A model based on movable cellular automata (MCA) is described and applied for simulating the stress–strain and sliding behavior of a nanocomposite consisting of an epoxy matrix and 6 vol.% of homogeneously distributed silica nanoparticles. Tensile tests were used for verification of the model. It was realized that a slight modification of epoxy properties due to the addition of silica nanoparticles had to be taken into account in order to obtain good correlation between experimental and modeling results. On the other hand, sliding simulations revealed no susceptibility of results to slight modifications of matrix properties, but a significant impact of nanoparticles on the interface structure and smoothness of sliding mechanism. Furthermore, assuming both possibilities, bond breaking and rebinding of automata pairs, can explain different friction levels of polymer materials.
A model based on movable cellular automata has been applied to study the sliding behaviour of tribofilms formed during automotive braking. Since it is not possible yet to determine the composition of real tribofilms quantitatively, final verification of modelling results is needed. This was done by preparing artificial third bodies with compositions and nanostructures matching the ones assumed for modelling. Pin-on-disc tests were performed while applying the artificial third bodies to the contact. The results revealed that not only the structure of the third body but also the amount of the applied normal pressure determines the COF obtained by modelling and that much better correlation between experimental and modelling results was obtained while assuming high normal pressures at asperity contacts.
Copper is one of the most important components in brake pads and its amount can reach up to 14%. In spite of a number of positive features copper usage in brake pad formulations has recently become the subject of considerable discussions, primarily due to concerns about potential risks related to environmental impacts of copper particles. So, for developing new pad formulations with possible replacements of copper content, it is very important to understand the functionality of copper additions to brake friction materials. In the paper theoretical investigation of the role of copper as a pad ingredient was carried out on the basis of modelling by the method of movable cellular automata (MCA). Our previous studies show that copper as a constituent of the tribofilm formed during braking provides smooth sliding by forming a granular layer of mechanically mixed materials from the friction layers. In the present study the concentration of copper particles in a Fe3O4-matrix was varied systematically in the range 5.5-28 vol. % and compared to mixtures with the same amount of graphite nanoparticles. The sliding simulations were performed while assuming material properties at 500°C in order to assess the beneficial role of copper during severe braking conditions corresponding to fading cycles during dynamometer testing.