Cathodic protection (CP) is a common method for rehabilitation of reinforced concrete structures suffering from Chloride induced corrosion. A sufficient protection of the corroding rebar can be ensured by use of several protection criteria. The use of these assessment criteria, in particular the so called 100 mV-criterion, can lead to erroneous resuits for certain unconventional arrangements of rebar and cp anode.
Therefore a joint research project of the Institute for Building Materials Research, RWTH-Aachen University, Germany, (ibac) and the Federal Institute for Materials Research and Testing, Berlin, Germany, (BAM) has been set up to determine the applicability of CP under arbitrary geometrical conditions. A special focus was set on the applicability of surface applied anode Systems for protection of the reinforcement of structures opposite to the accessible side (e.g. outer side of tunnel Shell, Bridge deck protected from inside a box girder) In this paper, the impact of the time dependent changes of the Polarisation behaviour of the rebar on the current and potential distribution is shown by means of parametric studies using the FEM method.
Die Instandsetzung von Stahlbetonbauteilen bzw.-werken, welche durch chloridinduzierte Korrosion der Bewehrung gefährdet oder bereits geschädigt sind, hat in den letzten Jahrzehnten weltweit an Bedeutung gewonnen. Der kathodische Korrosionsschutz, als elektrochemisches Instandsetzungsverfahren, bildet in diesem Fall eine zuverlässige und oftmals kostengünstige Methode zur Instandsetzung. Am Beispiel des Parkhauses Am Gericht in Frankfurt am Main werden die Durchführung solch einer Maßnahme sowie die Besonderheiten des Verfahrens beschrieben. Es werden die theoretischen Hintergründe erläutert und die praktische Umsetzung sowie zu klärende Detailfragen beschrieben. Die Daten der ersten Depolarisationsmessungen zeigen den aktuellen Zustand der Anlage sowie des Schutzobjektes.
Pitting corrosion of carbon steel and iron in chloride containing alkaline environment is already well investigated, although a couple of questions are not clarified satisfactorily. The critical chloride content for steel in concrete and the critical chloride to hydroxide ion ratio for steel in alkaline solutions is still a major concern, considering chloride induced corrosion problems of steel in concrete. Another not satisfactorily clarified point is the repassivation of carbon steel in consequence of cathodic polarization. In the recent literature some indications are shown that repassivation occurs after a certain time of polarization. GLASS [4-9] and PEDEFERRI [1-3] draw the conclusion that the ennoblement of open circuit potentials (OCP) indicates re-passivation effects due to cathodic polarization. SAGÜÉS [10] carried out potentiodynamic repassivation tests and draws the conclusion that the repassivation potential Er is nearly independent of the solution composition, but influenced by severity of corrosion attack and is in the potential range from - 0.8 V to - 0.4 V vs. Saturated Calomel Electrode (SCE). The transferability of SAGÜÉS results to questions concerning cathodic protection (cp) is questionable, as potentiodynamic polarization tests (PPT) give no information on changes induced by long time polarization.
Therefore, the investigations discussed in this paper aim to clarify, to what extend the re-passivation of carbon steel due to cathodic polarization occurs, and if the ennoblement of OCP is a sufficient indication for repassivation. In a first step the corrosion state of five nominal equal test specimens was determined by electrochemical techniques, i.e. electrochemical noise measurements (ENM) and electrochemical impedance spectroscopy (EIS). After determining the initial corrosion state by evaluating the charge transfer resistance and the polarization resistance respectively as well as evaluating potential and current noise signals, the specimens were polarized cathodically. Impedance data were recorded previous to, during and after polarization. The impedance data were evaluated by equivalent circuit fitting with special attention to charge transfer resistances and diffusion properties. The results show that reduction of oxides and oxygen diffusion during cathodic polarization has strong impact on the systems behavior.