Filtern
Erscheinungsjahr
Dokumenttyp
Schlagworte
- Beton (5)
- Accelerated concrete prism test (2)
- Automated expansion measurement (2)
- 60 °C-Betonversuch (1)
- 60 °C-CPT (1)
- AKR (1)
- ASR (1)
- ASR expansion monitoring (1)
- ASR modelling (1)
- Accelerated testing (1)
- Alkali silica reaction (1)
- Alkali-Kieselsäure-Reaktion (1)
- Alkali-silica reaction (1)
- Alkali–silica reaction (1)
- Auslaugung (1)
- Autogenes Schwinden (1)
- Automated testing (1)
- Automatische Dehnungsmessung (1)
- Baustoffe (1)
- Bauwerkssicherheit (1)
- Brandverhalten (1)
- Building Materials (1)
- Compressive Cyclic loading (1)
- Concrete (1)
- Concrete Prism Test at 60 °C (1)
- Continuous monitoring (1)
- Damage analysis (1)
- Datenmanagement (1)
- Digitalisierung (1)
- Ermüdungsverhalten (1)
- Expansion modelling (1)
- FAIR-Prinzip (1)
- Fatigue (1)
- Frühe Rissbildung (1)
- High-strength concrete (1)
- Hochleistungsbetone (1)
- Hydratation (1)
- Hydraulic engineering structures (1)
- Innovative Prüftechnik (1)
- Leaching of alkalis (1)
- Materialdaten (1)
- Metadaten (1)
- Microstructure (1)
- Mitigation strategies (1)
- Naturstein (1)
- Non destructive testing (1)
- Non-destructive testing (1)
- Ontologie (1)
- Quasi non-destructive assessment (1)
- Radar (1)
- Rissbildung (1)
- Road pavement (1)
- Schadensanalyse (1)
- Schallemissionsanalyse (1)
- Schallemissionsprüfung (1)
- Schädigungsprozesse (1)
- Ultrasonic and ray (1)
- Ultrasonic testing (1)
- Verformung (1)
- Wissengraph (1)
- Zerstörungsarme und zerstörungsfreie Prüfverfahren (1)
- Zusatzstoffe (1)
- alkali-silica-reaction (1)
- concrete pavements (1)
- damage monitoring (1)
- fatigue (1)
Organisationseinheit der BAM
Vom Baustoff zum sicheren Bauwerk: Einsatz der Schallemissionsanalyse in der Bauabteilung der BAM
(2013)
Seit 2006 wird die Schallemissionsanalyse (SEA) in der Abteilung 7 Bauwerkssicherheit der BAM genutzt, um Gefügeveränderungen in Betonen zu untersuchen. Dabei haben sich bis heute im Wesentlichen folgende vier Forschungsbereiche herauskristallisiert:
Hydratation
Während der Hydratation von Beton ist eine ausgeprägte Schallemissionsaktivität zu beobachten, anhand derer der Hydratationsverlauf nachvollzogen werden kann. Zur Aufklärung der Quellmechanismen der Schallemissionen besteht noch weiterer Forschungsbedarf. Des Weiteren kann mit Hilfe der SEA die frühe Rissbildung in Betonen, hervorgerufen durch autogenes oder plastisches Schwinden, analysiert werden.
Alkali-Kieselsäure-Reaktion (AKR)
Bei der AKR handelt es sich um eine Reaktion alkaliempfindlicher Gesteinskörnungen mit den Alkalien des Betons bzw. mit extern, z.B. durch Tausalze, zugeführten Alkalien. Dabei werden um die oder in der Gesteinskörnung quellfähige Gele gebildet, die zu einer völligen Zerstörung des Gefüges führen können. Mit der SEA können die Rissbildung detektiert und somit die Schädigungsphasen im Verlauf der AKR identifiziert werden.
Brandverhalten
Unter Brandeinwirkung platzt die Oberfläche gefügedichter Hochleistungsbetone explosionsartig ab. Um dies zu verhindern und somit den Feuerwiderstand von Bau-teilen aus Hochleistungsbeton zu erhöhen, werden dem Beton Polypropylenfasern beigemischt. Das Schmelzen der Fasern bei einer Temperaturerhöhung trägt zu einer erhöhten Mikrorissbildung bei, die einen Spannungsabbau ermöglicht. Die SEA konnte erfolgreich eingesetzt werden, um diesen Wirkmechanismus der Fasern nachzuweisen und weiter aufzuklären.
Ermüdungsverhalten
Durch die hohen zyklischen Lasten, für die Türme und Fundamente von Windkraft-anlagen ausgelegt werden müssen, gewinnen gesicherte Kenntnisse über das Ermüdungsverhalten von Betonen an Bedeutung. Mit der SEA ist es bei hochzyklischen Belastungsversuchen an Betonen möglich, den Schädigungsgrad im Verlauf der Beanspruchung zu bestimmen. Die Schallemissionsaktivität eignet sich als Kriterium, um die Versuche bei vorab definierten Schädigungsgraden zu unterbrechen und so Proben für weitergehende Untersuchungen zu gewinnen. Diese Ergebnisse sollen perspektivisch für Überwachungssysteme für Betonbauwerke unter zyklischer Beanspruchung genutzt werden.
Alkali-silica reaction (ASR) is a chemical reaction within concrete which can lead over time to cracking and spalling. Due to the complexity of the problem, it still causes damage to concrete constructions worldwide.
The publication aims to illustrate the interdisciplinary research of the German Federal Institute for Materials Research and Testing (BAM) within the last 20 years, considering all aspects of ASR topics from the macro to the micro level. First, methods for characterization and assessment of ASR risks and reaction products used at BAM are explained and classified in the international context. Subsequently the added value of the research approach by combining different, preferably nondestructive, methods across all scales is explained using specific examples from a variety of research projects. Aspects covered range from the development of new test-setups to assess aggregate reactivity, to analysis of microstructure and reaction products using microscopical, spectroscopical and X-ray methods, to the development of a testing methodology for existing concrete pavements including in-depth analysis of the visual damage indicator and the de-icing salt input using innovative testing techniques. Finally, research regarding a novel avoidance strategy that makes use of internal hydrophobization of the concrete mix is presented.
ln most of the ASR-test procedures, the expansion of concrete or mortar specimens is used as an indicator to assess the ASR-potential of an aggregate or a specific concrete mix. For these tests, the specimens are stored in an ASR-provoking environment, where the reaction is accelerated by elevated temperature and humidity. To measure the length change, the storage must be interrupted for at least a few minutes. Düring the 60 °C Concrete Prism Test (60 °C-CPT), the specimens are cooled down to 20 °C for 24 hours, to ensure the same hygrothermal conditions for every measurement. This limits the number of measurements during the test period and may lead to additional effects, that probably influence the expansion development.
With a recently developed device, it is possible to continuously monitor the expansion ofprisms without interrupting the ASR-provoking storage. Due to the dense database of this automated test, the results can contribute to a better understanding of the ASR-process. This study compares results of the automated and conventional 60 °C-CPT. Tests of different aggregates showed, that the results of the automated and conventional test are consistent, but the expansions during the conventional test are generally higher. Preliminary results led to the conclusion, that the cooling for the measurements leads to additional expansions. Therefore, a modified threshold should be discussed for the automated 60 °C-CPT.
In recent years the German motorway network has seen an increase in the occurrence of damage to concrete road surfaces which can be attributed to the alkali-silica reaction (ASR). In view of the often drastically reduced life expectancy of road surfaces due to ASR, research activity in this field has notably increased. Alongside preventative measures in concrete technology, the main research focus up to now has been the development of performance-oriented testing procedures for ASR prevention. This included more specifically the accelerated simulation of climatic effects and external alkali penetration on road surfaces. The effects of mechanical pre-damage resulting from cyclic traffic loading and climatic impact had previously not been taken into consideration. Since 2011, the five-partner research group 1498 sponsored by the German Research Foundation (DFG) has been pursuing research on how simultaneous cyclic loading and external alkali penetration impacts destructive ASR in road surface concretes. The depiction of the myriad degradation and transport processes necessary for an understanding of these effects requires close interaction between experiments and their multi-scale modelling. This paper aims to focus on the aforementioned experiments by means of innovative testing techniques. The research is founded on a series of cyclic fatigue tests performed on large-format beams, both with and without previous application of a sodium chloride (NaCl) solution, with simultaneous tracking of crack development. Subsequently, smaller test specimens were extracted from the pre-damaged beams for further experiments. These included the spatial visualization and quantification of fatigue-induced cracks using micro X-ray 3D-computed tomography (3D-CT). Additionally, the effects of fatigue-induced cracks on alkali transport were investigated using Laser-Induced Breakdown Spectroscopy (LIBS). Subsequent storage of the small-format test specimens, with and without cyclic pre-damage, in an ASR-conducive environment then provided initial findings on the influence of fatigue-induced predamage on the ASR.
In diesem Beitrag werden Untersuchungsergebnisse vorgestellt, die den Einfluss von Mikrosilica auf die Selbstaustrocknung und das damit verbundene autogene Schwinden der Bindemittelmatrix von Hochleistungsbetonen beschreiben. Die dadurch hervorgerufenen Schädigungsprozesse wurden mit Hilfe von zerstörungsfreien Prüfmethoden verfolgt. Dabei zeigte sich, dass eine durch äußeren Zwang bedingte Mikrorissbildung durch Schallemissionsanalyse detektiert werden kann.
The susceptibility of concrete structures due to alkali–silica reaction (ASR) can be assessed by means of ASR concrete prism testing at 60 °C, according to RILEM AAR 4.1. There, expansion of concrete prisms indicates alkali-reactivity of the examined concrete mix. This work applies in situ expansion measurement to accelerated concrete prism testing. Automated measuring facilitates both storage without the usually necessary interruptions for manual measurement and acquisition of quasi-continuousexpansion data. A comparative experimental programme showed that conventional testing resulted in stronger expansion and leaching of alkalis than automated testing. Experimental simulation of interruptions, typically associated with manual measurements in conventional testing, could prove the influence of these cooling–heating cycles. Two phenomenological approaches, frequently used for describing reaction kinetics of ASR by linking it to expansion results from ASR-testing, were validated with continuous expansion data of three types of aggregate. Experimental expansion depicted s-shaped curves similar to them of the modelling approaches. However, strong swelling recorded in the beginning of the test was not covered by the model curves. Auxiliary measurement of acoustic emissions and ultrasonic velocity helped characterising mechanisms such as hydration and cracking, which also influence prism expansion. The proposed modification of the measurement procedure provides an extended basis to analyse expansion mechanisms. Regarding data for validation of ASR-expansion models, continuous expansion results are preferable to conventional test results.