Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (212)
- Vortrag (111)
- Beitrag zu einem Tagungsband (29)
- Beitrag zu einem Sammelband (18)
- Buchkapitel (10)
- Posterpräsentation (6)
- Monografie (2)
- Forschungsbericht (1)
Sprache
- Englisch (313)
- Deutsch (73)
- Mehrsprachig (3)
Schlagworte
- Flame retardancy (67)
- Flame retardant (40)
- Flammability (34)
- Fire retardancy (29)
- Cone calorimeter (28)
- Nanocomposites (27)
- Epoxy resin (24)
- Flame retardance (23)
- Pyrolysis (23)
- Graphene (21)
Organisationseinheit der BAM
Paper des Monats
- ja (1)
Eingeladener Vortrag
- nein (111)
The flame retardant effect of zinc sulphide (ZnS) in plasticised poly(vinyl chloride) (PVC-P) materials was investigated. PVC-P containing different combinations of additives such as 5% ZnS, 5% of antimony oxide (Sb2O3) and 5% of mixtures based on Sb2O3 and ZnS were compared. The thermal degradation and the combustion behaviour were studied using thermogravimetry (TG), coupled with FTIR (TG-FTIR) or with mass spectroscopy (TG-MS), and a cone calorimeter, respectively. A detailed and unambiguous understanding of the decomposition and release of the pyrolysis products was obtained using both TG-MS and TG-FTIR. The influence of ZnS, Sb2O3 and the corresponding mixtures on the thermal decomposition of PVC-P was demonstrated. Synergism was observed for the combination of the two additives. The combustion behaviour (time to ignition, heat release, smoke production, mass loss, CO production) was monitored versus external heat fluxes between 30 and 75 kW m-2 with the cone calorimeter. Adding 5% of ZnS has no significant influence on the fire behaviour of PVC-P materials beyond a dilution effect, whereas Sb2O3 works as an effective fire retardant. Synergism of ZnS and Sb2O3 allows the possibility of replacing half of Sb2O3 by ZnS to reach equivalent fire retardancy.
Das Ziel des Forschungsvorhabens war die Untersuchung der Wirkungsweise von halogenfreien Flammschutzmitteln in WPC.
Eine große Anzahl verschiedener Flammschutzmittel wurde hinsichtlich ihrer Wirkmechanismen umfassend untersucht, um ein Verständnis für die ablaufenden Prozesse zu entwickeln. Hierbei wurden verschiedene Brandtests eingesetzt, um die Materialien bezüglich verschiedener Applikationen (E&E, Transportwesen, Bauwesen) zu beleuchten.
Die verschiedenen Untersuchungen liefern aber auch ein umfassendes Bild vom Brandverhalten in den verschiedenen Eigenschaften, wie Entflammbarkeit und Brandausbreitung.
Die prinzipiellen Ansätze wurden anhand von verschiedenen Flammschutzmitteln beleuchtet, ihre Pyrolyse und ihre Performance in verschiedenen Brandtests gegenübergestellt. Bei der angestrebten geringen Zusatzmenge ist durch den Zusatz eines einzigen Flammschutzmittels keine zufriedenstellende Reduktion der Brandeigenschaften zu erwarten. Multikomponentensysteme zur Steigerung der Effizienz sind angezeigt. Einige prinzipielle Kombinationsmöglichkeiten wurden für alle Hauptflammschutzmittel durchgespielt. Die teilweise deutlichen Verbesserungen zeigen Wege zur erfolgreichen Produktentwicklung auf. So konnten bei den Spritzgießcompounds Eigenschaften erzielt werden, die eine UL 94 V0 Klassifizierung ermöglichen.
Ein Einsatz der im Forschungsvorhaben hergestellten Compounds als Baustoff ist aufgrund des Brandverhaltens in den baustoffspezifischen Prüfungen nicht möglich. Hier sind weitere Flammschutz-Konzepte zu erproben.
Gleitmittel nehmen bei den untersuchten Extrusionscompounds keinen Einfluss auf das Brandverhalten. Haftvermittler nehmen ebenfalls keinen signifikanten Einfluss auf das untersuchte Brandverhalten, können aber zu einer veränderten Verteilung der Füllstoffe
und damit zur Ausbildung einer effektiveren Schutzschicht führen.
Feinere Holzpartikel schneiden bei den Brandprüfungen besser ab als grobe Holzpartikel.
Bei Einsatz von grobem Holz wird eine schlechtere Rückstandsstruktur ausgebildet, was das Brandverhalten negativ beeinflusst. Der Einsatz von vorbehandeltem Holz
brachte nicht die erwartete Verbesserung.
Die neu konzipierte Aufbereitungsanlage auf Basis des Planetwalzenextruders konnte erfolgreich in Betrieb genommen werden. Vergleichende Versuche mit dem Doppelschneckenextruder zeigten, dass der PWE-Aufbau eine gute Alternative zur etablierten DSE-Aufbereitung darstellt.
Zusätzlich wurden an Compounds vielversprechender Flammschutzansätze weitere Materialprüfungen (Biegeversuch, Schlagversuch, Wasseraufnahme) durchgeführt, um den Einfluss der FSM auf die spezifischen Eigenschaften der WPC zu beleuchten.
The pyrolysis and flame retardancy of a bisphenol A polycarbonate/silicon rubber/bisphenol A bis(diphenyl phosphate) (PC/SiR/BDP) blend were investigated and compared to those of PC/BDP and PC/SiR. The impact modifier SiR consists mainly of poly(dimethylsiloxane) (PDMS > 80 wt %). The pyrolysis of PC/SiR/BDP was studied by thermogravimetry (TG), TG–FTIR to analyze the evolved gases, and a Linkam hot stage cell within FTIR as well as 29Si NMR and 31P NMR to analyze the solid residue. The fire performance was determined by PCFC, LOI, UL 94, and a cone calorimeter under different external irradiations. The fire residues were studied by using ATR-FTIR as well as the additional binary systems PC + PDMS, PC + BDP, and BDP + PDMS, focusing on the specific chemical interactions. The decomposition pathways are revealed, focusing on the competing interaction between the components. Fire retardancy in PC/SiR/BDP is caused by both flame inhibition in the gas phase and inorganic-carbonaceous residue formation in the condensed phase. The PC/SiR/BDP does not work as well superimposing the PC/SiR and PC/BDP performances. PDMS reacts with PC and BDP, decreasing BDP's mode of action. Nevertheless, the flammability (LOI > 37%, UL 94 V-0) of PC/SiR/BDP equals the high level of PC/BDP. Indeed, SiR in PC/SiR/BDP is underlined as a promising impact modifier in flame-retarded PC/impact modifier blends as an alternative to highly flammable impact modifiers such as acrylonitrile–butadiene–styrene (ABS), taking into account that the chosen SiR leads to PC blends with a similar mechanical performance.
Whereas the degradation of flame retardant polymers has been discussed since decades, only more recently, the lifetime of the flame retardancy itself becomes an important factor, e.g. for cables used as building products. In this work, several kinds of accelerated artificial ageing tests are performed simulating different environmental exposures and thus highlighting different degradation mechanisms: artificial accelerated weathering, climatic chamber, water immersion, salt spray chamber, and autoclave test. The durability is expected to be different for different flame-retardant materials. Thus, various sets of halogen-free fire-retarded polymers were investigated: ethylene vinyl acetate (EVA) with aluminum hydroxide (ATH), boehmite and synergists, ester-based and ether-based thermoplastic polyurethane (TPU) with melamine cyanurate (MC), aluminum diethylphosphinate (AlPi), and boehmite, and glass fiber reinforced polyamide 66 (PA66) with AlPi-based mixtures.
Intensive degradation of the surface was observed, e.g. yielding discoloration and yellowing, EVA showed cracking when weathered. Changes in chemical structure was investigated by ATR-FTIR. The flammability was investigated with the cone calorimeter, UL-94 classification, and oxygen index (LOI). The flame retardancy of most of the materials studied degraded only slightly for the investigated exposure times. EVA/ATH achieved an improved LOI due to flame retardants agglomeration at the surface. Sets of materials, based on EVA and TPU, were also investigated as cable jackets. While flame retarded EVA exhibited no dripping during burning, TPU flame-retarded with MC cables showed pronounced melt-dripping. Cone calorimeter tests were carried out using cable rafts as well as our self-made cable module test, simulating a vertical bundle of cables at the bench scale. The comparison of different fire tests, different exposure conditions, and different materials carved out the specific degradation phenomena with respect to each of these parameters.
Most of this work was supported by the IGF Project (18926 N) of the Fördergemeinschaft für das Süddeutsche Kunststoff-Zentrum e.V., supported by the AiF within the framework of the program “Förderung der Industriellen Gemeinschaftsforschung (IGF)” of the German Federal Ministry for Economic Affairs and Energy based on a decision of the Deutschen Bundestag.
The influence of weathering on the fire retardancy of polymers is investigated by means of a cone calorimeter test, before and after artificial weathering. The surface degradation was monitored using different techniques (ATR–FTIR, microscopy, colour measurement). Different kinds of polymeric materials were chosen, all as they are used in practice: polycarbonate (PC) blends, polyamide (PA) and polypropylene (PP) flame-retarded with arylphosphate, melamine cyanurate (MC) and intumescent formulation based on ammonium polyphosphate (APP), respectively.
All samples show material degradation at the surface due to weathering. No significant weathering influence occurs on the flame retardancy when it is a bulk property, as was observed for aryl phosphates in PC blends and MC in PA. When the fire retardancy is dominated by a surface mechanism, dependence on the duration of weathering is detected: for intumescent formulations based on ammonium APP in PP, a worsening in the formation of the intumescent network was observed.