Nanocomposites were prepared by solution blending of polyhedral oligomeric silsesquioxane with phenethyl substituents (PhenethylPOSS) into polystyrene (PS). The prepared materials were investigated by dielectric spectroscopy, differential scanning calorimetry (DSC), and density measurements. Additional FTIR investigations were carried out. Pure polystyrene shows two relaxation processes, an intermediate β*-process at lower and the α-relaxation at higher temperatures, the latter corresponding to segmental dynamics (dynamic glass transition). The molecular assignment of the β*-process needs further investigation. PhenethylPOSS can be incorporated into PS up to about 40 wt % without any indication of phase separation. With increasing PhenethylPOSS content, the α-relaxation of the composites shifts to lower temperatures and the loss peak broadens. Thus, the main effect of the nanofiller in the polystyrene matrix is to enhance the segmental dynamics, i.e., plasticization. The incorporation of approximately 40 wt % (approximately 5 mol %) PhenethylPOSS shifts the glass transition temperature Tg by 50 K to lower temperatures. The obtained results for polystyrene are discussed together with those reported recently for polycarbonate where a phase-separated morphology is observed for higher concentrations of PhenethylPOSS. The different behavior of PhenethylPOSS in polystyrene and polycarbonate is interpreted in terms of the different interaction of the phenyl rings within the POSS substituents with the phenyl rings of the polymers. For polystyrene, the interaction is stronger than for polycarbonate which probably leads to the enhanced miscibility of PhenethylPOSS into polystyrene. A detailed analysis of the temperature dependence of the dielectric relaxation strengths points also to additional interactions in the nanocomposites when compared to pure polystyrene. The broadening of the loss peak with increasing concentration is discussed in the framework of composition fluctuations.
Nanocomposites were prepared by solution blending of polyhedral oligomeric silsesquioxane with phenethyl substituents (PhenethylPOSS) into poly(bisphenol A carbonate) (PBAC). The nanocomposites were investigated by dielectric spectroscopy, differential scanning calorimetry (DSC) and density measurements. PhenethylPOSS shows one relaxation process, the α-relaxation, confirmed by DSC investigations. PBAC shows a β-relaxation at lower and an α-relaxation at higher temperatures. With increasing PhenethylPOSS content the α-relaxation of the composites shifts to lower temperatures. Thus, incorporation of PhenethylPOSS leads to a plasticization of PBAC due to a decrease of the packing density which is rationalized by density measurements. For higher concentrations of PhenethylPOSS (>10 wt %) the α-relaxation of the polycarbonate matrix splits into two peaks. Moreover, close to the α-relaxation of PhenethylPOSS a third process is observed. These results indicate a phase separation into a PBAC matrix with a few percents of molecularly solved POSS and POSS-rich domains. These POSS-rich domains are surrounded by an interfacial layer of PBAC having a higher concentration of POSS than the matrix. A phase diagram is deduced providing a miscibility criterion. For the phase separated nanocomposites an interfacial polarization phenomena is observed. Using a simplified model the time constant of this process is correlated with the size of the PhenethylPOSS-rich domains and theire increasing size with the increase of the concentration of POSS.
According to basic phenomenological models describing the solution-diffusion based mechanism of penetrant diffusion in dense polymers, a connection between the diffusive transport of gas molecules in a polymeric matrix and the molecular mobility of that matrix on a certain length scale is, in principle, established for a long time. However, experimental data directly showing this correlation are rare. The investigation of a series of nanocomposites based on a polyhedral oligomeric silsesquioxane (POSS) and a polycarbonate matrix allows a systematic change of the molecular mobility on a local length scale (β-relaxation) and of the corresponding activation energy EA, both determined by broadband dielectric spectroscopy. Independently, activation energies of penetrant diffusion (ED) of these nanocomposites were determined for N2, O2, CO2, and CH4 and a clear linear correlation between the two activation energies was established for the first time.
Carbon nanomembranes are synthetic two-dimensional sheets with nanometer thickness, macroscopic lateral dimensions, and high structural homogeneity. They have great application potential in various branches of nanotechnology. Because of their full carbon structure, it is not clear whether macromolecules like poly(methyl methacrylate) (PMMA) can be irreversibly adsorbed on their surface. Here, irreversible adsorption means that the polymer chains cannot be removed by a leaching process, which is assumed in technological transfer processes. However, if polar defects are present on the carbon nanomembranes (CNMs), it may occur that polymers can be irreversibly adsorbed. To address this question, PMMA was spin-coated on top of CNMs, annealed for a specific time at different temperatures, and then tried to be removed by a acetone treatment in a leaching approach. The samples were investigated in detail by atomic force microscopy, X-ray photoelectron spectroscopy, and broadband dielectric spectroscopy, where the latter method has been applied to CNMs for the first time. Unambiguously, it was shown that PMMA can be adsorbed on the surface of CNMs after annealing the sample above the glasstransition temperature of PMMA. The general occurrence of polar defects on the surface of CNMs and the adsorption of polymers open opportunities for advanced innovative hybrid materials combining the properties of the CNM with those of the polymer.
Hexakis(n-alkyloxy)triphenylene) (HATn) consisting of an aromatic triphenylene core and alkyl side chains are model discotic liquid crystal (DLC) systems forming a columnar mesophase. In the mesophase, the molecules of HATn self-assemble in columns, which has one-dimensional high charge carrier mobility along the columns. Here, a homologous series of HATn with different length of the alkyl chain (n = 5,6,8,10,12) is investigated using differential scanning calorimetry (DSC), broadband dielectric spectroscopy (BDS) and advanced calorimetric techniques including fast scanning calorimetry (FSC) and specific heat spectroscopy (SHS). The investigation of the phase behavior was done utilizing DSC experiments and the influence of the alkyl chain length on the phase behavior was revealed. By the dielectric investigations probing the molecular mobility, a c-relaxation due to localized fluctuations as well as two glassy dynamics, the acore- and aalkyl-relaxation, were observed in the temperature range of the plastic crystalline phase. Moreover, the observed glassy dynamics were further studied employing advanced calorimetry. All observed relaxation processes are attributed to the possible specific molecular fluctuations and discussed in detail. From the results a transition at around n = 8 from a rigid constrained (n = 5,6) to a softer system (n = 10,12) was revealed with increasing alkyl chain length. A counterbalance of two competing effects of a polyethylene-like behavior of the alkyl chains in the intercolumnar domains and self-organized confinement is discussed in the context of a hindered glass transition.
Epoxy nanocomposites are promising materials for industrial applications (i.e., aerospace, marine and automotive industry) due to their extraordinary mechanical and thermal properties. Here, the effect of hollow halloysite nanotubes (HNT) on an epoxy matrix (Ep) was the focus of the study. The structure and molecular mobility of the nanocomposites were investigated using a combination of X-ray scattering, calorimetry (differential (DSC) and fast scanning calorimetry (FSC)) and dielectric spectroscopy. Additionally, the effect of surface modification of HNT (polydopamine (PDA) and Fe(OH)3 nanodots) was considered. For Ep/HNT, the glass transition temperature (Tg) is was de-creased due to a nanoparticle-related decrease of the crosslinking density. For the modified system, Ep/m-HNT, the surface modification resulted in enhanced filler–matrix interactions leading to higher Tg values than the pure epoxy in some cases. For Ep/m-HNT, the amount of interface formed between the nanoparticles and the matrix ranged from 5% to 15%. Through BDS measurements, localized fluctuations were detected as a β- and γ-relaxation, related to rotational fluctuations of phenyl rings and local reorientations of unreacted components. A combination of calorimetry and BDS dielectric spectroscopy revealed a dynamic and structural heterogeneity of the matrix, as confirmed by two glassy dynamics in both systems, related to regions with different crosslinking densities.
The complex effect of nanoparticles on an epoxy-based and anhydride cured DGEBA/Boehmite nanocomposite with different particle concentrations is considered in this chapter. A combination of X-ray scattering, calorimetry (fast scanning and temperature modulated calorimetry) and dielectric spectroscopy was employed to characterize the structure, vitrification kinetics and the molecular dynamics of the nanocomposites. Firstly, the unfilled polymer was found to be intrinsically heterogeneous, showing regions with different crosslinking density, indicated by two separate dynamic glass transitions. Moreover, the glass transition temperature decreases with increasing nanoparticle concentration, as a result of changes in the crosslinking density. In addition, it was shown that the incorporation of nanoparticles can result in simultaneous increase in the number of mobile segments for low nanoparticle concentrations and on the other hand, for higher loading degrees the number of mobile segments decreases, due to the formation of an immobilized interphase.
The effect of a nanometre confinement on the molecular dynamics of liquid crystals was studied by broadband dielectric and neutron spectroscopy. As confining host the molecular sieve Al-MCM-41 (Si/Al=60) with a mean pore diameter of 3 nm was selected. As guest the liquid crystals 8CB and E7 were chosen where the latter does not crystallize but undergoes a glass transition forming a nematic glass.
Dielectric spectroscopy shows that for the confined systems one relaxation process is observed. Ist characteristic relaxation time is much lower compared to that of the bulk. No signature of the Phase transition characteristics of the bulk liquid crystal is detected. The temperature dependence of the relaxation time of this relaxation process has to be described by the Vogel-Fulcher-Tammann equation and thus shows similarities to glassy dynamics.
The vibrational density of states measured by neutron spectroscopy (IN6, ILL; TOFTOF, MLZ) Shows excess contributions with respect to the Debye density of states (boson peak). For the confined systems the low frequency contributions of the boson peak are suppressed, an effect which is also found for conventional glass forming systems.
In addition elastic scans were carried out at the backscattering spectrometer (BS) IN10 at ILL. Such measurements provide an overview about the temperature dependence of the microscopic dynamics.
Assuming a Gaussian form for the elastically scattered intensities the effective mean square displacement was calculated. For the nanoconfined samples the mean square displacement is strongly reduced in comparison to the bulk. Also these measurements show the signature of a glass Transition indicated by a change in the temperature dependence of the mean square displacement. For confined E7 the extracted glass transition temperature is shifted by more than 20 K to higher temperatures.
Broadband inelastic neutron scattering was carried out by combining time-of-flight (IN6, ILL; TOFTOF, MLZ) and backscattering (IN10, ILL; SPHERES, MLZ) experiments in the time domain.
The time dependence of the incoherent intermediate scattering function Sinc(q,t) shows two Relaxation processes which were quantitatively analyzed by fitting the KWW function to the data. The process at shorter times shows a close similarity the methyl group rotation found for polymeric systems. The process at longer times was assigned to glassy dynamics. The obtained data are compared in detail in their temperature dependence to the dielectric results.
The glass transition behavior of ultra-thin supported polymer films is discussed controversially in the literature for around 20 years. Substantial efforts have been archived to understand it. In this contribution, a combination of methods sensitive to bulk properties of a system, like dielectric or specific heat spectroscopy with surface analytics, for instance, atomic force microscopy (AFM), contact angle measurements, and X-ray photoelectron spectroscopy (XPS) were employed to study the glass transition of ultra-thin supported films. All investigations were carried out on identically prepared and treated samples. Different systems with different complexities going from more or less flexible homopolymers over rigid main chain macromolecules to polymer blends have been studied. For the investigated flexible macromolecules, the dynamic glass transition temperature estimated within the frame of the linear response approach is independent of the film thickness down to several nanometers and identical to the bulk value. For polystyrene it was found the thermal glass transition temperatures can depend on the film thickness. This different behavior is not well understood till now and needs further experimental clarification. For the investigated main chain polymers polycarbonate and polysulfone. Dynamic and thermal glass transition temperature estimated from the dielectric measurements increases with decreasing film thickness. This is discussed in the frame of a strong interaction of the polymer segments with the surface of the substrate. In general for homopolymers, the interaction energy of the polymer segments with the substrate surface cannot be considered as the only parameter, which is responsible for the change in the thermal glass transition with the film thickness. For the investigated miscible blend system of polystyrene/poly(vinyl methyl ether) at a composition of 50/50 wt-% a decrease of the dynamic glass transition temperature with decreasing film thickness is found. This is explained by the formation of a poly(vinyl methyl ether)-rich surface layer with a higher molecular mobility.
The basics of broadband dielectric spectroscopy were introduced in detail. The analysis of the data was discussed. As application of broadband dielectric spectroscopy the alpha-relaxation (dynamic glass transition), the chain dynamics of polymers, and the behavior of a high performance polymer were illustrated.