With CO2 being one reason for climate change carbon capture and storage (CCS) is discussed to mitigate climate change. When emission gases are compressed into deep geological layers CO2-corrosion can easily cause failure of injection pipes. Different steels 42CrMo4, X46Cr13 and X20Cr13 were tested as well as X35CrMo17 and X5CrNiCuNb16-4 in a laboratory Environment similar to the conditions of the CCS engineering site at the Northern German Bassin. Samples were exposed to synthetic aquifer water saturated with technical CO2 at a flow rate of 3 NL/h.
Corrosion rates obtained via mass loss vary in a wide range (0,005 to 2.5 mm/year). The precipitations within the corrosion scale revealed a complicated multiphase layer containing siderite FeCO3, goethite α-FeOOH, lepidocrocite γ-FeOOH, mackinawite FeS and akaganeite Fe8O8(OH)8Cl1,34 and spinelphases of various compositions.
In geothermal power plants materials e.g. pumps are exposed to extremely corrosive thermal water. This results in corrosion fatigue and so inevitably the reduction of the lifetime of these components. Also in the field of the carbon dioxide storage technology (carbon capture and storage CCS) components are exposed to a corrosive environment and mechanical stress. In order to gain knowledge upon the corrosion fatigue strength of materials a corrosion chamber for "in situ" conditions was designed and successfully applied.Two different steels X46Cr13 and X5CrNiCuNb16-4 have been tested and their corrosion fatigue behavior was compared. To simulate the frequency of operating pumps (30 – 40 Hz) a resonant testing machine was used. In addition technical CO2 was introduced into the closed system at a rate close to 9 L/h to keep stable environmental conditions. The samples have a surface roughness of Rz = 4 to simulate technical machined surfaces. The calculated tensile strength of X46Cr13 with soft annealed microstructure (coagulated cementite in ferrite-perlite matrix) is about 680 MPa and the yield strength is about 345 MPa. The tensile strength of X5CrNiCuNb16-4 is about 1078 MPa and the yield strength about 928 MPa. Testing parameters are: corrosion media: saline aquifer water (Stuttgart Aquifer) temperature of the brine at 60 °C and load ratio of R=-1. For X46Cr13 a stress amplitude between 160 MPa to 270 MPa and for X5CrNiCuNb16-4 a stress amplitude between 150 to 500 was chosen. Cycles until crack initiation differ strongly and were found to start at 5 x 104 up to 12.5 x 106 cycles.X46Cr13 has reached a maximum number of cycles (12.5 x 106) at a stress amplitude of 173 MPa. X5CrNiCuNb16-4 has reached the maximum number of cycles (10 x 106) at a stress amplitude of 150 MPa. The range of scatter for X5CrNiCuNb16-4 is very high (1:34) in comparison the range of scatter for X46Cr13 (1:3.5).
The commercial usage of latent thermal energy storages primarily depends on the development of a suitable phase change material (PCM). For industrial high temperature applications above 400 °C multicomponent chloride eutectics are promising and therefore discussed seriously. The profound thermodynamic investigation of such eutectics requires a much greater amount of specimen material than conventional calorimeter can handle. Therefore, a special adiabatic calorimeter was developed and designed. With a specimen mass of > 100 g the typical thermodynamic measurements with a commercial calorimeter can be extended by cycle stability measurements, which are often decisive for practical application of PCM. Furthermore, by implementing corrosion specimens inside the calorimeter high temperature corrosion experiments according to ISO 21608 can be performed inside the calorimeter. Adiabatic measuring conditions can be provided by using two separate heating systems. Therefore, the outer “protective system” follows the temperature curve of the inner “measuring system” minimizing the temperature difference between the heating systems and simultaneously preventing heat losses from the measuring systems.
The lifetime reduction of cyclically loaded AISI 420C (X46Cr13, 1.4034) constantly exposed to highly corrosive CO2-saturated hot thermal water is demonstrated in in situ-laboratory experiments (60 °C, brine: Stuttgart Aquifer, flowing CO2: 30 L/h). SN plots, micrographic-, phase-, fractographic- and surface analysis were applied to obtain sustainable information on the corrosion and corrosion fatigue behavior. Maximum number of cycles (here 12.5 × 106 cycles to failure) is reached at σa = 173 MPa. Hydroxide and siderite layers were found on pits and crack surfaces. No typical fatigue limit exists and pit corrosion prior to crack initiation may be identified as failure cause.
During capture and storage technology (CCS) as well as in geothermal energy production Steels need to withstand the corrosive environment such as: heat, pressure, salinity of the aquifer and CO2-partial pressure. 1.4542 shows unusual corrosion phenomena, but is still sufficiently resistant in corrosive environments. To better understand its behaviour differently heat treated coupons of 1.4542 and for comparison X20Cr13 and X46Cr13 were kept in the artificial brine of the Northern German Basin at T=60 °C. Ambient pressure as well as p=100 bar for 700 h - 8000 h in water saturated supercritical CO2 and CO2-saturated synthetic aquifer Environment was applied. Fatigue tests were performed via push-pull tests with a series of 30 specimens from 150 MPa to 500 MPa (sinusoidal dynamic test loads, R=-1; resonant frequency ~ 30 Hz). FeCO3 and FeOOH are corrosion products also after dynamic corrosion tests. Martensitic microstructure offers good corrosion resistance in geothermal environment. The S-N-curve showing no typical fatigue strength and very steep slopes of possible fatigue strength for finite life. Possible influencing artefacts, such as Al-inclusions could not be correlated to early rupture despite specimens containing inclusions at the fracture surface and cross section reached lower number of cycles. Applied potential proofed to enhance fatigue life tremendously.
The process chain for Carbon Capture and Sequestration (CCS) includes tubing for injection of CO2 into saline aquifers. The compressed CO2 is likely to contain specific impurities; small concentrations of SO2 and NO2 in combination with oxygen and humidity are most harmful. In addition, CO2 saturated brine is supposed to rise in the well when the injection process is interrupted. The material selection has to ensure that neither CO2 nor brine or a combination of both will leak out of the inner tubing. In this comprehensive paper the investigated materials range from low-alloy steels and 13% Cr steels up to high-alloy materials. Electrochemical tests as well as long term exposure tests were performed in CO2, in brine and combination of both; pressure was up to 100 bar, temperature up to 60 °C. Whereas the CO2 stream itself can be handled using low alloy steels, combinations of CO2 and brine require more resistant materials to control the strong tendency to pitting corrosion. The corrosion behavior of heat-treated steels depends on factors such as microstructure and carbon content. For different sections of the injection tube, appropriate materials should be used to guarantee safety and consider cost effectiveness.
The corrosion behaviour of martensitic stainless injection-pipeline steel X46Cr13 exposed to CO2 saturated artificial saline brine with high chloride concentration similar to onshore CCS-site at Ketzin, Germany has been investigated by means of electrochemical technique and microscopic observations at short exposure times (up to 24?h) and by mass loss and metallographic observations at exposure times up to 17520?h. Pitting corrosion kinetics has been characterised and the predictions about the corrosion mechanism are made.
Degradation of AISI 630 exposed to CO2-saturated saline aquifer at ambient pressure and 100 bar
(2018)
In general high alloyed steels are suitable as pipe steels for carbon capture and storage technology (CCS), because they provide sufficient resistance against the corrosive environment of CO2-saturated saline aquifer which serves as potential CCS-site in Germany. High alloyed martensitic steel AISI 630 has been proven to be sufficient resistant in corrosive environments, e.g. regarding heat, pressure, salinity of the aquifer, CO2-partial pressure), but reveals a distinct corrosion pattern in CCS environment. Therefore coupons of AISI 630 heat treated using usual protocols were kept at T=60 °C and ambient pressure as well as p=100 bar up to 8000 h in an a) water saturated supercritical CO2 and b) CO2-saturated synthetic aquifer environment similar to on-shore CCS-sites in the Northern German Basin. AISI 630 precipitates a discontinuous ellipsoidal corrosion layer after being exposed for more than 4000 hours. Best corrosion resistance in the CO2-saturated synthetic aquifer environment phase is achieved via normalizing prior to exposure. In water saturated supercritical CO2 tempering at medium temperatures after hardening gives lowest corrosion rates. Corrosion fatigue via push-pull tests with a series of 30 specimens was evaluated at stress amplitudes between 150 MPa and 500 MPa (sinusoidal dynamic test loads, R=-1; resonant frequency ~ 30 Hz). The endurance limit of AISI 630 is reduced by more than 50% when exposed to CCS environment (maximum number of cycles (10 x 106) at a stress amplitude of 150 MPa).
Design of a high pressure system for in-situ tests on the corrosion fatigue of metallic materials
(2014)
In geothermal power plants pumps are exposed to corrosive and oscillating loads. This leads to corrosion fatigue and reduces the lifetime of certain components. Usually underwater power pumps are placed inside the borehole. In this case an installation depth of 600 to 800 meters below ground level is typical. In these depths an additional load due to high pressure and high temperature is introduced which is based on geothermal brine. Therefore the material which is used for the pump is steel.For fatigue testing at loads existing in deep geological layers an appropriate system for fatigue tests under in-situ conditions was set up. The requirements of the design are: temperature of the corrosion medium of 200 °C pressure of 200 bars and the complete immersion of the specimen in flowing corrosion medium containing mixtures of corrosive gasses during the entire test period.The test system has three main components the corrosion chamber the heating module and the reservoir. It is important that the corrosion chamber is only fixed onto the specimen which allows for highest flexibility of the test system operational in many different test machines. The heating module heats the corrosion medium up to 200 °C. The reservoir make sure that the volume of the corrosion medium satisfies requirements of the DIN 50905 Part 1 is conformed providing minimum required corrosive medium of 10 ml/cm² in relation to the sample surface.This innovative fatigue test system aims at performing in- situ fatigue corrosion tests simultaneously at high pressure and high temperature in liquid and gaseous corrosive environment. Results from the tests will allow determining the fatigue life of several materials influenced by pressure and temperature under corrosive conditions.
CO2-induced corrosion of casing and tubing steels is a relevant safety issue for compressing emission gasses into deep geological layers (CCS, Carbon Capture and Storage). The influence of CO2 and pressure of the surrounding media on steels is demonstrated in laboratory experiments providing a corrosive environment similar to a geological onshore CCS-site in the Northern German Basin (T = 60 °C, p = 1 - 100 bar, Stuttgart Aquifer, CO2-flow rate of 3 l/h, 7008000 h exposure time). Corrosion kinetics and microstructures were characterized using specimens of heat treated 42CrMo4 (1.7225, casing) and soft annealed X46Cr13 (1.4034, tubing).