Schlagworte
- Cement paste (2) (entfernen)
The complex matter of external sulphate attack on cement-based construction materials is still not completely understood. The concentration of sulphate is a crucial factor for the formation of secondary phases and phase transitions of cement hydrates due to sulphate ingress into the microstructure. The sulphate attack on building materials for high and low sulphate concentrations was monitored by laboratory experiments. Hardened cement paste consisting of ordinary Portland cement (CEM I) were exposed to aqueous solutions of sodium sulphate for 18 months. Three sample compositions were used for this research, including different supplementary cementitious materials (SCM). The phase composition was determined for different time spans by high resolution synchrotron X-ray diffraction. Cross sections of exposed cement prisms were investigated as a representation of the microstructural profile. Based on the data, a temporal and spatial determination of the stages of the sulphate attack and the deterioration course was possible. Cement matrices blended with slag showed the highest resistance against sulphate attack.
The exact mechanisms of the phase transitions caused by a combined sulphate-chloride attack are discussed controversially. The main points concern the mutual influences of sulphate and chloride ions during the secondary binding processes of these anions within cement hydrate phases. We simulated combined sulphate-chloride attack under laboratory conditions using solutions containing NaCl and Na2SO4 in different concentrations. Three sample compositions were used for the preparation of the specimens. In two of them, 30% of Portland cement was replaced by supplementary cementitious materials (fly ash, slag). The phase distribution in the samples was determined using synchrotron X-ray diffraction. The analysis with high spatial resolution allows the localisation of the secondary phase formation in the microstructural profile of the sample. A mechanism of the phase developments under combined sulphate-chloride attack is derived.