Filtern
Dokumenttyp
- Zeitschriftenartikel (20)
- Vortrag (12)
- Buchkapitel (1)
- Posterpräsentation (1)
Schlagworte
- Transmission electron microscopy (11)
- High entropy alloy (9)
- High entropy alloys (9)
- Corrosion (6)
- X-ray diffraction (5)
- Compositionally complex alloys (4)
- Creep (4)
- EXAFS (4)
- Scanning electron microscopy (4)
- Lattice misfit (3)
Organisationseinheit der BAM
- 5 Werkstofftechnik (34)
- 5.1 Mikrostruktur Design und Degradation (31)
- 6 Materialchemie (8)
- 6.3 Strukturanalytik (5)
- 5.2 Metallische Hochtemperaturwerkstoffe (4)
- 5.5 Materialmodellierung (4)
- 5.0 Abteilungsleitung und andere (3)
- 6.2 Material- und Oberflächentechnologien (3)
- 9 Komponentensicherheit (3)
- 9.0 Abteilungsleitung und andere (3)
Paper des Monats
- ja (2)
Eingeladener Vortrag
- nein (12)
While a lage amount of research on high entropy alloys is oriented towards mechanical properties and the microstructural improvement it is also necessary to keep an eye on the environment that potential application materials will be submitted to. The Co-Cr-Fe-Ni based high entropy family has shown great potential over the years of high entropy research and some candidate alloys are chosen for an insight into their corrosion behaviour. Several atmospheres are studied, i.e. O2, H2O, SO2 and a mix thereof in argon as well as synthetic air. Just as for classic alloys, the chromium is the most important element in terms of protection agains further corrosion. The addition of manganese, as in case of the “Cantor alloy” CrMnFeCoNi, overpasses Cr when it comes to oxygen affinity and thus counteracts the layer formation of Cr2O3. Even without Mn, a temperature chosen too high will also affect the formation of the chromium oxide layer and spall it off, annulling its protective potential. We can also observe how trace elements influence the layer formation. These effects and their mechanisms will be discussed for the alloys CrFeNi, CoCrNi, CrMnFeCoNi and variations of Al10Co25Cr8Fe15Ni36Ti6 using a combination of electron microscopy, thermodynamic calculations and x-ray diffraction.
Spurenelemente spielen eine wichtige Rolle bei der Verfeinerung der Eigenschaften von komplexen Materialien. Diese Arbeit zeigt die Korrelation zwischen der Mikrostruktur, der Gitterfehlpassung und den Kriecheigenschaften. Die Legierung Al10Co25Cr8Fe15Ni36Ti6 (in at. %) mit komplexer Zusammensetzung wurde mit den Elementen Hf und W verstärkt. Die Zugabe von Hf bewirkt eine eckigere Form der würfelförmigen gamma'-Ausscheidungen und einen erhöhten Anteil der Heusler-Phase. Die Zugabe von W wiederum formt die Würfelchen rundlicher und löst die Heusler-Phase auf. Eine Mischung der beiden Spurenelemente zeigt einen Übergang zwischen den beiden Extremen, sowohl in Hinsicht auf die Form der Ausscheidungen als auch in Bezug auf die Gitterfehlpassung und die Kriecheigenschaften.
The current lack of quantitative knowledge on processing-microstructure–property relationships is one of the major bottlenecks in today’s rapidly expanding field of additive manufacturing. This is centrally rooted in the nature of the processing, leading to complex microstructural features. Experimentally-guided modeling can offer reliable solutions for the safe application of additively manufactured materials. In this work, we combine a set of systematic experiments and modeling to address creep anisotropy and its correlation with microstructural characteristics in laser-based powder bed fusion (PBF-LB/M) additively manufactured Inconel-738LC (IN738LC). Three sample orientations (with the tensile axis parallel, perpendicular, and 45° tilted, relative to the building direction) are crept at 850 °C, accompanied by electron backscatter secondary diffraction (EBSD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) investigations. A crystal plasticity (CP) model for Ni-base superalloys, capable of modeling different types of slip systems, is developed and combined with various polycrystalline representative volume elements (RVEs) built on the experimental measurements. Besides our experiments, we verify our modeling framework on electron beam powder bed fusion (PBF-EB/M) additively manufactured Inconel-738LC. The results of our simulations show that while the crystallographic texture alone cannot explain the observed creep anisotropy, the superlattice extrinsic stacking faults (SESF) and related microtwinning slip systems play major roles as active deformation mechanisms. We confirm this using TEM investigations, revealing evidence of SESFs in crept specimens. We also show that the elongated grain morphology can result in higher creep rates, especially in the specimens with a tilted tensile axis.
High‐temperature KCl‐induced corrosion of high Cr and Ni alloys investigated by in‐situ diffraction
(2024)
High‐temperature KCl‐induced corrosion in laboratory air was observed in situ utilizing X‐ray diffraction. High Cr‐containing model alloys (Fe‐13Cr, Fe‐18Cr‐12Ni, and Fe‐25Cr‐20Ni) were coated with KCl and exposed to dry air at 560°C. KCl‐free alloys were studied in the equivalent atmosphere as a reference. After exposure to KCl‐free environments, all alloys showed the formation of very thin oxide layers, indicating good corrosion resistance. In contrast, KCl‐bearing alloys showed distinct damage after exposure.