Several expandable graphites (EGs), differing in Expansion volume but with the same mean size, are compared as flame retardants in polyurethane (PUR) foams. Not only common sulfur-intercalated graphites are investigated but also a new one intercalated with phosphorus. The main aim of this article is to understand which properties of EG are important for its flame retardancy effectiveness in PUR foams. Thermal stability, flammability, and fire behavior are analyzed through limiting oxygen index and cone calorimeter tests. Detailed characterization of the phosphorus-intercalated graphite is also provided as well as physical–mechanical characterization. The results show that the well-known sulfur-intercalated graphites and the one with phosphorus both enhance the residue yield, induce a protective layer, and thus efficiently flame-retard PUR foams. While the expansion volume of the EGs had a surprisingly limited influence on the performance of the foams, at least in the range tested, the most important feature Controlling the effectiveness of EG in terms of flame retardant PUR foams was the type of intercalant. The presence of EG affected the physical–mechanical properties of the foams; however, no significant effect of the expansion volume or intercalant type has been revealed on the physical–mechanical properties of the foams.
Functionalized graphene nanosheets TRGO and MLG 250, prepared from thermally reduced graphite oxide, represent attractive carbon additives for improving the performance of flame retardant polypropylene (PP-FR). The influence of carbon nanofiller type and content on morphology, thermal, mechanical, and electrical properties as well as the fire behavior of melt-extruded PP-FR is investigated. In contrast to conventional nano- and micron-sized carbon fillers such as expanded graphite (EG 40), nano-scaled carbon black (CB), and multiwall carbon nanotubes (CNT), only TRGO and MLG 250 afford uniform dispersion combined with simultaneously improved stiffness (+80%), electrical conductivity (3 × 10-5 S · cm-1) and enhanced flame retardancy of PP-FR, as expressed by lower peak heat release rate (-76%).