Basic research on the corrosive effect of flue gases has been performed at the BAM Federal Institute for Materials Research and Testing (Germany). Conditions at both high and low temperatures were simulated in specially designed experiments. Carburization occured in flue gases with high CO2 content and temperatures higher than 500 °C. In SO2 containing flue gases sulphur was detected in the oxide scale. At lower temperatures no corrosion was observed when gases with low humidity were investigated. Humidity higher than 1500 ppm was corrosive and all steels with Cr contents lower than 12% revealed corroded surfaces. At low temperatures below 10 °C a mixture of sulphuric and nitric acid condensed on metal surfaces. Acid condensation caused severe corrosion. Humidity, CO2, O2, and SO2 contents are the important factors determining corrosion. Below 300 °C acid condensation is the primary reason for corrosion. Low humidity and low temperatures are conditions which can be expected in the CO2 separation and treatment process. This work includes major conditions of the flue gas and CO2 stream in CCS plants and CCS technology.
Comparative study on high temperature oxidation of T92 steel in dry and wet oxyfuel environments
(2015)
Fireside oxidation of T92 steel was studied after exposure times up to 1000 h in the temperature range of 580–650 °C in simulated dry (CO2–27 % N2–2 % O2–1 % SO2) and wet (CO2–20 % H2O–7 % N2–2 % O2–1 % SO2) oxyfuel environments. Water vapour addition to the oxyfuel gas substantially increased the oxidation rate. The oxide scales developed under wet environment contained more defects, resulting in higher access of oxidants to the substrate material and enhanced oxidation. In addition, the oxide scales had lower chromium enrichment in the inner layer as compared to that in the dry condition. The oxide scales consisted of hematite and magnetite in the outer layer and a mixture of (Fe, Cr)-spinel, sulphides and wustite in the inner layer. The sulphur distribution differed between the oxide scales developed in dry and wet oxyfuel environments. Sulphur was mainly concentrated in the inner layer and at the oxide/alloy interface. In contrast to the wet oxyfuel gas, very high sulphur concentration was measured in the inner oxide scale formed in the dry oxyfuel gas. Additionally, Fe-sulphide was formed at the interface of inner and outer oxide layer in the wet condition.