The pyrolysis and fire behavior of halogen-free flame-retarded DGEBA/DMC, RTM6 and their corresponding 60 vol.-% carbon fibers (CF) composites were investigated. A novel phosphorous compound (DOPI) was used. Its action is dependent on the epoxy matrix. DGEBA/DMC and DOPI decompose independently of each other. Only flame inhibition occurs in the gas phase. RTM6 shows flame inhibition and a condensed phase interaction increasing charring. Both mechanisms decrease with increasing irradiance, whereas in RTM6-CF charring is suppressed at low ones. RTM6+DOPI shows a higher LOI (34.2%) than DGEBA/DMC+DOPI and a V-0 classification in UL 94. Adding CF only enhances the LOI, DOPI+CF leads to a superposition in LOI for DGEBA/DMC-CF+DOPI (31.8%, V-0) and a synergism for RTM6-CF+DOPI (47.7%, V-0).
Starting from trivalent 10-alkoxy-10H-9-oxa-10-phosphaphenanthrenes, a broad range of DOPO derivatives was synthesized via transesterification with aliphatic alcohols and subsequent Michaelis-Arbuzov rearrangement using catalytic amounts of p-toluenesulfonic acid methylester. Due to the considerable differences in the nature of the alcohols employed, several procedures for processing them are presented.
10-Ethyl-9-oxa-10-phosphaphenanthrene-10-oxide (1) can be nitrated using acetic anhydride and fuming nitric acid. The nitro group is reduced using palladium on charcoal and hydrogen. These reaction conditions are used for the synthesis of an analogous DOPO-based diaminic hardener (7). An evaluation of the curing behavior, mechanical properties and flammability of a neat resin made of DGEBA and 7 (DGEBA + 7) and of a carbon fiber-reinforced resin made of DGEBA, 4,4-diaminodiphenylsulfon (DDS) and 7 (DGEBA + DDS + 7) shows the potential of this hardener to lead to flame-retardant systems while keeping relevant properties on a high level; especially when compared to a similar system (DGEBA + DDS + 1).
The reactivity of the flame retardant and its decomposition temperature control the condensed-phase action in bisphenol A polycarbonate/acrylonitrile–butadiene–styrene/polytetrafluoroethylene (PC/ABSPTFE) blends. Thus, to increase charring in the condensed phase of PC/ABSPTFE + aryl phosphate, two halogen-free flame retardants were synthesized: 3,3,5-trimethylcyclohexylbisphenol bis(diphenyl phosphate) (TMC-BDP) and bisphenol A bis(diethyl phosphate) (BEP). Their performance is compared to bisphenol A bis(diphenyl phosphate) (BDP) in PC/ABSPTFE blend. The comprehensive study was carried out using thermogravimetry (TG); TG coupled with Fourier transform infrared spectrometer (TG-FTIR); the Underwriters Laboratory burning chamber (UL 94); limiting oxygen index (LOI); cone calorimeter at different irradiations; tensile, bending and heat distortion temperature tests; as well as rheological studies and differential scanning calorimeter (DSC). With respect to pyrolysis, TMC-BDP works as well as BDP in the PC/ABSPTFE blend by enhancing the cross-linking of PC, whereas BEP shows worse performance because it prefers cross-linking with itself rather than with PC. As to its fire behavior, PC/ABSPTFE + TMC-BDP presents results very similar to PC/ABSPTFE + BDP; the blend PC/ABSPTFE + BEP shows lower flame inhibition and higher total heat evolved (THE). The UL 94 for the materials with TMC-BDP and BDP improved from HB to V0 for specimens of 3.2 mm thickness compared to PC/ABSPTFE and PC/ABSPTFE + BEP; the LOI increased from around 24% up to around 28%, respectively. BEP works as the strongest plasticizer in PC/ABSPTFE, whereas the blends with TMC-BDP and BDP present the same rheological properties. PC/ABSPTFE + TMC-BDP exhibits the best mechanical properties among all flame-retarded blends.
PET-P-DOPO is a phosphorus-containing polyester prepared from the glycol ether of the hydroquinone derivative of 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) and dimethyl terephthalate. PET-P-DOPO and a blend of PBT with PET-PDOPO were investigated with respect to pyrolysis and fire behavior. PET-P-DOPO achieves a V-0 rating in the UL 94 test and exhibits a high LOI of 39.3%. The outstanding flame-retardant properties of PET-P-DOPO are the result of three different mechanisms (flame inhibition, charring and a protection effect of the intumescent char) that are active in PET-P-DOPO. The fire load and the peak of heat release rate (pHRR) are reduced to 34% and 17%, respectively. The char exhibits an intumescent multicellular structure enabling it to act as an efficient protection layer. As PET-P-DOPO is immiscible with PBT, the blend shows a lower breaking elongation than pure PBT. Compared to pure PET-P-DOPO, the flame retardancy of the blend is decreased according to the fraction of PET-P-DOPO used. Nevertheless, the flame-retardancy of PET-P-DOPO in the blend was good enough to compete with PBT flame-retarded by AlPi-Et (aluminum diethylphosphinate) that was used as a Benchmark.
Condensed-phase mechanisms play a major role in fire-retardant polymers. Generations of development have followed the concept of charring to improve fire properties. Whereas the principal reactions are believed to be known, the specific description for multicomponent systems is lacking, as is the picture across different systems. A two-step approach is proposed in general, and also presented in greater detail. The second step covers the specific reactions controlling charring, whereas the actual reactants are provided in the preceding step. This model consistently incorporates the variety of structureproperty relationships reported. A comprehensive case study is presented on seven phosphorus flame retardants in two epoxy resins to breathe life into the two-step approach.