Filtern
Dokumenttyp
- Vortrag (4)
- Beitrag zu einem Tagungsband (2)
- Posterpräsentation (2)
- Zeitschriftenartikel (1)
Schlagworte
- Composite (5)
- Pressure vessel (5)
- Hydrogen (4)
- Glass fiber reinforced polymers (2)
- Residual stress (2)
- Residual stresses (2)
- Carbon fiber (1)
- Competence center (1)
- Failure mechanisms (1)
- Filament winding (1)
Organisationseinheit der BAM
- 3 Gefahrgutumschließungen; Energiespeicher (6)
- 3.5 Sicherheit von Gasspeichern (6)
- 5 Werkstofftechnik (3)
- 5.3 Polymere Verbundwerkstoffe (3)
- 2 Prozess- und Anlagensicherheit (1)
- 2.1 Sicherheit von Energieträgern (1)
- 8 Zerstörungsfreie Prüfung (1)
- 8.1 Sensorik, mess- und prüftechnische Verfahren (1)
- 9 Komponentensicherheit (1)
- 9.0 Abteilungsleitung und andere (1)
Eingeladener Vortrag
- nein (4)
Localized patches are a cost- and time-effective method for repairing fiber-reinforced polymer (FRP) sandwich wind turbine rotor blade shells. To increase the understanding of their effect on the fatigue of the blades, this study examines the effect of various layup methods of localized repair patches on the structural integrity of composite sandwich structures. Manufactured with the vacuum-assisted resin infusion (VARI) process, the shell test specimens are produced as a curved structure with glass fiber reinforced polymer (GFRP) sandwiching a polyvinyl chloride (PVC) foam core. Patch repairs are then introduced with varying layup techniques, and material properties are examined with cyclic fatigue tests. The transition region between patch and parent material is studied in greater detail with finite element method (FEM) simulations, with a focus on the effect of fiber orientation mismatch. Damage onset, crack development, and eventual failure are monitored with in-situ non-destructive testing methods to develop a robust understanding of the effects of repair concepts on material stiffness and strength.
A potential repair alternative to restoring the mechanical properties of lightweight fiberreinforced polymer (FRP) structures is to locally patch these areas with scarf joints. The effects of such repair methods on the structural integrity, however, are still largely unknown. In this paper, the mechanical property restoration, failure mechanism, and influence of fiber orientation mismatch between parent and repair materials of 1:50 scarf joints are studied on monolithic glass fiber-reinforced polymer (GFRP) specimens under tensile load. Two different parent orientations of [-45/+45]2S and [0/90]2S are exemplarily examined, and control specimens are taken as a baseline for the tensile strength and stiffness property recovery assessment. Using a layer-wise stress analysis with finite element simulations conducted with ANSYS Composite PrepPost to support the experimental
investigation, the fiber orientation with respect to load direction is shown to affect the critical regions and thereby failure mechanism of the scarf joint specimens.
The publication is an extended abstract on the modelling of the manufacturing process related residual stresses in type 4 pressure vessels for hydrogen storage. A 2D analytical model based on the classical laminate theory and a 3D finite element model are introduced. The calculated residual stress state after the filament winding process as well as the stress state in service are presented and discussed.
Non-Destructive Testing (NDT) of type 4 composite pressure vessels can be seen as key to better understanding the behaviour of the composite structure and the impact of the manufacturing process on its quality. In this presentation, NDT methods used in the “Trustworthy Hydrogen” project are introduced. A brief discussion of the observed phenomena is provided.