The flame retardant effect of zinc sulphide (ZnS) in plasticised poly(vinyl chloride) (PVC-P) materials was investigated. PVC-P containing different combinations of additives such as 5% ZnS, 5% of antimony oxide (Sb2O3) and 5% of mixtures based on Sb2O3 and ZnS were compared. The thermal degradation and the combustion behaviour were studied using thermogravimetry (TG), coupled with FTIR (TG-FTIR) or with mass spectroscopy (TG-MS), and a cone calorimeter, respectively. A detailed and unambiguous understanding of the decomposition and release of the pyrolysis products was obtained using both TG-MS and TG-FTIR. The influence of ZnS, Sb2O3 and the corresponding mixtures on the thermal decomposition of PVC-P was demonstrated. Synergism was observed for the combination of the two additives. The combustion behaviour (time to ignition, heat release, smoke production, mass loss, CO production) was monitored versus external heat fluxes between 30 and 75 kW m-2 with the cone calorimeter. Adding 5% of ZnS has no significant influence on the fire behaviour of PVC-P materials beyond a dilution effect, whereas Sb2O3 works as an effective fire retardant. Synergism of ZnS and Sb2O3 allows the possibility of replacing half of Sb2O3 by ZnS to reach equivalent fire retardancy.
Polymeric nanocomposites are discussed as one of the most promising advanced materials whose nanoscale effects can be exploited for industry. Layered silicate polypropylene-graft-maleic anhydride nanocomposites are investigated as a model to clarify the potential of such materials in terms of fire retardancy. The nanostructure is characterized using transmission electron microscopy (TEM) and shear viscosity. The fire behavior is characterized using different external heat fluxes in cone calorimeter, limiting oxygen index and UL 94 classification. A comprehensive fire behavior characterization is presented which enables an assessment of the materials’ potential with respect to different fire scenarios and fire tests. The influence of morphology and the active mechanisms are discussed, such as barrier formation and changed melt viscosity. To our knowledge, it is the first attempt to illuminate the concept’s strengths, such as the reduction of flame spread, and weaknesses, such as the lack of influence on ignitability, in a clear, comprehensive and detailed manner.
The thermal degradation and the combustion behavior of glass fiber-reinforced PA 66 materials containing red phosphorus were investigated. Thermogravimetry (TG), TG coupled with FTIR, and TG coupled with mass spectroscopy were used to investigate the thermal decomposition. The flame retardant red phosphorus was investigated with respect to the decomposition kinetics and the release of volatile products. The combustion behavior was characterized using a cone calorimeter. Fire risks and fire hazards were monitored versus external heat fluxes between 30 and 75 kW/m2. Red phosphorus acts in the solid phase and its efficiency depends on the external heat flux. The use of red phosphorus results in an increased amount of residue and in a corresponding decrease in total heat release. The decrease of the mass loss rate peak results in a corresponding decrease of the peak heat release. With increasing external heat flux applied the first effect on the total heat release decreases linearly, whereas the second effect on the peak heat release expands linearly. The investigation provides insight into the mechanisms of how the fire retardant PA 66 is achieved by red phosphorus controlling the degradation kinetics. Taking into account that a decrease of the volatile products also leads to a decrease of heat production in the flame zone and that the char acts as heat transfer barrier, a reduced pyrolysis temperature is suggested as a further feedback effect.
Pyrolysis and fire behavior of high impact polystyrene (HIPS) containing red phosphorus and melamine polyphosphate were investigated. The thermal and thermo-oxidative decomposition were characterized using thermogravimetry coupled with FTIR and MS, respectively. The fire behavior was monitored with a cone calorimeter using different external heat fluxes and determining the LOI. Red phosphorus reduced the heat release in HIPS due to radical trapping in the gas phase. The reduction in effective heat of combustion was accompanied by an increase of incomplete combustion products such as smoke and carbon monoxide. Melamine polyphosphate in HIPS acted in the condensed phase with barrier formation. The heat release rate was reduced, whereas the total heat evolved, smoke and carbon monoxide formation were not influenced significantly. Using both fire retardants, the resulting fire retardancy was characterized mainly by superposition.
The cone calorimeter has become one of the most important and widely used instruments for the research and development of fire retarded polymeric materials. The paper addresses three important ways in which the principal setup influences the results factors which sometimes do not receive due consideration when drawing conclusions. The paper discusses in detail the impact on cone calorimeter results of the choice of external heat flux, the influence on the peak of heat release rate of sample thickness and thermal feedback from the back of the sample, and the influence on irradiance of the horizontal and vertical distances from the cone heater.
Flame Retardant Mechanisms of Red Phosphorus and Magnesium Hydroxide in High Impact Polystyrene
(2004)
The flame retardant mechanisms of red phosphorus, magnesium hydroxide and red phosphorus combined with magnesium hydroxide were studied in high impact polystyrene by means of comprehensive decomposition studies and combustion tests. The study is intended to illuminate prerequisites and the potential of red phosphorus as a fire retardant for hydrocarbon polymers in the condensed phase and in the gas phase. Thermal and thermo-oxidative decomposition, decomposition kinetics and the product gases evolved were characterized using thermogravimetry coupled with Fourier transform infrared spectroscopy and mass spectroscopy, respectively. Fire behaviour was investigated with a cone calorimeter using different external heat fluxes, whereas the flammability was determined by limited oxygen indices. The combustion residues were analysed using XPS. Red phosphorus reduced the heat release in HIPS due to radical trapping in the gas phase. Magnesium hydroxide influenced fire behaviour by heat sink mechanisms, release of water and the formation of a magnesia layer acting as a barrier. The combination of both flame retardants in HIPS nearly resulted in a superposition. A slight synergy in barrier characteristics was due to the formation of magnesium phosphate, whereas a slight anti-synergism occurred in flammability and in the gas phase action. The latter effect is controlled by a decreased fuel rate due to the barrier layer rather than by an initiation of red phosphorus oxidation in the condensed phase.