The creep behavior of single crystals of the nickel-based superalloy CMSX-4 was investigated at 1288 °C, which is the temperature of the hot isostatic pressing treatment applied to this superalloy in the industry. It was found that at this super-solvus temperature, where no gammaPrime-strengthening occurs, the superalloy is very soft and rapidly deforms under stresses between 4 and 16 MPa. The creep resistance was found to be very anisotropic, e.g., the creep rate of [001] crystals was about 11 times higher than that of a [111] crystal. The specimens of different orientations also showed a very different necking behavior. The reduction of the cross-sectional area psi of [001] crystals reached nearly 100 pct, while for a [111] crystal psi = 62 pct. The EBSD analysis of deformed specimens showed that despite such a large local strain the [001] crystals did not recrystallize, while a less deformed [111] crystal totally recrystallized within the necking zone. The recrystallization degree was found to be correlated with deformation behavior as well as with dwell time at high temperature. From the analysis of the obtained results (creep anisotropy, stress dependence of the creep rate, traces of shear deformation, and TEM observations), it was concluded that the main strain contribution resulted from <01-1>{111} octahedral slip.
A γ-analogue of the superalloy CMSX-4 that does not contain the strengthening γ′ -phase and only consists of the γ-solid solution of nickel has been designed, solidified as single-crystals of different orientations, and tested under creep conditions in the temperature range between 1150 and 1288 °C. The tests have revealed a very high creep anisotropy of this alloy, as was previously found for CMSX-4 at supersolvus temperature of 1288 °C. This creep anisotropy could be explained by the dominance of 〈011〉{111} octahedral slip. Furthermore, the analysis of the creep data has yielded a high value of the creep activation energy, Qc≈442 kJ/mol, which correlates with the high activation energy of Re diffusion in Ni. This supports the hypothesis that dislocation motion in the γ-matrix of Re-containing superalloys is controlled by the diffusion of the Re atoms segregating at the dislocation core. The Norton stress exponent n is close to 5, which is a typical value for pure metals and their alloys. The absence of γ′ -reprecipitation after high-temperature creep tests facilitates microstructural investigations. It has been shown by EBSD that creep deformation results in an increasing misorientation of the existing low angle boundaries. In addition, according to TEM, new low angle boundaries appear due to reactions of the a/2 〈011〉 mobile dislocations and knitting of new networks.
The large number of TEM investigations and the regular microstructure
of single-crystal nickel-base superalloys has boosted the development of a number of physically motivated constitutive laws. In contrast to the more phenomenological models discussed in the next chapter, these models use dislocation densities as internal variables. Obvious advantages are that the computed densities can be compared to TEM observations and the Deformation mechanisms can be easier translated into mathematical equations.
Single crystal superalloys usually contain pores of sizes 5-10 micro-m after casting and heat treatment. These pores can be reduced under compression by combined creep and diffusion in a subsequent treatment called Hot Isostatic Pressing (HIP). The paper presents a methodology to simulate pore shrinkage under HIP conditions in two dimensions (2D).
At the scale of the pores, which is also the scale of the sub-grains (<50 micro-m) the dislocation sources cannot be assumed to be homogeneously distributed. Thus, the applicability of classical crystal plasticity is questionable. In this case, the transport of dislocations under an applied stress from the location where they are nucleated must be explicitly modelled. This is done by solving the transport equations for the dislocation densities and the elasticity equations in 2D. The dislocations are assumed to be nucleated at Low Angle Boundaries. They glide or climb through the sub-grains with a stress dependent velocity.
The transport equations are solved by the Flux-Corrected Transport method, which belongs to the predictor-corrector class of algorithms. In the first step, an artificial diffusion is introduced, which suppresses spurious oscillations of the solution. In a second step, the solution is corrected in such a way that no additional extremes appear and that the extremes do not grow. The algorithm is validated by simulating the transport of simple distributions with a constant velocity field.
With the dislocation velocities and the computed dislocation densities, the inelastic shear rate at the slip system level is computed by integrating the Orowan equation. In the 2D-setting, three slip systems are considered. The contributions of these slip systems are summed up to obtain the total inelastic strain rate. Dislocation glide and climb and the coupling of climb with vacancies diffusion are considered.
The resolution of the equilibrium equations from the inelastic strains turned out to be prone to numerical instabilities. As an alternative, the stresses are directly computed from the distribution of geometrically necessary dislocations following the method presented in. The resulting boundary value problem is solved by the Least-Square Finite Element method.
Examples of simulations are presented for a representative region under creep tension and for a pore shrinking under external pressure.
The creep behavior of single-crystals of the nickel-base superalloy CMSX-4 was investigated at 1288°C, which is the temperature of the hot isostatic pressing (HIP) treatment applied to this superalloy in the industry. It was found that at this super-solvus temperature, where no Gamma’-strengthening occurs, the superalloy is very soft and rapidly deforms under stresses between 4 and 16 MPa. The creep resistance was found to be very anisotropic, e.g. the creep rate of [001] crystals was about 11 times higher than that of a [111] crystal. The specimens of different orientations also showed a very different necking behavior. The reduction of the cross-section area psi of [001] crystals reached nearly 100%, while for a [111] crystal psi=62%. The EBSD analysis of deformed specimens showed that despite such a large local strain the [001] crystals didn’t not recrystallize, while a less deformed [111] crystal totally recrystallized within the necking zone. From the shape of deformed specimens and TEM investigations it was concluded that the main strain contribution resulted from <011> {111} octahedral slip.
Gas turbines are widely used for a variety of purposes including power generation, compression or as jet engines in aircrafts. The critical components of a gas turbine are the high-pressure turbine blades which operate under severe conditions. These include thermo-mechanical loadings over temperatures ranging from room temperature up to 1100°C.
While a large number of constitutive models for single crystals have been proposed, most applications are restricted to special loading scenarios, temperature range and deformation mechanisms. In particular, a number of models are focused on pure creep. Only a few papers consider application of both creep and fatigue. Applications of the constitutive models to long-term stress relaxation are even scarcer. The new model assumes deformation-induced softening and can properly reproduce the viscous behavior at different time scales.
The model has been calibrated with the uniaxial tests at 800°C and 950°C in [001], [011] and [111] specimens of a nickel-basis superalloy. The predicted creep, short- and long-term relaxation and cyclic tests are in reasonable agreement with the experimental observations.
Rafting during high temperature deformation in a single crystal superalloy: experiments and modeling
(2012)
Experimental characterization and mechanical modeling of creep induced rafting in superalloys
(2012)
A constitutive model has been developed for the high temperature mechanical behavior of single crystal superalloys, including rafting and its consequences. The flow stress depends on the γ channel width via the Orowan stress. An evolution equation for channel widening during high temperature straining has been derived and calibrated with measurements. Therein, rafting is assumed to be driven by the relaxation of internal stresses. The model is able to represent the mechanical softening at high stresses consecutive to rafting. The model has been applied to simulate rafting during uniaxial creep in several crystal orientations, in notched specimens as well as in cyclically loaded specimens.
Constitutive modelling of creep degradation due to rafting in single-crystalline Ni-base superalloys
(2009)
A constitutive model for the mechanical behaviour of single-crystalline superalloys at high temperatures has been developed. The model relies on the slip system theory and is able to predict rafting and its influence on plastic flow. The kinetics of rafting are assumed to be driven by the reduction of the internal stresses represented by the macroscopic back-stress. The rafting effect is incorporated in the model through the dependence of the Orowan stress on the channel width. The model has been validated for the alloy CMSX-4 at 950 °C. The rafting part of the model has been calibrated by measurements of the channel widths after several levels of creep strains and for several loads.
Single-crystal components made of nickel base superalloys contain pores after casting and homogenization heat treatment. Hot isostatic pressing (HIP), which is carried above the γ' -solvus temperature of the alloy, is industrially applied to reduce porosity. A modeling of HIP based on continuously distributed dislocations is developed in a 2D setting. Glide and climb of straight-edge dislocations, as well as vacancy diffusion, are the deformation mechanisms taken into account.
Thereby, dislocation glide is controlled by dragging a cloud of large atoms, and climb is controlled by vacancy diffusion. Relying on previous investigations of the creep behavior at HIP temperatures, it is assumed that new dislocations are nucleated at low-angle boundaries (LAB) and move through subgrains until they either reach the opposite LABs or react with other dislocations and annihilate.
Vacancies are created at the pore surface and diffuse through the alloy until they are either consumed by climbing dislocations or disappear at the LABs. The field equations are solved by finite elements. It is shown that pore shrinking is mostly controlled by vacancy diffusion as the shear stresses at the LABs are too low to
nucleate a sufficient amount of dislocations.
Material modelling and lifetime prediction of Ni-base gas turbine blades under TMF conditions
(2014)
Under cyclic thermomechanical loading conditions, various damage mechanisms such as strain accumulation, creep cavitation, ageing, fatigue surface cracking etc. may take place in the material of a gas turbine blade. Depending on the loading conditions, all these effects can contribute to reduce the lifetime of the component. Subject of the present work is the development of a material model to describe the mechanical effects mentioned above, as well as the development of a lifetime model able to discriminate the different damage mechanisms.
Under cyclic thermomechanical loading conditions, various effects such as strain accumulation, creep damage, ageing, fatigue etc. may occur in the material of a gas turbine blade. Depending on the loading conditions, all these effects contribute to reduce the lifetime of the component. Subject of the present work is the development of a lifetime model able to discriminate between the different damage mechanisms, as well as the development of a material model to describe the mentioned effects and thus providing the input data for lifetime prediction.
Gas turbines are widely used for a variety of purposes including power generation, compression or as jet engines in aircrafts. The critical components of a gas turbine are the high-pressure turbine blades which operate under severe conditions. These include thermo-mechanical loadings over temperatures ranging from room temperature up to 1100°C.
While a large number of constitutive models for single crystals have been proposed, most applications are restricted to special loading scenarios, temperature range and deformation mechanisms. In particular, a number of models are focused on pure creep. Only a few papers consider application of both creep and fatigue. Applications of the constitutive models to long-term stress relaxation are even scarcer. The new model assumes deformation-induced softening and can properly reproduce the viscous behavior at different time scales.
The model has been calibrated with the uniaxial tests at 800°C and 950°C in [001], [011] and [111] specimens of a nickel-basis superalloy. The predicted creep, short- and long-term relaxation and cyclic tests are in reasonable agreement with the experimental observations.
It is shown experimentally that, during annealing and creep under low applied stresses, matrix dislocation loops frequently cross-glide. The periodic length of the zigzag dislocations deposited in the interfaces is equal to that of the γ/γ'-microstructure. Initially, the zigzag dislocations move in the (001) interface by a combination of glide and climb but then they stop near the γ'-edges and align along (100). Reactions of such dislocations lead to the formation of square interfacial networks consisting of (100) oriented edge dislocations. The complex dislocation movement is explained by the inhomogeneity of the misfit stresses between γ- and γ'-lattices. The tensile components of the stress tensor drive the dislocations through the channel, whereas the shear components near the γ'-edges cause the zigzag movement and the (100) alignment. The total effect is the most efficient relaxation of the misfit stresses. The results are relevant, especially for single-crystal superalloys of the newest generations, which have an increased γ/γ'-misfit due to the high level of refractory elements.
Micromechanical investigations and modelling of a copper-antimony-alloy under creep conditions
(2014)
In many practical applications, creep damage is the limiting factor of a components lifetime. A micromechanical model of creep induced grain boundary damage is proposed, which allows for the simulation of creep damage in a polycrystal within the framework of finite element analysis. The model considers grain boundary cavitation and sliding according to a micromechanically motivated cohesive zone model while creep deformation of the grains is described following the slip system theory. The model can be applied to idealised polycrystalline structures, such as a Voronoi tessellation or, like demonstrated here, to real grain structures of miniature creep specimens. Creep tests with pure Cu single crystals and with a coarse-grained polycrystalline Cu-1 wt.% Sb alloy at 823 K have been performed and used to calibrate the polycrystal model. The grain structure of the polycrystalline CuSb specimens has been revealed by the EBSD method. Extensive grain boundary sliding and cavitation has been observed in the crept specimens. Grain boundary sliding has been found to promote wedge-type damage at grain boundary triple junctions and to contribute significantly to the total creep strain. Furthermore, the assumed stress sensitivity of the models grain boundary cavity nucleation rate strongly influences the development of wedge-type damage.