRFA (1)
- Materialdaten (1)
- Mechanical strength (1)
- Metadaten (1)
- Mineralogie (1)
- Modellierung (1)
- Mortar (1)
- Nasschemie (1)
- Non destructive testing (1)
- Ontologie (1)
- Ontologien (1)
- Pavement (1)
- Performance test (1)
- Phase composition (1)
- Phasenzusammensetzung (1)
- Photogrammetric analysis (1)
- Portland Cement (1)
- Production technology (1)
- Raman microscopy (1)
- Spannstahl (1)
- Steelmaking slag (1)
- Strain hardening (1)
- Tausalz (1)
- Test methods (1)
- Thermodynamik (1)
- Tobermorit (1)
- Tobermorite (1)
- Traffic (1)
- Transport mechanism (1)
- Tricalcium-silicate (1)
- Tricalciumsilikat (1)
- Ultra-High Performance Concrete (1)
- Ultra-High-Performance Concrete (1)
- Ultra-high performance concrete (1)
- Ultrahigh-performance concrete (1)
- Ultrasonic testing (1)
- Verkehr (1)
- Wissengraph (1)
- Wärmebehandlung (1)
- XRD (1)
- ZfP (1)
- Zyklischen Belastung (1)
- gas permeability (1)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (28) (entfernen)
Eingeladener Vortrag
- nein (2)
Alkali-Kieselsäure-Reaktion in Betonfahrbahndecken unter Berücksichtigung von Verkehr und Taumitteln
(2019)
In Betonfahrbahndecken treten häufig Schäden auf, welche mit einer Alkali-Kieselsäure-Reaktion (AKR) in Verbindung gebracht werden. Obwohl die Hintergründe einer solchen AKR intensiv untersucht wurden, gibt es bei Betonfahrbahndecken besondere Randbedingungen, welche die Schadreaktion signifikant erhöhen können. Diese sind vor allem die Überlagerung der mikrostrukturellen Degradation durch Verkehrsbeanspruchung mit externer Alkali-Zufuhr durch Taumittel. Bisherige Untersuchungen der AKR beschränkten sich auf die Ausgangsstoffe (Gesteinskörnung, Zement, Bewertung des Betons), wobei die besonderen Randbedingungen außer Acht gelassen wurden. Betonfahrbahndecken sind zyklischen Belastungen aus Verkehr und Witterungsbedingungen ausgesetzt.
In einem gemeinschaftlichen Forschungsprojekt wurden die verschiedenen, gegenseitig voneinander abhängigen, Einflussfaktoren auf eine schädigende AKR in Betonfahrbahndecken sowohl experimentell untersucht als auch numerisch modelliert. Auf Mikro-Ebene wurden die AKR-bezogenen Transportprozesse innerhalb der Gesteinskörnung, sowie die Gelbildung und der Ionen-Transport, untersucht. Auf Meso-Ebene fokussierte das Projekt auf die Charakterisierung der durch zyklische Belastung induzierten Schädigung im Mikrogefüge des Betons. Des Weiteren wurde das Transportverhalten in ein derart geschädigtes Betongefüge mit und ohne Berücksichtigung des zusätzlichen Einflusses überrollender Reifen beschrieben und dessen Auswirkung auf eine AKR analysiert. Schließlich wurde auf Makro-Ebene das Risiko eines AKR-bedingten Schadens bewertet. Einige ausgewählte Ergebnisse werden in diesem Beitrag dargestellt.
In concrete pavements, damages occurred which are related to an Alkali-Silica-Reaction (ASR). Although the background for such an ASR has been studied extensively, special conditions in pavements increase this reaction significantly. These are especially the superposition of microstructural degradation caused by cyclic loading with an external alkali supply. Previous investigations of ASR focused mainly on the material itself (aggregates, cements, assessment of the concrete) while these special circumstances have not been considered. Concrete pavements are subjected to cyclic loadings by traffic and climate changes.
Within cooperative research projects the different interdependent influencing factors for a damaging ASR in concrete pavements are studied by experiments as well as by numeric modelling. On the micro-level the ASR-related processes within the aggregate, such as gel-formation or ion-transport, are investigated. On the meso-level, the project focuses on the characterization of degradation effects in the concrete microstructure due to cyclic loading. Further, special attention is paid to the transport behavior of fluids in such pre-damaged concrete structures with and without the effect of overrunning tires as well as the impact on the ASR itself. Finally, on the macro-level the risk of an ASR-damage is assessed.
Severe mechanical fatigue conditions for worldwide proliferating windfarms are a Major challenge for high-performance concrete in towers, connecting joints and foundations of wind turbines. High-performance concrete offers potential for the application in offshore windfarms, not only regarding its good mechanical, but also chemical resistivity due to low diffusivity in the highly densified microstructure. For a more reliable fatigue assessment, monitoring based on nondestructive testing can be a valuable complement to design rules. Both approaches demand reliable experimental data, information about scalability and the development of standardized testing methods. This article presents results of an ongoing research program of BAM (Bundesanstalt für Materialforschung und -prüfung), which is a part of a joint national project (WinConFat) funded by the German Federal Ministry for Economic Affairs and Energy. The subproject implemented by BAM examines the fatigue behavior in dependence of size and slenderness for varying concrete strength at different stress levels. Besides fatigue strength, nondestructive testing is carried out additionally.
Methods used are strain measurement and ultrasonic testing. The change of strain, stiffness and ultrasonic pulse velocity in the fatigue process is discussed. Results disclose a deeper insight into the damage process under cyclic loading of high-performance concrete and contribute to improve nondestructive monitoring.
Baustoffe im Betonbau
(2019)
In dem Kap. „Baustoffe im Betonbau“ werden zunächst die Baustoffe vorgestellt, die für die Herstellung von Stahlbeton- und Spannbetonbauwerken erforderlich sind (im Wesentlichen Beton, Betonstahl und Spannstahl). Herstellungsbedingte, typische Eigenschaftsprofile der Baustoffe werden aufgezeigt und ein Bezug zu entsprechenden Anwendungsgebieten hergestellt.
Even after autoclaving for 2 weeks in the temperature range of 120 to 200 °C, CEM I paste with a water-to-cement ratio of 0.5 still contains some low-crystalline C-S-H. The conversion of low-crystalline C-S-H to crystalline is faster with increasing temperature. The observed low-crystalline and crystalline C-S-H phases (reinhardbraunsite, jaffeite) indicate that the sampleshave not reached equilibrium yet under these experimental conditions. However, there is a good agreement between experiment and thermodynamic modelling for the other solids indicating that the used datasets are suitable for this application.
ln most of the ASR-test procedures, the expansion of concrete or mortar specimens is used as an indicator to assess the ASR-potential of an aggregate or a specific concrete mix. For these tests, the specimens are stored in an ASR-provoking environment, where the reaction is accelerated by elevated temperature and humidity. To measure the length change, the storage must be interrupted for at least a few minutes. Düring the 60 °C Concrete Prism Test (60 °C-CPT), the specimens are cooled down to 20 °C for 24 hours, to ensure the same hygrothermal conditions for every measurement. This limits the number of measurements during the test period and may lead to additional effects, that probably influence the expansion development.
With a recently developed device, it is possible to continuously monitor the expansion ofprisms without interrupting the ASR-provoking storage. Due to the dense database of this automated test, the results can contribute to a better understanding of the ASR-process. This study compares results of the automated and conventional 60 °C-CPT. Tests of different aggregates showed, that the results of the automated and conventional test are consistent, but the expansions during the conventional test are generally higher. Preliminary results led to the conclusion, that the cooling for the measurements leads to additional expansions. Therefore, a modified threshold should be discussed for the automated 60 °C-CPT.
Fatigue induced degradation in pavement concrete and its effect on the alkali-silica reaction
(2018)
In recent years the German motorway network has seen an increase in the occurrence of damage to concrete road surfaces that can be attributed to the alkali-silica reaction (ASR). In view of the often drastically reduced service life of road surfaces due to ASR, research activity in this field has notably increased. Alongside preventative measures in concrete technology i.e. the usage of low-alkali cements, the main research focus up to now has been on the development of performance-oriented testing procedures for ASR prevention. The effects of mechanicallyinduced damage resulting from cyclic traffic and climatic loading have previously not been taken into consideration.
The assessment of the myriad degradation and transport processes necessary for an understanding of these effects requires close interaction between experiments and corresponding multi-scale models. This contribution is focused on the experiments utilizing innovative testing techniques. The research is founded on a series of fatigue tests performed on large-scale beams with simultaneous tracking of the degradation process using non-destructive evaluation methods. Subsequently, smaller test specimens were extracted from the predamaged beams for further experiments. These experiments included investigation of the influence of fatigue-induced cracks on moisture and alkali transport. Subsequent storage of the small-scale test specimens, with and without cyclic pre-damage, in an ASR-conducive environment then provided initial findings on the influence of fatigue-induced degradation on the ASR.
The results show that the degradation process can be well observed with the test Setup developed for the fatigue experiments. Further, a small but noticeable increase of mass Transport due to fatigue-induced degradation was measured, which correspondingly indicated an increased ASR damage potential.
Beton ist weltweit einer der wichtigsten Konstruktionswerkstoffe und zeichnet sich durch eine enorme Anpassungsfähigkeit an sich verändernde Anforderungen aus. Damit verbunden ist eine hohe und kontinuierlich zunehmende Komplexität hinsichtlich der Ausgangsstoffe, Rezepturen und des Herstellungsprozesses. Folglich setzt eine Ausschöpfung des technischen und umweltbezogenen Potenzials der Betonbauweise höchste Expertise bei den Einzelakteuren der Bauindustrie voraus.
Die sprunghaft zunehmende Wichtigkeit von FAIR- und Open-Data für die Qualitätssicherung, aber auch für die Nachnutzbarkeit von Daten und den Erkenntnisfortschritt führt zu enormem Flandlungsbedarf in Forschung und Entwicklung. Damit verbunden laufen derzeit vielfältige, ambitionierte Aktionen, z. B. bezüglich der Erstellung von Ontologien und Wissensgraphen. Das Knowhow entwickelt sich rasant, die Ansätze zur Implementation entstehen in verschiedenen Fachwelten bzw. mit
unterschiedlichen Zielsetzungen parallel, so dass recht heterogene Herangehensweisen resultieren.
Diese Veröffentlichung fokussiert auf Arbeiten, die derzeit als möglichst ganzheitlicher Ansatz für Materialdaten im Rahmen der Digitalisierungsinitiative „Plattform MaterialDigital" vorangetrieben werden. Die Autoren bearbeiten baustoffbezogene Aspekte im Verbundprojekt „LeBeDigital - Lebenszyklus von Beton". Zielsetzung ist die digitale Beschreibung des Materialverhaltens von Beton über den kompletten Herstellungsprozess eines Fertigteils mit einer Integration von Daten und Modellen innerhalb eines Workflows zur probabilistischen Material- und Prozessoptimierung.
Es wird über die Vorgehensweise und die dabei gewonnenen Erfahrungen berichtet, nicht ohne den Blick auf die oft unterschätzte Komplexität der Thematik zu lenken.
Alkali silica reaction (ASR) is a major concrete durability problem resulting in significant maintenance and reconstruction costs for concrete infrastructures all over the world. To determine whether an aggregate is potentially reactive, accelerated concrete tests are used. Aim of this study is the chemical and microstructural characterization of ASR-products formed under the performance conditions of motorway pavements and during subsequent tests on the remaining ASR susceptibility. Samples were taken from concrete motorway pavements. Some of the samples already showed first indications for beginning damages whereas others showed deteriorations only after applying a performance testing procedure for the estimation of future risk of ASR damage. In a first step ASR-products were identified by polarized light microscopy in thin sections. The reaction products where then analyzed by Raman Spectroscopy and finally the chemical composition of the ASR-products was identified by SEM with EDX.
The results indicate that most reaction products show an increasing Ca/Si-ratio with progressive crack length. If an ASR-product develops inside an aggregate and moves through the cement paste, it has a high (Na+K)/Si-ratio at the beginning which decreases with increasing distance from its place of origin. The Raman spectra of the ASR-products are characterized by two broad bands indicating specific Q-species of different amorphous gel networks. Within the scope of the analysis distinctions in the microstructure and the chemical composition of the ASR-gels were detected relating to various conditions of accelerated testing.