Discoloration Effects of High-Dose gamma-Irradiation and Long-Term Thermal Aging of (U) HMW-PE
(2017)
Two polyethylene types with ultra-high (UHMWPE) and high molecular weight (HMW-PE) used as neutron radiation shielding materials in casks for radioactive waste were irradiated with doses up to 600 kGy using a 60Co gammasource. Subsequently, thermal aging at 125∘C was applied for up to one year. Degradation effects in the materials were characterized using colorimetry, UV-Visspectroscopy, IR spectroscopy, and DSC. Both materials exhibited a yellowing upon irradiation.The discoloration of UHMW-PE disappeared again after thermal aging.Therefore, the yellowing is assumed to originate fromannealable color centers in the formof free radicals that are trapped in the crystalline regions of the polymer and recombine at elevated temperatures. For the antioxidantcontaining HMWPE, yellowing was observed after both irradiation and thermal aging. The color change was correlated mainly to decomposition products of the antioxidant in addition to trapped radicals as in UHMW-PE. Additionally, black spots appeared after thermal aging of HMW-PE.
Due to delays in the siting procedure to establish a deep geological repository for spent nuclear fuel and high level radioactive waste as well as in construction of the already licensed Konrad repository for low and intermediate level radioactive waste, extended periods of interim storage become more relevant in Germany. BAM is involved in most of the cask licensing procedures and especially responsible for the evaluation of cask-related long-term safety issues.
The long-term performance of elastomer seals for lid systems of transport and storage casks, whether used as auxiliary seals in spent fuel casks or as primary seals for low and intermediate level waste packages, is an important issue in this context. The polymeric structure of these seals causes a complex mechanical behavior with time-dependent sealing force reduction.
The results of a comprehensive purpose-designed test program consisting of basic compression and tension tests as well as relaxation tests on unaged specimens of representative types of elastomers (fluorocarbon rubber (FKM) and ethylene propylene diene rubber (EPDM)) at different temperatures and strain rates are presented. They were used to identify the constitutive behavior and to obtain parameters for finite element material models provided by the computer code ABAQUS®. After estimating the influence of uncertainties such as Poisson’s ratio and friction coefficient by sensitivity analyses, the chosen parameters had to prove their suitability for the finite element simulation of the specimen tests themselves.
Based on this preliminary work the simulation of a specific laboratory test configuration containing a typical elastomer seal with circular cross section is presented. The chosen finite element material model and the implemented parameters had to show that they are able to represent not only the specimen behavior under predominantly uniaxial load but also the more complex stress states in real components. Deviations between the measured and calculated results are pointed out and discussed.
For the consideration of long-term effects in the simulation of elastomer behavior, test results of aged specimens are needed. First information about a new test program, started recently and planned to provide these data, are given.
Characterisation of degradation and determination of end-of-lifetime criterion for O-ring seals
(2017)
The ageing of polymers, including elastomers, is an undesirable but inevitable process leading to a limited lifetime of rubber products such as seals. Independent of the application, as e.g. in automotive, piping or container applications, a long lifetime or at least a timely exchange of a seal before occurrence of critical failure is desired.
In order to investigate the degradation of material properties and to determine the lifetime of elastomers used as seals, an ageing programme was started with hydrogenated acrylonitrile butadiene rubber (HNBR), ethylene propylene diene rubber (EPDM) and fluorocarbon rubber (FKM) [1-3]. Both O-ring seals (uncompressed and compressed by 25 %) with a cord diameter of 10 mm as well as sheets with a thickness of 2 mm were aged at 75 °C, 100 °C, 125 °C and 150 °C for up to two years. The changes of material properties during ageing were characterised for each material using samples from the sheets by means of e.g. Dynamic Mechanical Analysis and tensile tests, while sealing properties such as leakage rate were determined on O-rings. The experimental results indicate that while material properties show considerable degradation effects, the static leakage rate stays constant or even decreases before failure occurs quite suddenly at advanced degradation levels. This reveals that static leakage rate has only limited sensitivity for the degradation of the seal material.
Our approach to determine a suitable end of lifetime criterion, which involves a partial decompression of the seal during the leakage test, is presented and discussed.
Elastomer seals are widely used as barrier seals in containers for low and intermediate level radioactive waste and in some countries for spent fuel transportation casks. Depending on the area of use, the rubber materials have to demonstrate proper sealing performance with regard to mechanical, thermal and environmental conditions as well as irradiation during the entire operation period.
In Germany the low and intermediate level radioactive waste is planned to be disposed in the Konrad repository in standardized containers. Many of these containers use an elastomer seal between lid and container body. Depending on the radiactive inventory and a possible containment of the waste in inner barrels and/or concrete structures, such containers may require a specific leak tightness. In such cases, specified leakage rates are shall not be exceeded by the the seals to keep potential activity releases from the inventories well below defined limits.
Generally, all waste containers have to fulfill the waste acceptance criteria for the Konrad repository as defined by the reports BfS SE-IB-29/08 and SE-IB-30/08. From these criteria several requirements for seal performance are derived. The seals have to:
- ensure full functionality until final container disposal,
- maintain its function in case of a thermal or mechanical accident,
- ensure encapsulation also at -20 °C.
This combination of requirements is challenging especially as a seal exchange, which is typical for many other applications, is hardly possible and thus a sound understanding of how to perform safety evaluation of containers is required. Therefore BAM has initiated investigations on elastomer seal behaviour. This work focuses on low temperature behaviour and sealing performance concerning static conditions as well as partial loss of compression and ageing of elastomer seals. Concerning ageing, property changes caused by long-term thermooxidative conditions as well as gamma irradiation are investigated.
This contribution presents an overview and explanation of the aims of the ongoing research and gives an update of the most relevant results.
Für Anwendungen, bei denen Elastomerdichtungen ihre Dichtheit über sehr lange Zeiträume (z. B. Jahrzehnte) behalten müssen, ohne dass ein Austausch praktikabel wäre, ist es nötig, die Lebensdauer solcher Dichtungen zuverlässig bestimmen zu können. Aus diesem Grund wurden Alterungsversuche an O-Ring-Dichtungen sowie Flachproben auf Basis von hydriertem Acrylnitril-Butadien-Kautschuk (HNBR), Ethylen-Propylen-Dien-Kautschuk (EPDM) und Fluorkautschuk (FKM) über bis zu zwei Jahre bei mehreren Temperaturen durchgeführt. Zur Untersuchung der auftretenden Eigenschaftsveränderungen wurden u. a. Härtemessungen, Zugversuche, dynamisch-mechanische und thermogravimetrische Analysen durchgeführt. Zur Beurteilung des Relaxations- und Rückstellverhaltens der alternden Dichtungen wurden außerdem Druckspannungsrelaxations- und Druckverformungsrestmessungen durchgeführt. Darüber hinaus wurde die Leckagerate gemessen, um ein Versagen der Dichtung zu detektieren. Durch die Untersuchung der gealterten Proben wurden sowohl die auftretenden Eigenschaftsveränderungen charakterisiert wie auch die damit zusammenhängenden Alterungsmechanismen diskutiert. Anhand der großen Datenmenge aus Ergebnissen von verschiedenen Untersuchungsmethoden, die für mehrere Alterungszeiten und -temperaturen durchgeführt wurden, sollte zusätzlich die günstigste Vorgehensweise für Lebensdauervorhersagen ermittelt werden. Dies beinhaltete auch die Bestimmung eines Lebensdauerkriteriums, das mit dem Auftreten von Leckage und damit dem Versagen der Dichtung zusammenhängt. Hinsichtlich der Eigenschaftsänderungen und Alterungsmechanismen wurde beim HNBR eine starke Versprödung aufgrund dominanter Vernetzungsreaktionen während der Alterung festgestellt. Diese resultierten auch darin, dass die Sauerstoffpermeabilität abnahm, so dass der Sauerstofftransport ins Innere der Probe (hauptsächlich bei den dickeren O-Ringen) behindert wurde. Dies führte dazu, dass diffusionsbegrenzte Oxidationseffekte (DLO-Effekte) auftraten, d. h. dass das Probeninnere weniger stark alterte als oberflächennahe Bereiche. Während der Alterung von EPDM traten sowohl Kettenspaltungen wie auch Vernetzungsreaktionen auf, was sich vor allem in einer Verschlechterung der Zugeigenschaften und einer Abnahme der Druckkraft sowie in einem steigenden Druckverformungsrest äußerte. Bei sehr stark gealterten Proben dominierten ebenfalls Vernetzungsreaktionen, was sich auch in deutlichen DLO-Effekten äußerte. Aufgrund seiner ausgeprägten Oxidations- und Hochtemperaturbeständigkeit wies FKM vergleichsweise geringe Degradationserscheinungen auf. Nur mit Druckspannungsrelaxation und Druckverformungsrest waren nennenswerte Änderungen ersichtlich. Messungen der statischen Leckagerate ergaben, dass die O-Ringe erst bei sehr weit fortgeschrittener Degradation undicht wurden und bis zu diesem Zeitpunkt kein allmählicher Anstieg der Leckagerate beobachtet werden konnte. Aus diesem Grund wurden Leckagemessungen mit einem modifizierten Versuchsaufbau durchgeführt, bei dem die Dichtung während der Messung leicht entlastet wird. Da dieser Test eine dynamische Rückstellung der Dichtung erfordert und damit höhere Ansprüche an die Dichtung stellt, wurde am geprüften EPDM-O-Ring ein früheres Versagen beobachtet. Der entsprechende Alterungszeitpunkt wurde als Versagenszeitpunkt definiert. Dieser wurde anhand der Daten verschiedener Messmethoden mit dem Degradationszustand korreliert und entspricht beispielsweise einem Druckverformungsrest von 80 %. Auf der Grundlage dieses Kriteriums konnten Lebensdauern mittels Zeit-Temperatur-Verschiebung bestimmt werden. Im Rahmen dieser Arbeit wurden zahlreiche Erkenntnisse darüber gewonnen, worauf bei beschleunigten Alterungsversuchen und Lebensdauerprognosen von O-Ringen zu achten ist und welche Fehlerquellen vermieden werden sollten. Dies wird zusammen mit Empfehlungen für eine bestmögliche Versuchsdurchführung ausführlich diskutiert.
At BAM, which is the federal institute for materials research and testing in Germany, it is one of our tasks to evaluate the safety of casks designed for transport and/or storage of radioactive material. This includes the assessment of the service lifetime of elastomeric seals that are part of the container lid system with regard to the requirements for long-term safety (40 years and more) of the containers. Therefore, we started an accelerated ageing programme with selected rubbers often used for seals (HNBR, EPDM and FKM) which are aged at four different temperatures (75 °C, 100 °C, 125 °C and 150 °C) up to 1.5 years. In order to assess sealability, O-rings are aged in compression by 25 % (corresponding to the compression during service) between plates as well as in flanges that allow leakage rate measurements. For comparison, uncompressed O-rings are aged as well. Further methods characterising seal performance are compression stress relaxation (CSR) reflecting the loss of sealing force of a compressed seal over time, and compression set (CS) which represents the recovery behaviour of a seal after release from compression. Additionally, hardness is measured for information about the change of mechanical properties. The experimental results indicate that while hardness, CSR and CS show considerable degradation effects, the leakage rate stays relatively constant or even decreases until shrinkage combined with the loss of resilience of the aged seal leads to leakage. This demonstrates that static leakage rate, which is the only available direct seal performance criterion, has only limited sensitivity towards the degradation of the seal material. CS data is extrapolated using time-temperature shifts and Arrhenius graphs. An exemplary CS of 50 % would be reached after approx. 1.2, 17 and 29 years at 60 °C for HNBR, EPDM and FKM respectively.
Due to their simple and reliable application, elastomers are used for many tasks. Many fields of application like transport, aviation and process technology, entail low temperatures where proper functionality of the employed seals has to be ensured. Therefore, understanding the low temperature behavior of elastomeric seals is important for safe seal operation to restrict the temperature application range.
For all areas of application, the question of seal lifetime is also important for replacement or maintenance intervals. The lifetime is especially important in applications that allow no seal replacement. Since the seal can determine the lifetime of storage in such cases, reliable lifetime estimation is necessary for these applications, and requires an extensive knowledge of the specific aging behavior.