Filtern
Dokumenttyp
Sprache
- Englisch (5)
Schlagworte
- Eigenspannungen (3)
- Gas metal arc welding (2)
- Martensitbildung (2)
- Martensite kinetic (2)
- Residual stresses (2)
- Schweißsimulation (2)
- Sensitivity analysis (2)
- Sysweld (2)
- Welding simulation (2)
- AZ31 magnesium alloy (1)
Austenite grain growth during welding is a critical factor for controlling weld microstructure in addition to nominal composition and thermal cycles. Recently, experimental data suggesting a decrease in martensite start temperature with a decrease in prior austenite grain size has been published. However, the actual sensitivity of this phenomenon on residual stresses evolution in the heat-affected zone has not been investigated, yet. Therefore, a numerical model was modified to consider this phenomenon. Numerical simulations were performed for welding of a low-alloy structural steel with minimum yield strength of 355 MPa (S355J2+N) and a heat-resistant steel P91 or 9Cr–1Mo, respectively. The results clarify the influence of prior austenite grain size on the residual stress development and show the importance martensite transformation temperatures and final martensite fraction. Consequently, the residual stress evolution of P91, which completely transforms to martensite while cooling, based on the enhanced model leads to maximum stress differences of 200 MPa in the heat-affected zone.
Continuous cooling transformation (CCT) behavior affects the transient state of
material properties employed in a numerical welding simulation, having a direct influence
on the developing stress state. Three different CCT diagrams for S355J2 steel
were employed to understand the influence of variations in CCT behavior on the numerical
calculation of welding-induced residual stresses. The CCT diagrams were
constructed from transformation data contained in the Sysweld software database,
measured dilatometric data from Gleeble experiments, and transformation data calculated
from the JMatPro software. The calculated transverse and longitudinal residual
stress distributions provided a qualitative correction only in comparison to experimental
measurements, with the largest deviation occurring near the weld
interface. Overall, the results indicate a weak dependency of the calculated residual
stresses due to anticipated CCT variations. The most significant effect on the calculated
residual stresses was shown to be related to the proportion of formed martensite.
It is suggested that CCT data of approximate accuracy is sufficient for reliable
calculation of welding-induced residual stresses.
Resistance spot welds were prepared on 3 mm thick sheets of continuous cast and rolled AZ31 magnesium alloy. The microstructure and composition analysis of weld nugget, heat affected zone (HAZ) and base metal were examined using optical and scanning electron microscopy (HR-SEM and EDS/X). The resistance spot welded magnesium alloy joints consist mainly of weld nugget and HAZ. The nugget contains two different structures, i.e. the cellular-dendritic structure at the edge of the nugget and the equiaxed dendritic structure in the centre of the nugget. The structure transition is attributed to the changes of solidification conditions. In the HAZ, grain boundary melting occurred and grain boundaries became coarse. It has been shown that hardness reduction in the weld nugget and HAZ compared with base metal is evident due to dendritic microstructure and grain growth, respectively. The results showed that spot welded joints have failed in interfacial mode under torsion and tensile–shear loading conditions. Digital image correlation during tensile–shear testing showed that low surface strains occur in the interfacial failure mode, because fracture and deformation happened primarily in the nugget area.