- NEXAFS (43)
- XPS (35)
- Plasma polymerization (9)
- Plasma (7)
- ToF-SIMS (7)
- ESCA (5)
- ESCA/XPS (4)
- Graphene (4)
- Surface analysis (4)
- Oberflächenanalyse (3)
Organisationseinheit der BAM
- 6 Materialchemie (10)
- 6.1 Oberflächen- und Dünnschichtanalyse (10)
- 1 Analytische Chemie; Referenzmaterialien (1)
- 1.1 Anorganische Spurenanalytik (1)
- 1.4 Prozessanalytik (1)
- 1.6 Anorganische Referenzmaterialien (1)
- 4 Material und Umwelt (1)
- 4.1 Biologische Materialschädigung und Referenzorganismen (1)
- 6.3 Strukturanalytik (1)
- P Präsident (1)
We report a surface analytical study of poly(methyl methacrylate) (PMMA) microparticles (beads) with a grafted shell of poly(acrylic acid) (PAA) with thicknesses up to 4 nm using scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), time-of-flight secondary ion mass spectrometry (ToF-SIMS), and near-edge X-ray adsorption fine structure (NEXAFS) spectroscopy. These polymer microparticles were analyzed before and after reaction of the surface carboxyl (CO2H) groups with 2,2,2-trifluoroethylamine (TFEA) to gain a better understanding of methods with use of covalently bound probe molecules for surface group analysis. The results obtained with chemical derivatization XPS using TFEA are discussed in terms of surface quantification of reactive CO2H groups on these PAA-coated microparticles. A labeling yield of about 50% was found for TFEA-derivatized particles with amounts of surface-grafted CO2H groups of 99 µmol/g or more, which is consistent with predicted reaction yields for homogeneously dispersed PAA hydrogels.
NEXAFS analysis of a plasma treated, partially crystalline poly(ehtylene terephtalate) surface
(1996)
Self-assembled octadecyltrichlorosilane (CH3(CH2)17SiCl3, OTS) films were deposited on an oxidized silicon wafer. They were carefully exposed to a low-pressure oxygen direct current (dc) plasma and/or Cr vapor. Subsequently, they were characterized by X-ray photoelectron spectroscopy, near-edge X-ray absorption fine structure spectroscopy, and atomic force microscopy. Detailed information on the oxygen functionalization and the molecular conformation of the OTS films was obtained. The main result was that functionalization conditions can be found where the order of the film remains almost unaffected. Similarly, Cr evaporation of pure OTS films revealed only slight effects on the order in the film. Cr evaporation of an ordered but functionalized OTS film immediately changes its state toward a fully isotropic one. In the course of interaction, oxygen sites at the surface of the functionalized OTS film are reduced whereas Cr becomes oxidized. A redox reaction scheme is proposed for this interfacial reaction. Finally, it is concluded that the given study should be of importance for advanced plasma processing of polyolefins.
Barrier properties of plasma and chemically fluorinated polypropylene and polyethyleneterephthalate
(1995)
The functionalization, perfluorination or an coating of polypropylene (PP) and polyethyleneterephthalate (PET) surfaces in different plasma atmospheres and in an F[2] + N[2] gas mixture were investigated. The aim of this work was to form a barrier layer against solvent and fuel permeation. Typical test solvents were n-pentane, toluene, tetrachloroethylene and mixtures of n-pentane and methanol. The permeation was gravimetrically measured. The permeation of the solvent mixtures was analyzed by mass spectrometry and Fourier transform IR spectroscopy. The permeation of the solvent mixtures through the plasma-modified polymer samples was associated with increased absorption of polar solvent components in the polymer film. The thickness of the plasma-fluorinated PP surface layer was 10-100 nm and that of chemically fluorinated PP about 5000 nm. Nearly the same barrier efficiency was measured for both plasma- and chemically fluorinated samples.
Neues vom Urkilogramm
(1999)
Overlayers of SiO2 (nominally 4, 6 and 8 nm thick) on silicon, prepared by thermal oxidation, were investigated using x-ray photoelectron spectroscopy (XPS). The thickness of these overlayers was obtained from a measurement of the photoelectron intensities originating from the substrate and the oxide overlayer by applying an appropriate quantitative model. The uncertainty budget of that thickness measurement method is given. The relative combined standard uncertainty of the method was found to be 15%. The effective attenuation lengths or the corresponding electron inelastic mean free paths are of considerable importance for both the estimated values of overlayer thickness and combined standard uncertainties. The XPS results were compared with ellipsometry data.
Powder x-ray diffraction (XRD) defined -Al2O3 has been investigated by x-ray photoelectron spectroscopy (XPS) and x-ray excited Auger electron spectroscopy (XAES). The Au 4f7/2 orbital is used for static charge referencing. This feature originates from well-defined and chemically inert 20 nm highly dispersed gold particles deposited on the sample surface. The particles, with a narrow particle size distribution, were obtained from a highly purified colloidal solution (sodium concentration below 1 mg/l). This procedure allows a determination of gold-referenced XPS and XAES data sets. ©2001 American Vacuum Society.
Several approaches were investigated to produce monosort functionalized polymer surfaces with a high density and homogeneity of functional groups: (i) Plasma oxidation followed by wet-chemical reduction, (ii) formation of radicals and grafting on of functional group carrying molecules, (iii) plasma bromination followed by (iv) Williamson or Gabriel-like synthesis of spacer molecules, and (v) a pulsed plasma polymerization of functional groups bearing monomers or (vi) their copolymerisation with other comonomers. The formation of hydroxyl (OH), primary amino (NH2), and carboxyl (COOH) groups was studied in detail. The oxygen plasma treatment (i) in a low-pressure non-isothermal glow discharge results in the formation of a wide variety of O functional groups, polymer degradation and crosslinking. Low power densities and short exposure times (0.1 to 2 s) are required to functionalize a surface while preserving the original polymer structure. Carbonate, ester, and aromatic groups are rapidly degraded by an oxygen plasma treatment leading to scissions of polymer backbones and loss in molecular weight. Also the formation of macrocycles and C=C bonds was observed in a region of around 4 nm in depth. The investigated polymers could be classified by their degradation behaviour on exposure to the oxygen plasma.___TAGSTART___BR___TAGEND___ In order to maximize the process selectivity for OH groups, the variety of oxygen functionalities formed by the oxygen plasma was wet-chemically reduced by diborane, vitridetrade (Na complex), and LiAlH4. Typical yields were 9 to 14 OH groups per 100 carbon atoms.___TAGSTART___BR___TAGEND___ Plasma bromination (iii) (40 Br per 100 C atoms) of polymers, followed by grafting of spacer molecules (iv), has been proved to be a highly selective reaction.___TAGSTART___BR___TAGEND___ Another way to produce high densities of monosort functionalities was the pulsed plasma polymerization of functional group bearing monomers such as allylamine, allylalcohol or acrylic acid (v). The retention of chemical structure and functional groups during plasma polymerization was achieved by using low power densities and the pulsed plasma technique. The maximum yields were 30 OH, 18 NH2, and 24 COOH groups per 100 C atoms. To vary the density of functional groups a chemical copolymerization with ''chain-extending'' comonomers such as butadiene and ethylene was initiated in the pulsed plasma (vi). Additionally, the often-observed post-plasma oxidations of such layers initiated by reaction of trapped radicals with oxygen from the air were successfully suppressed by using NO gas as radical quencher.