- Corrosion (44)
- CCS (41)
- Steel (35)
- CO2-storage (18)
- Pipeline (17)
- High temperature corrosion (12)
- CO2-injection (9)
- Heat treatment (8)
- Supercritical CO2 (7)
- Aquifer (6)
Organisationseinheit der BAM
Eingeladener Vortrag (wissenschaftliche Konferenzen)
- nein (6)
In coal-fired power plants using oxyfuel combustion process with carbon capture and sequestration, instead of air, a mixture of oxygen and recirculated flue gas is injected in the boiler. A series of steels were exposed to CO2-SO2-Ar-H2O gas mixtures at 600 °C for 1000 h to compare their high temperature corrosion behavior. During the corrosion process, carburization, decarburization and recrystallization were observed underneath the oxide scale depending on the gas mixture and alloy composition. The conditions that lead to carburization are not yet completely understood, but decarburization can be simulated using thermodynamic and kinetic models. In this work, the results of these simulations are compared with measured values for one of the alloys that displayed a decarburized region. Since the mobility of carbon in the scale is not known, two strategies were adopted: simulation of alloy-atmosphere contact; and estimation of the carbon flux to produce the observed decarburization. The second approach might give an insight on how permeable to carbon the scale is.
In CCS environment (carbon capture and storage) pipes are loaded statically and/or cyclically and at the same time exposed constantly to the highly corrosive hot thermal water. Experimental procedures such as ambient pressure immersions tests, in-situ corrosion fatigue experiments using a flexibly designed corrosion chamber at ambient pressure and a specially designed corrosion chamber at high pressure. Experimental set-ups for push/pull and rotation bending load are introduced. The corrosion behavior and lifetime reduction of high alloyed steels (X46Cr13, 1.4043), (X5CrNiCuNb16-4, 1.4542) and (X2CrNiMoN22-5-3, 1.4462) is demonstrated (T=60 °C, geothermal brine: Stuttgart Aquifer flow rate: 9 l/h, CO2 ).
The Ni-Cr-Mo-W alloy is characterized by the excellent high-temperature corrosion resistance, good strength and ability to work in aggressive environments. To protect the surface of the substrate 13CrMo4-5 steel against aggressive environments the Inconel 686 as clad layer was used. The corrosion process was performed in oxidizing mixture of gases like O2, COx, SOx. The second part of corrosion Experiment concerned the corrosion test of the coating in reducing atmosphere of the specified gases with ashes, which contained e.g. Na, Cl, Ca, Si, C, Fe, Al.
The most efficient construction materials for boiler water walls and superheaters in steam power plants are ferritic and martensitic steels. In practical operation, tubes are exposed simultaneously to combustion gas and air/steam on their opposite surfaces. The corrosion behavior of ferritic-martensitic steels under such dual atmospheres is nondistinctive and has been investigated in a specially designed test equipment between 500°C and 620°C. The power plant conditions were simulated with a flowing and pressurized (80 bar) combustion gas on the inner side of the tube, which contains water (H2O) and carbon dioxide (CO2). On the outer side, tube material was exposed to air. Oxides that formed on the air side under dual atmosphere conditions were significantly different from the oxide scales formed when the alloy was exposed to air only. It is assumed that the anomalous corrosion behavior during the dual atmosphere exposure is due to hydrogen and carbon diffusion through the bulk alloy from the combustion gas side to the air side. Both species are produced when the material reacts with the gas phase. Because of its high diffusivity, hydrogen is thought to affect the corrosion process on the air side from the beginning of the corrosion exposure, whereas carbon reaches the opposite side after a considerably longer time period.
During carbon capture and storage (CCS) CO2-corrosion of pipe steels is a relevant safety issue when emission gasses are compressed in deep geological layers. The reliability of the steels 42CrMo4, X20Cr13, X46Cr13 and X35CrMo17 is demonstrated in long term laboratory experiments up to 2 years of exposure time. Testings were carried out at ambient pressure under an equivalent corrosive environment as found at the geological onshore CCS-site at Ketzin, Germany (T=60 °C, aquifer water).
In future power plant technologies, oxyfuel, steels are subjected to steam rich and carbon dioxide rich combustion gases. The effect of simulated combustion gases H2O/CO2/O2 (30/69/1 mol%) and H2O/CO2 (30/70 mol%) on the corrosion behavior of low alloyed steels, 9-12% chromium steels and an austenitic steel were studied. It was discovered that the formation of protective chromium rich oxides is hampered due to the carburization of the base material and the formation of chromium rich carbides. The kinetics of corrosion and carburization are quantified. The effect of temperature and the effect of gas pressure are analyzed statistically.
Nachdem im Verbundprojekt COORAL das Hauptaugenmerk auf überkritisches CO2 gelegt wurde, d. h. Transport über kurze Strecken bei erhöhter Temperatur, wurde in CLUSTER ein größeres lokales Transport-Netzwerk betrachtet, bei dem CO2 bei geringeren Temperaturen, also vorwiegend im flüssigen Zustand transportiert wird. Wurden in COORAL die CO2-Ströme von Kohlekraftwerken untersucht, ging es in CLUSTER zusätzlich um die Emissionen von relevanten Industrien, deren CO2-Emissionen nicht ohne Weiteres vermieden werden können.
Aufgrund der Erfahrungen in COORAL konnte eine Auswahl von kommerziellen Werkstoffen getroffen werden, die für einen konkreten Einsatz für CCS zur Verfügung stünden. Die gemischten und fluktuierenden CO2-Zusammensetzungen sind bei geeigneten Begrenzungen der Begleit¬stoffe im CO2 bezüglich Korrosionsvorgänge beherrschbar. Die Machbarkeit eines lokalen CCS-Clusters erscheint daher gegeben, soweit dies die Anlagen für Kompression, Transport und Injektion betrifft.
The geological storage of carbon dioxide (Carbon Capture and Storage, CCS) in depleted gas reservoirs or in saline aquifers is a widely discussed issue. Carbon dioxide may induce corrosion on the piping steels during compression, transportation and injection. Therefore,
selection of appropriate piping steels is a key factor in order to increase the safety and reliability of the CCS technology, and to keep the processes cost-effective.
The here described subproject of the COORAL project (German acronym for “C02 purity for capture and storage”) deals with the levels of impurities in the C02 stream that will be acceptable when using specific steels. Material exposure to carbon dioxide (C02) containing
specific amounts of water vapor, oxygen (02) sulfur dioxide (S02), nitrogen dioxide (N02), carbon monoxide (CO) can be a challenge to steels. Within this subproject 13 different Steels are tested for suitability as materials used for compression, transportation and injection Units within the CCS chain.
Coupons of X5CrNiCuNb16-4 that may be used as injection pipe with 16% Chromium and 0.05% Carbon (1.4542, AISI 630) were exposed for 3000 h to CO2-saturated saline aquifer water similar to the conditions in the Northern German Basin at ambient pressure and 60 °C. Surface corrosion layers and pits reveal carbonate corrosion products on the surface such as FeCO3 and FeOOH as the main precipitation phases with no dependence on the original surface roughness. Corrosion rates for polished and technical surfaces were below 0.005 mm/year compared to corrosion rates of 0.035 mm/year after shot peening.
The appropriate strength of steels used for saline aquifer carbon capture and storage sites (CCS) is usually achieved by applying heat treatments. Thus, heat treatment influences the corrosion resistance for injection pipe steels with 13% chromium and different carbon content: 1.4034/X46Cr13 and 1.4021/X20Cr13 in CO2 saturated saline aquifer water at 60 °C, 1 and 100 bar. X46Cr13 shows better corrosion resistance with respect to corrosion rate, number of pits and maximum intrusion depth. Low corrosion rates are obtained for steels with martensitic microstructures exposed to supercritical CO2 at 100 bar, whereas normalized steels show better corrosion resistance at ambient pressure.