Filtern
Erscheinungsjahr
- 2018 (10) (entfernen)
Dokumenttyp
- Zeitschriftenartikel (6)
- Vortrag (2)
- Beitrag zu einem Tagungsband (1)
- Posterpräsentation (1)
Schlagworte
- Flame retardant (3)
- Flame retardancy (2)
- Foam (2)
- Phosphorus (2)
- Acrylphosphate (1)
- Aliphatic polyester (1)
- Bench scale fire testing (1)
- Cables (1)
- DOPO (1)
- Fire behaviour (1)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (2)
Polyesters with 9,10-dihydro-9-oxy-10-phosphaphenanthrene-10-oxide-containing comonomers are synthesized aiming to improve the flame retardancy of aliphatic polyesters such as poly(butylene succinate) and poly(butylene sebacate). The influence of the chemical structure on the thermal decomposition and pyrolysis is examined using a combination of thermogravimetric analysis (TGA), TGA-Fourier transform infrared (FTIR) spectroscopy, pyrolysis-gas chromatography/mass spectrometry, and microscale combustion flow calorimetry. Thermal decomposition pathways are derived and used to select suitable candidates as flame retardants for PBS. The fire behavior of the selected polymers is evaluated by forced-flaming combustion in a cone calorimeter. The materials show two modes of action for flame retardancy: strong flame inhibition due to the release of a variety of molecules combined with charring in the solid state.
After introducing into the activities and competence of BAM in the field of fire science, several aspects of successful and tailored flame retardancy of polyolefins are discussed. The talk gives an overview of the works relevant for developing flame retardant polyolefins performed in the working group flame retardancy of polymers. The hypothesis of conservation of effective heat of combustion is proposed. The role of charring, inert fillers, protection layer, and intumescence is assessed for flame retarded polyolefins. Distinct routes of optimization sketched. Examples of controlling the dripping and melt flow to obtain the desired fire behaviour are discussed. Finally the cable modul for the cone calorimeter is presented.
Elastomers are usually mechanically reinforced with high loadings of carbon black (CB) to achieve the properties demanded; high amounts of mineral flame retardants are used to fulfill fire safety requirements. In this study, multilayer graphene (MLG), a nanoparticle made of only 10 graphene sheets, is applied in low loadings, 3 parts per hundred rubber (phr) to reduce the total amount of filler or boost performance in hydrogenated acrylonitrilebutadiene rubber (HNBR). In the HNBR/MLG nanocomposites, 3 phr MLG replaced 15 phr CB, 3 phr aluminum trihydroxide (ATH), or 15 phr CB + 3 phr ATH. The nanocomposites were prepared via master batch by ultrasonically assisted solution mixing and subsequent conventional two-roll milling. A comprehensive study is presented, illustrating the impact of MLG on curing and mechanical properties; e.g. replacing 2.5 phr ATH with 3 phr MLG increased the Young's modulus by over 60% and hardness by 10%, while improving flame retardancy, and reducing the total heat evolved by 10%. MLG is a multifunctional filler, as demonstrated by various enhancements in terms of the mechanical and flame retardancy properties of the rubber composites.
The rapid mass calorimeter (RMC) was used as a screening tool based on accelerated fire testing to assess flame-retarded thermoplastic polyurethane (TPU). The reliability of RMC results was proven with the cone calorimeter as reference fire test. The influence of melamine cyanurate (MC) concentration on the fire performance of TPU was investigated, along with some flame-retardant combinations such as MC with aluminium diethylphosphinate (AlPi), aluminium trihydrate (ATH), and melamine polyphosphate (MPP). The two-stage burning behaviour of TPU was investigated in detail; the first stage corresponds mainly to the hard segments' decomposition and has a much lower effective heat of combustion (EHC) than the second stage, in which mainly the soft segments decompose and an intensive liquid pool fire is observed in the cone calorimeter set-up. In addition to fire testing with the cone calorimeter, RMC, and UL 94 flammability tests, the decomposition of the materials was investigated using thermogravimetric analysis coupled with infrared spectrometry (TGeFTIR). TPU/MC/AlPi shows the most promising results, achieving V-0 classification in UL 94 and reducing the extreme peak heat release rate (PHRR) of the liquid pool fire from 3154 kW/m2 to 635 kW/m2. Using MC/AlPi/MPP enhances the latter PHRR reduction further. The decomposition products identified in the gas phase via TGeFTIR reveal specific MCeAlPi eMPP interactions, as they differ from products seen in systems with MC/AlPi or MC/MPP. Correlations between RMC and cone calorimeter results were examined and presented in the final part of the paper. Several characteristics correlate strongly, pointing out that RMC is a reliable high-throughput fire testing method to screen multicomponent flame-retardant solutions in TPU.
The ubiquity of polymeric materials in daily life Comes with an increased fire risk, and sustained research into efficient flame retardants is key to ensuring the safety of the populace and material goods from accidental fires. Phosphorus, a versatile and effective element for use in flame retardants, has the potential to supersede the halogenated variants that are still widely used today: current formulations employ a variety of modes of action and methods of implementation, as additives or as reactants, to solve the task of developing flameretarding polymeric materials. Phosphorus-based flame retardants can act in both the gas and condensed phase during a fire. This Review investigates how current phosphorus chemistry helps in reducing the flammability of polymers, and addresses the future of sustainable, efficient, and safe phosphorus-based flame-retardants from renewable sources.
High-throughput fire tests and weathering-induced degradation behaviour of intumescent coatings
(2018)
In this work, the weathering-induced degradation of intumescent coatings was investigated by a systematic and comprehensive approach. A mechanism is revealed that is proposed to be responsible for the loss of function of intumescent coatings induced by weathering.
First, the thermal decomposition of artificially weathered intumescent coatings was examined. To get a better understanding of the weathering and ageing phenomena, the degradation behaviour of the single ingredients during the weathering process was investigated, as well as their chemical and physical interactions. For the systematic approach, the materials that are essential for intumescence (ammonium polyphosphate, pentaerythritol, titanium dioxide, melamine and the binder) are treated with moisture, elevated temperature and UV radiation.
Thermogravimetry (TG) and IR spectroscopy were used to compare the initial samples with their different grades of weathering. We demonstrate that ammonium polyphosphate, melamine and the binder are mainly responsible for the ageing process. Further, it was demonstrated that TG and IR spectroscopy are suitable measuring methods to detect the effects of weathering on intumescent coatings.
Finally, a small-scale fire test procedure is introduced. Based on the reduction of the sample size, up to 50 samples can be tested in a single fire test. The results of this fire test have the same quality as the results from standard intermediate fire tests corresponding to DIN 4102-8.
The Role of Decomposition Temperature for Flame Redartancy Mode of Action in the Condensed Phase
(2018)
Condensed-phase mechanisms play a major role in fire-retardant polymers. Generations of development have followed the concept of charring to improve fire properties. Whereas the principal reactions are believed to be known, the specific description for multicomponent systems is lacking, as is the picture across different systems. One important aspect in achieving, adjusting and optimising flame retardancy in the condensed phase is exploiting chemical reactions between the pyrolysing polymer and flame retardant at the right place, time and temperature. It is the aim of this contribution to address the role of the decomposition temperature of both flame retardant and polymer by the means of two examples: First, aryl phosphates in Polycarbonate/ Acrylonitrile-Butadiene-Styrene (PC/ABS) blends, where the reaction with the early stage decomposition products of PC is controlling the flame retardancy mechanism in the condensed phase. Second, a comprehensive set of phosphorus flame retardants in thermosets and their corresponding carbon fibre reinforced composites based on two different epoxy systems. Both examples show that key reactions between intermediate decomposition products only occur when the decomposition temperature ranges correspond to each other. The systems can be shifted towards condensed phase activity such as charring or inorganic glass formation as well as towards phosphorus release and thus flame inhibition in the gas phase. Changing the role of flame retardancy mechanisms also influence the efficiency in the achieved flame retardancy.
Flexible polyurethane foams with densities of 40 ± 2 kg m−3 were prepared by combining different ecofriendly fillers such as layered double hydroxides (LDH) and kraft lignin (a byproduct of the pulp and paper industry) with a phosphorous polyol (E560) in order to study their effect on the mechanical performance and fire behavior of the foams. Two series of foams were prepared, some containing lignin or LDH separately, and some with a combination of both: one of the series was prepared without E560 (0E foam series) and the other with 5 parts per hundred of E560 polyol (5E series). The use of fillers resulted in increased viscosity of the reactive mixture, requiring higher blowing agent content in order to hold the density of the foams constant. It was observed that urea phase segregation was favored in the series of 0E foams due to their lower viscosity than the 5E series. This had consequent effects on the resilience, compression force deflection and compression set of these foams. In terms of fire behavior it was observed that while the limiting oxygen index decreased, cone calorimeter results showed that the combination of lignin, LDH and E560 decreased the heat release of the foams. In addition, the combination of fillers and E560 contributed to increase the viscosity of the pyrolysis products, preventing the dripping of the molten polymer, which is a key factor in flame propagation towards adjacent objects in fire scenarios.
Rigid polyurethane foams (RPUFs) typically exhibit low thermal inertia, resulting in short ignition times and rapid flame spread. In this study, the fire phenomena of RPUFs were investigated using a multi-methodological approach to gain detailed insight into the fire behaviour of pentaneand water-blown polyurethane (PUR) as well as pentane-blown polyisocyanurate Polyurethane (PIR) foams with densities ranging from 30 to 100 kg/m3. Thermophysical properties were studied using thermogravimetry (TG); flammability and fire behaviour were investigated by means of the limiting oxygen index (LOI) and a cone calorimeter. Temperature development in burning cone calorimeter specimens was monitored with thermocouples inside the foam samples and visual investigation of quenched specimens’ cross sections gave insight into the morphological changes during burning. A comprehensive investigation is presented, illuminating the processes taking place during foam combustion. Cone calorimeter tests revealed that in-depth absorption of radiation is a significant factor in estimating the time to ignition. Cross sections examined with an electron scanning microscope (SEM) revealed a pyrolysis front with an intact foam structure underneath, and temperature measurement inside burning specimens indicated that, as foam density increased, their burning behaviour shifted towards that of solid materials. The superior fire performance of PIR foams was found to be based on the cellular structure, which is retained in the residue to some extent.
Der Beitrag versucht sich an der Herausforderung, trotz beschränktem zeitlichen Rahmen einen ansprechenden Spagat zwischen umfangreichem Überblick und wissenschaftlichem Verständnis und so eine unabhängige und unparteiliche Einführung in Thematik flammgeschützte PUR-Schäume zu geben. Er kann sicherlich nicht individuelle Antworten oder konkrete Entwicklungsziele wie neue Rezepturvorschläge liefern, aber hofft zum Hintergrund und als Handwerkzeugs für das Aufstellen und Überdenken von Entwicklungsstrategien beizutragen.