Filtern
Erscheinungsjahr
- 2018 (5) (entfernen)
Dokumenttyp
- Zeitschriftenartikel (2)
- Vortrag (2)
- Posterpräsentation (1)
Sprache
- Englisch (5)
Schlagworte
- Spectroscopic ellipsometry (2)
- Electron probe microanalysis (EPMA) (1)
- Ellipsometric metrology (1)
- Femtosecond laser (1)
- Friction (1)
- Glass transition (1)
- Iridium oxide (1)
- Oxidation (1)
- PVME (1)
- Polymers (1)
Organisationseinheit der BAM
- 6 Materialchemie (5)
- 6.7 Materialsynthese und Design (5)
- 6.6 Physik und chemische Analytik der Polymere (2)
- 5 Werkstofftechnik (1)
- 5.1 Mikrostruktur Design und Degradation (1)
- 6.1 Oberflächen- und Dünnschichtanalyse (1)
- 6.2 Material- und Oberflächentechnologien (1)
- 9 Komponentensicherheit (1)
- 9.5 Tribologie und Verschleißschutz (1)
Eingeladener Vortrag
- nein (2)
In this presentation, we report on the Determination of the glass transition temperature of thin layers of Polyvinylmethylether (PVME) depending on the thickness of the polymer layer. The glass Transition of thin polymer layers is currently under much investigation due to the nano-confinement effects proposed to appear in dependence on the layer thicknesses in the nm range. The properties of the polymer, the temperature range, as well as the thicknesses range of the polymer layers pose a serious challenge to the investigation by means of
spectroscopic ellipsometry. By careful choice of experimental parameters, we were able to investigate the thickness change by temperature of PVME layers in the range between 2 and 300 nm and in the temperature range between 200 K and 340 K. By optimizing the analysis process, we were able to determine Tg values within this parameter range with sufficient accuracy to investigate the Tg change due to confinement effects.
Alongside the change of position of the glass transition with thickness, we discuss the details of the ellipsometric analysis and its implications for the resulting thermal properties of the thin polymer layers as well as the accuracy of the Tg value with respect to the method used in the analysis process.
Ellipsometry is well known as a highly sensitive and reproducible surface analysis technique. However, in a context of metrological applications, the most important property of a measurement process is accuracy, relying on statistical precision, (reproducibility) and trueness (in an absolute sense versus a given standard). The latter is much more difficult to achieve. In this presentation, we discuss the possibility of establishing ellipsometry in a diverse metrological landscape by means of defining standard procedures and best practice methodologies for the measurement and for calibration purposes. The most important task of this approach is to determine the model-inherent uncertainty, originating from parameter coupling. We achieve this by means of sensitivity analysis of the parameters resulting from the fit process. We discuss the definition of reference materials by which accuracy can be made available for ellipsometry, passed along between ellipsometry laboratories and for other measurement techniques. The determination of uncertainty is presented in this work for a number of examples involving difficult analysis models employed for samples from different production environments. We present a standardization initiative with the goal to disseminate this work into an international standard alongside an inter-laboratory study comparing the results for complex samples gained by laboratories with different instrumentation. We also present the results gained within EURAMET projects focused on the metrology of materials with strong non-idealities used in photovoltaics and other energy technology.
For the determination of porosity of Ir oxide thin films, electron probe microanalysis (EPMA) can be used as part of a combined SEM/EDS/STRATAGem analysis. The mass deposition (in μg cm-2) of films was calculated with the analysis software STRATAGem via k-values measured with EDS. The average density of coated films was obtained from the mass deposition and the film thickness as measured by the cross-section SEM. The porosity was calculated by dividing the average film density by the bulk (theoretical) density of the film material.
Film porosities were counterchecked by spectroscopic ellipsometry (SE) using the Bruggeman effective medium approximation (BEMA).
The results obtained by both analytical approaches/methods used, SEM/EDS/STRATAGem and SE were in good agreement.
Surface analysis is still gaining importance, as most modern technology is in essence surface and thin film technology. In microelectronics and optics but also in many fields of energy storage and conversion, thin surface layers or structured surfaces are key components. Optical surface measurements are useful because of their reliability, robustness, and scalability – properties, which are especially desirable in a production environment. However, many of these methods take require considerable effort in data analysis. Spectroscopic ellipsometry (SE) is maybe the prime example of this class of methods. To combine the advantages of SE with metrological trueness and traceability, we combine it in a group of other methods, such as electron microscopy, instrumental surface analysis, X-ray diffraction.
This presentation will give an overview on the principles of SE, its available quantities and the general properties of this measurement technique. Several examples from current and past projects of BAM-6.7 will show how a measurement community involving ellipsometry can benefit many fields of interest, from polymer science to energy applications. In the context of creating a “measurement landscape”, standardisation and standard compliance play an important role. The efforts of BAM in standardisation and accrediting of ellipsometry will be shown demonstrating the possible impact on quality assurance in different fields of technology.
Commercial grade-1 titanium samples (Ti, 99.6%) were treated using three alternative methods, (i) femtosecond laser processing, (ii) thermal heat treatment, and (iii) electrochemical anodization, respectively, resulting in the formation of differently conditioned superficial titanium oxide layers. The laser processing (i) was carried out by a Ti:sapphire laser (pulse duration 30 fs, central wavelength 790 nm, pulse repetition rate 1 kHz) in a regime of generating laser-induced periodic surface structures (LIPSS). The experimental conditions (laser fluence, spatial spot overlap) were optimized in a sample-scanning setup for the processing of several square-millimeters large surface areas covered homogeneously by these nanostructures. The differently oxidized titanium surfaces were characterized by optical microscopy, micro Raman spectroscopy, variable angle spectroscopic ellipsometry, and instrumented indentation testing. The tribological performance was characterized in the regime of mixed friction by reciprocating sliding tests against a sphere of hardened steel in fully formulated engine oil as lubricant. The specific tribological performance of the differently treated surfaces is discussed with respect to possible physical and chemical mechanisms.