A three-dimensional turbulent steady state numerical model was used to investigate the influence of an alternating current (AC) magnetic field during high power laser beam keyhole welding of 20 mm thick stainless steel AISI 304 being modeled as an ideal non-ferromagnetic material. Three-dimensional heat transfer and fluid dynamics as well as the electromagnetic field equations were solved with the finite element package COMSOL Multiphysics 4.2 taking into account the most important physical effects of the process. Namely, the thermo-capillary (Marangoni) convection at the weld pool boundaries, natural convection due to gravity and density differences in the melt volume as well as latent heat of solidliquid phase transitions at the phase boundaries were included in the model.
It is shown that the gravity drop-out associated with the welding of thick plates due to the hydrostatic pressure can be prevented by the application of AC magnetic field between 80 mT and 135 mT for corresponding oscillation frequencies between 1 kHz and 10 kHz below the weld specimen. Experimentally, a value of the magnetic flux density of around 230 mT was found to be necessary to allow for single-pass laser beam welding without sagging or drop-out of melt for a 20 mm thick combination of austenitic stainless steel AISI 304 and ferritic construction steel S235JRC at an oscillation frequency of around 2.6 kHz.
The ever larger requirements of the material selection in the range of maritime industry necessitate the application of high-tech materials. Titanium because of its excellent mechanical properties at low weight is an attractive alternative for the construction of ships. The goal of this investigation was to design a welding method for joining samples of 16 mm thick Ti3Al2.5 V. The welding experiments with a 20 kW Yb-fiber laser source and varying combinations of parameters were intended to qualify the laser beam welding process. The welding results were analyzed by non-destructive and destructive testing. In addition, the welding tests were recorded with two high-speed cameras to observe the weld pool and the vapor plume. The evaluation of the high-speed images in correlation with the results of non-destructive testing shows, that a significant improvement of process stability and weld quality can be achieved by the suppression of the vapor plume.
The objective of this study was to investigate the influence of externally applied magnetic fields on the weld quality in laser beam welding. The optimization of the process parameters was performed using the results of computer simulations. Welding tests were performed with up to 20 kW laser beam power. It was shown that the AC magnet with 3 kW power supply allows for a prevention of the gravity drop-out for full penetration welding of 20 mm thick stainless steel plates. For partial penetration welding it was shown that an0.5 T DC magnetic field is enough for a suppression of convective flows in the weld pool. Partial penetration welding tests with 4 kW beam power showed that the application of AC magnetic fields can reduce weld porosity by a factor of 10 compared to the reference joints. The weld surface roughness was improved by 50%.