The CCS technique involves the compression of emission gasses in deep geological layers. To guarantee the safety of the site, CO2-corrosion of the injection pipe steels has to be given special attention when engineering CCS-sites. To get to know the corrosion behaviour samples of the heat treated steel 1.72252CrMo4, used for casing, and the stainless injection-pipe steel 1.4034 X46Cr13 were kept at T=60 °C and ambient pressure as well as p=100 bar for 700 h - 8000 h in a CC 2-saturated synthetic aquifer environment similar to possible geological on-shore CCS-sites in the northern German Basin. The isothermal corrosion behaviour obtained by mass gain of the steels in the gas phase, the liquid phase and the intermediate phase gives surface corrosion rates around 0.1 to 0.8 mm/year at ambient pressure and much lower about 0.02 to 0.2 mm/year at 100 bar where the CO 2 is in its supercritical state. Severe pit corrosion with pit heights around 4.5 mm are only located on the 42CrMo4 steel. Main phase of the continuous complicated multi-layered carbonate/oxide structure is siderite FeCO 3 in both types of steel.
Dealing with first corrosion screening experiments to predict the reliability and safety of Germanys first Carbon Capture and Storage site in the northern Bassin of Germany, northwest of the Capital Berlin, laboratory experiments have been established to simulate the particular conditions at T=60 °C, highly saline aquifer water similar to 'Stuttgart Aquifer', but only at ambient pressure. With mounting 2 independent full 2-grade titanium autoclave systems (running up to 250 bar and 300 °C) pressures up to p=100 bar are possible. In 2010 a specific corrosion chamber of 2-grade titanium working up to 100 °C, flowing aqui fer water with different gas mixtures was designed to fit to a high cycle fatigue testing machine. Long term fatigue experiments simulating fatigue crack growth under corrosive environments will soon start. These experiments may not only help engineering a CCS site, but results can be used to improve the maintenance of geothermal energy production sites, especially moved parts such as pumps and shafts.
The CCS technique involves the compression of emission gasses in deep geological layers. To guarantee the safety of the site, C02-corrosion of the injection pipe steels has to be given special attention when engineering CCSsites. To get to know the corrosion behaviour samples of the heat treated Steel 1.72252CrMo4, used for casing, and the stainless injection-pipe Steel 1.4034 X46Cr 13 were kept at T=60 °C and ambient pressure as well as p=100 bar for 700 h - 8000 h in a C02-saturated synthetic aquifer environment similar to possible geological on-shore CCS-sites in the northern German Basin. The isothermal corrosion behaviour obtained by mass gain of the steels in the gas phase, the liquid phase and the intermediate phase gives surface corrosion rates around 0.1 to 0.8 mm/year at ambient pressure and much lower about 0.02 to 0.2 mm/year at 100 bar where the C02 is in its supercritical state. Severe pit corrosion with pit heights around 4.5 mm are only located on the 42CrMo4 Steel. Main phase of the continuous complicated multi-layered carbonate/oxide structure is siderite FeCO} in both types of Steel.
The CCS technique involves the compression of emission gasses in deep geological layers. To guarantee the safety of the site, CC>2-corrosion of the injection pipe steels has to be given special attention when engineering CCS-sites. To get to know the corrosion behaviour samples of the heat treated Steel 1.72252CrMo4, used for casing, and the stainless injection-pipe Steel 1.4034 X46Crl3 were kept at T=60 °C and ambient pressure as well as p=100 bar for 700 h - 8000 h in a CC>2-saturated synthetic aquifer environment similar to possible geological onshore CCS-sites in the northern German Basin. The isothermal corrosion behaviour obtained by mass gain of the steels in the gas phase, the liquid phase and the intermediate phase gives surface corrosion rates around 0.1 to 0.8 mm/year at ambient pressure and much lower about 0.02 to 0.2 mm/year at 100 bar where the CO2 is in its supercritical state. Severe pit corrosion with pit heights around 4.5 mm are only located on the 42CrMo4 Steel. Main phase of the continuous complicated multi-layered carbonate/oxide structure is siderite FeCCh in both types of Steel.
When engineering a Carbon Capture and Storage site (CCS) local corrosion (pitting) of the injection pipe steel may become an issue when emission gasses from oxyfuel power plants are compressed into deep geological layers. This highly corrosive environment arises when the flue gasses, mainly composed of CO2 , are injected into saline aquifer water. Immediately carbonic acid is formed causing corrosive attack of the injection steels. The influence of heat treatment on the local corrosion resistance was demonstrated in laboratory experiments at 60 °C and ambient pressure for three steels X46Cr13 (1.4034), X20Cr13 (1.4021) and X5CrNiCuNb16-4 (1.4543) under a similar liquid corrosive environment as found at a geological onshore CCS-site in the Northern German Bassin.
Oxidation of a single crystal nickel-base superalloy at 950 °C - a kinetic and microstructure study
(2008)
The nickel-base single crystal alloy investigated is a widely used material for first and second row blades in stationary gas turbines. Nickel-base superalloys are especially designed to resist high temperature oxidation by process gases. To determine this high temperature behaviour oxidation testing was carried out using samples cut perpendicular to (001)-direction. Microstructures were characterized by X-ray diffraction XRD, Light Microscopy LM, Scanning Electron Microscopy SEM, and X-ray energy dispersive spectroscopy (EDS), after a series of heat treatments (950 °C, 0 h - 1000 h). Mass gain and the respective thicknesses of the different oxide layers were measured to determine oxidation kinetics. In general, the isothermal oxidation behaviour at 950 °C, as defined by weight gain, follows a parabolic law with a parabolic rate constant around 1.4 · 10-2 mg2/(cm4 · h). A short incubation time is followed by the constitution of a multi-layered oxide scale. The oxide scale consists of a three layer structure. An outer scale contains a Ti-bearing thin film associated as TiO2 and NiTiO3 but mostly Cr attributed to Cr2O3, (Ni/Co)Cr2O4 beside NiTaO4. This outer scale is connected to a discontinuous layer of inner oxidation consisting mainly of Al2O3, which is followed by an area of γ´-depletion within the base material.
The resistance of structural steels against corrosion in CO2-H2O and CO2-H2O-O2
atmospheres at temperatures above 550°C was observed with high magnification methods.
The test atmosphere is the basic composition of an oxyfuel coal combustion atmosphere. The
analytical information base was applied to develop reaction schemes for the oxidation of
steels. It was demonstrated that the formation of phases and the kinetics of oxidation reactions
in this atmospheres is affected by the formation of intermediate iron hydroxide and a high
carbon activity. In the temperature regime above 550°C the thermal equilibrium between H2O,
CO2 and Fe reacted and formed CO. CO triggers the formation of FeO and carbides and
increases the reaction kinetics. Porosity at the interface is established by gaseous phases
such as Fe(OH)2 or H2O. H2 formation is not limited to the steel - oxide interface but can occur
in the whole oxide scale. Examples of the experimental results were compared with a
thermodynamic approach. The objective of the work was to derive qualitative rules of the basic
corrosion reactions.
The most efficient construction materials for boiler water walls and superheaters in
steam power plants are ferritic and martensitic steels. In practical operation tubes are
simultaneously exposed to combustion gas and air/steam on their opposite surfaces. The
corrosion behaviour of ferritic-martensitic steels under such dual atmospheres is nondistinctive
and has therefore been investigated in a special designed test equipment between 500 and
620°C. The power plant conditions were simulated wi th a flowing and pressurised (80 bar)
combustion gas on the inner side of the tube which mainly consists of H2O and/or CO2. On the
outer side, the tube material was exposed to air. It was discovered that under similar
temperatures the oxides formed on the air side under dual atmosphere conditions were
significantly different to the oxide scales formed when the alloy was exposed to air only. It is
assumed that the anomalous corrosion behaviour during the dual atmosphere exposure is due
to the hydrogen transport through the bulk alloy from the combustion gas side to the air side.
Immersion tests of potential injection pipe steels 42CrMo4, X20Cr13, X46Cr13, X35CrMo4 and X5CrNiCuNb16-4 at T=60 °C and ambient pressure and p=100 bar were performed for 700 h - 8000 h in a CO₂-saturated synthetic aquifer environment similar to CCS-sites in the Northern-German-Basin. Main corrosion products are FeCO₃ and FeOOH. Highest surface corrosion rates at ambient pressure are 0.8 mm/year for 42CrMo4 and lowest 0.01 mm/year for X5CrNiCuNb16-4. Corrosion rates at 100 bar (max. 0.01 mm/year for 42CrMo4, X20Cr13, X46Cr13) are generally lower than at ambient pressure (<0.01 mm/year for X35CrMo4, X5CrNiCuNb16-4). Heat treatment to martensitic microstructure offers good corrosion resistance.