Organisationseinheit der BAM
Coupons of X5CrNiCuNb16-4 that may be used as injection pipe with 16% Chromium and 0.05% Carbon (1.4542, AISI 630) were exposed for 3000 h to CO2-saturated saline aquifer water similar to the conditions in the Northern German Basin at ambient pressure and 60 °C. Surface corrosion layers and pits reveal carbonate corrosion products on the surface such as FeCO3 and FeOOH as the main precipitation phases with no dependence on the original surface roughness. Corrosion rates for polished and technical surfaces were below 0.005 mm/year compared to corrosion rates of 0.035 mm/year after shot peening.
Coupons of X5CrNiCuNb16-4 with different surface roughness that may be utilized as injection pipe with 16% Chromium and 0.05% Carbon (1.4542, AISI 630) were exposed for 3000 h to CO2-saturated saline aquifer water simulating the conditions in the Northern German Basin at ambient pressure and 60 °C. Additionally, corrosion fatigue experiments (ambient pressure, technically clean CO2, saline aquifer water of Stuttgart Aquifer) were performed using specimen of X46Cr13 (1.4043, AISI 420C) with regard to the influence of the roughness of technical surfaces on the number of cycles to failure at different stress amplitudes. Specimen of Duplex stainless steel X2CrNiMoN22-3-2 (1.4462) for corrosion fatigue experiments were provided with technical surfaces after machining as well as polished surfaces. Results were obtained at load amplitudes ranging from 175 MPa to 325 MPa in the geothermal brine of the Northern German Basin at 98 °C. The main precipitation phases on the surface as well as within pits reveal carbonates or hydroxides such as siderite (FeCO3) and ferrous hydroxide goethite (FeOOH) independent of the original surface roughness. Corrosion rates for polished and technical surfaces were below 0.005 mm/year compared to corrosion rates of 0.035 mm/year after shot peening. Specimen with technical surfaces tested at high stress amplitudes (>275 MPa) lasted longer (cycles to failure: P50% at Sa 300 MPa=5x105) than specimen with polished surfaces (cycles to failure: P50% at Sa 300 MPa=1.5x105). This behavior is emphasized by the slope coefficient (technical surfaces k = 19.006, polished surfaces k=8.78) meaning earlier failure for polished at high stress amplitude Sa. Although rather low scatter ranges (technical surface: TN=1:1.35, polished surface: TN=1.1.95) indicate no change in failure mechanism it may be assumed that at low stress pitting is the initiating crack growth process whereas at high stress amplitudes the formation of micro cracks is reason for crack propagation and failure.
Die Lebensdauer von Bauteilen welche gleichzeitig mechanisch und korrosiv belastet werden kann mit vorhandenen Literaturwerkstoffdaten nicht ausreichend bestimmt werden. So kommt es entweder im Betrieb frühzeitigen versagen, oder einer Überdimensionierung bei der Konstruktion. Um Werkstoffe unter Bedingen der SchwingungsrisskorroSIOn zu prüfen und somit belastbare Materialkennwerte zu bekommen, ist es notwendig diese unter Realbedingungen in hierfür geeigneten Prüfanlagen zu testen.
During carbon dioxide storage technology (carbon capture and storage, CCS) components are exposed to a corrosive environment and mechanical stress, which results in corrosion fatigue and inevitably followed by the a lifetime reduction of these components. In order to gain knowledge upon the corrosion fatigue strength of materials, Samples of high alloyed stainless injection-pipe steels AISI 420 X46Cr13, and X5CrNiCuNb16-4 AISI 630 were tested in a at T=60 °C and ambient pressure in a CO2-saturated synthetic aquifer environment similar to possible geological on-shore CCS-sites in the northern German Basin. Therefore a corrosion chamber applied to a resonant testing machine allowing for “in situ” test conditions was designed and successfully tested. In-situ tension compression experiments were established using a resonant testing machine at a frequency as low as 30 – 40 Hz. In addition technical CO2 was introduced into the closed system at a rate close to 9 L/h to keep stable environmental conditions. Simultaneously electrochemical testing was performed to get information on failure causes and the mechanism of failure during the injection of CO2 into deep geological layers. S-N plots, micrographic analysis, and surface analysis of the fracture surface were applied to obtain sustainable information on the corrosion fatigue behavior of injection pipe steels. Samples used have a surface roughness of Rz = 4, to simulate technically machined surfaces. X46Cr13 reached the maximum number of cycles (12.5 x 106) at a stress amplitude of 173 MPa. X5CrNiCuNb16-4 reached the maximum number of cycles (10 x 106) at a stress amplitude at 150 MPa. The scatter range of X5CrNiCuNb16-4 is very high (1:34); by comparison the scatter range of X46Cr13 is only 1:3.5.
Samples of differently heat treated high alloyed stainless injection-pipe steels AISI 420 X46Cr13, AISI 420J X20Cr13 as well as X5CrNiCuNb16-4 AISI 630 were kept at T=60 °C and ambient pressure as well as p=100 bar for 700 h - 8000 h in a CO2- saturated synthetic aquifer environment similar to possible geological on-shore CCS-sites in the northern German Basin. Corrosion rates and scale growth are lowest after long term exposure for steels hardened and tempered at 600 to 670 °C and pits - indicating local corrosion- decrease in diameter but increase in number as a function of carbon content of the steel. Martensitic microstructure is preferred with respect to this particular CCS-site.
To resist the corrosive geothermal environment during carbon capture and storage CCS -such as: heat, pressure, salinity of the aquifer, CO2-partial pressure, properties of pipe steels-require certain specification. For evaluation samples of differently heat treated high alloyed stainless injection-pipe steels AISI 420 X46Cr13, AISI 420J X20Cr13 as well as X5CrNiCuNb16–4 AISI 630 were kept at T=60 °C and ambient pressure as well as p=100 bar for 700 h up to 8000 h in a CO2-saturated synthetic aquifer environment similar to a possible geological situation in the northern German Basin. Corrosion rates and scale growth are lowest after long term exposure for steels hardened and tempered at 600 °C to 670 °C and pits -indicating local corrosion- decrease in diameter but increase in number as a function of carbon content of the steel. Martensitic microstructure is preferred with respect to these particular conditions.
In the field of water pipelines, geothermal energy production as well as carbon capture and storage technology (CCS) materials have to provide a high resistance to corrosion and mechanical stress. The combination of cyclic load and corrosive aqueous environment leads to corrosion fatigue of pipes and components (e.g. pumps) and thus inevitably to the reduction of the lifetime of these components. To estimate the reliability of components from adjusted in-situ-laboratory experiments a corrosion chamber was designed and tested with CO2 saturated corrosive aqueous media flowing at a steady rate. Unique feature of this special chamber is its installation directly onto the sample and thus providing flexible usability in almost every testing machine. This allows simultaneous mechanical loading of the sample, operation at temperatures up to 100 °C and exposure to fluid flow of corrosive liquids and gases. The lifetime reduction of AISI 420C (X46Cr13, 1.4034) is demonstrated at T=60 °C, geothermal brine: Stuttgart Aquifer flow rate: 9 l/h, CO2. S-N plots, micrographic-, phase-, fractographic- and surface analysis were applied to obtain sustainable information on the corrosion fatigue behavior. Maximum number of cycles (here 12.5 x 106 cycles to failure) is reached at σa =173 MPa. No typical fatigue strength exists and passive corrosion fatigue may be identified as failure cause.
High-temperature-high pressure stress-strain testing of materials in CO2-containing saline solutions
(2015)
In-situ stress-strain testing under corrosive environment, such as corrosive gasses (e.g. CO2) and highly saline water, is a challenge in testing corrosion fatigue of materials, e.g. for geothermal application or CCS (carbon capture and storage). The first corrosion chamber system was designed for performance at ambient pressure up to 100 °C. The second allows for corrosion fatigue testing at high pressure up to 200 bar and 400 °C. The highly flexible corrosion chambers allow for fast changing and easy alignment of test samples, visual monitoring, CAD-camera monitoring electrochemical measurements, O2-partial pressure or gas partial pressure measurement. Novelty is the fixing of the corrosion chamber directly onto the specimen, that guarantees best fitting and enables the test system to be modified easily suiting a variety of fatigue test machines. All parts of the test system are conforming to the technical rules.