Filtern
Erscheinungsjahr
Dokumenttyp
- Zeitschriftenartikel (18)
- Monografie (1)
Sprache
- Englisch (19)
Schlagworte
- Plasma polymerization (4)
- Dielectric properties (3)
- Thermal stability (3)
- Graphene oxide (2)
- Lead ions (2)
- Polystyrene (2)
- Surface and bulk characterization (2)
- Surface functionalization (2)
- Thin films (2)
- Acrylic acid (1)
Organisationseinheit der BAM
Copolymers of acrylic acid and styrene (AA/S) were prepared by pulsed plasma deposition technique. Their structure–property relationships were studied in dependence on the comonomer ratio. Both, the regularity of the structure and the composition of the thin copolymer films were investigated by bulk-sensitive (dielectric spectroscopy, FTIR, and differential scanning calorimetry) as well as surface-sensitive methods such as X-ray photoelectron spectroscopy (XPS). For an unambiguous identification of the functionality of the deposited films the COOH groups were estimated by derivatization with trifluoroethanol and subsequent XPS measurement as well as by the quantitative analysis of the FTIR data. As a result, the concentration of COOH groups on the surface and in the bulk is increasing with the fraction of AA in precursor mixture in a non-monotonous way but similar to the dependence obtained by conventional free radical polymerization.
The pulsed plasma polymerization of allyl alcohol was employed under the aspect of maximal retention of OH groups and the formation of a regular polymer structure. It should be noted that earlier investigations on plasma polymers deposited from allyl alcohol did not show extensive postplasma addition of oxygen and water vapor from ambient air during storage, measuring the elemental O/C ratio by means of X-ray photoelectron spectroscopy (XPS).The identification of OH groups in the plasma polymerized polymer using FTIR spectroscopy was such an indicator for fragmentation. The peak area of OH groups in the film which was stored was increased by about 20% compared to that measured ('in situ'). These phenomenons reflected that moisture and O2 in air played an important role in scavenging the free radicals. The addition of water and more specifically chemical bonding of OH of water in the deposited plasma polymer may serve as an indicator for monomer fragmentation, poly recombination, and the remaining radicals responsible for film formation. Moreover, the dielectric measurements show that the plasma deposited films are not thermally stable but undergo a postplasma chemical reaction during heating, where the reaction kinetics depends on pressure.
Self-assembling biomolecules provide attractive templates for the preparation of metallic nanostructures. However, the intuitive transfer of the “outer shape” of the assembled macromolecules to the final metallic particle depends on the intermolecular forces among the biomolecules which compete with interactions between template molecules and the metal during metallization. The shape of the bio-template may thus be more dynamic than generally assumed. Here, we have studied the metallization of phospholipid nanodiscs which are discoidal particles of ~10 nm diameter containing a lipid bilayer ~5 nm thick. Using negatively charged lipids, electrostatic adsorption of amine-coated Au nanoparticles was achieved and followed by electroless gold deposition. Whereas Au nanoparticle adsorption preserves the shape of the bio-template, metallization proceeds via invasion of Au into the hydrophobic core of the nanodisc. Thereby, the lipidic phase induces a lateral growth that increases the diameter but not the original thickness of the template. Infrared spectroscopy reveals lipid expansion and suggests the existence of internal gaps in the metallized nanodiscs, which is confirmed by surface-enhanced Raman scattering from the encapsulated lipids. Interference of metallic growth with non-covalent interactions can thus become itself a shape-determining factor in the metallization of particularly soft and structurally anisotropic biomaterials.
Poly(acrylic acid) films with a thickness of about 150?nm were deposited using a pulsed plasma onto aluminum and glass. The structure/property relationships of these samples were studied in dependence to the duty cycle (DC) of the plasma by a broad combination of different techniques and probes. For the first time, volume sensitive methods (FTIR, dielectric spectroscopy, and differential scanning calorimetry) are combined with surface analyses i.e. XPS. For an unambiguous identification of COOH groups by XPS, derivatization with trifluoroethanol was accomplished. Quantitative FTIR investigations give qualitatively a dependence of the concentration of COOH groups upon DC similar to that given by XPS investigations. The observed differences are discussed considering the different analytical depths of both methods. The dielectric measurements reveal that the structure of the plasma deposited films is different from that of the bulk material. Moreover, these measurements show also that the plasma deposited films are not thermally stable but undergo a post plasma chemical reaction during heating, where the reaction kinetics depends on DC.
Poly(allyl alcohol) films with a thickness of about 150 nm were deposited by pulse plasma polymerization onto different substrates (inorganic and organic). The structure/property relationships of these samples were studied in dependence on the duty cycle (DC) of the plasma by a broad combination of different techniques and probes. For the first time volume sensitive methods (FTIR and dielectric spectroscopy) are combined with surface analytics by employing XPS for that system. FTIR spectroscopy gives qualitatively the same dependence of the concentration of the OH groups on DC like XPS.
The observed differences are discussed considering the different analytical depths of both the methods. The dielectric measurements show that the plasma deposited films are not thermally stable but undergo a post plasma chemical reaction during heating. The results obtained by dielectric spectroscopy are discussed in detail with the data from FTIR and XPS measurements.
A novel mixed matrix composite has been prepared using solution-casting method at different volume concentrations of polyvinyl alcohol; PVA (50, 67, 75 and 80 %) and fixed amount of Dimethoxydimethylsilane in air atmosphere. The hydrolyzed dimethyldisilanol acts as in-situ cross linker through a wet-out condensation between the hydroxyl moieties of SiOH and PVAOH. Such process improves the mechanical properties of composite membranes as compared to pristine PVA which has been determined as function of varied membrane components to evaluate the structure/property relationships.
Furthermore, DFT (B3LYP)/6-31G(d) geometry and frequency computations were carried out for the suggested dimeric PVA structures via 1,3-diol linkage followed by condensation and hydrogen bonding interaction. Vibrational interpretations of composite membranes were proposed based on the computed wavenumbers, Cartesian coordinates displacements for the suggested hydrolyzed products involving the dominant PVA/SiOH/SiOC/SiOSi functional groups compared with those given in literatures. FTIR and EDX provide clear evidences for incorporating silicon to 3D network. Meanwhile, the infrared de-convoluted spectral interpretations ensure 17-30% cross-linked SiOC within the network of Composite membranes.
Tetraethyl orthosilicate (TEOS) was used as a chemical precursor to deposit ultra-thin SiO x C y plasma polymer films onto mild steel surfaces for preventing the corrosion process. The structure–property relationships of the coatings were evaluated by X-ray Photo Spectroscopy (XPS), X-Ray Diffraction (XRD), Fourier Transform InfraRed spectroscopy (ATR-FTIR) and Energy Dispersive X-ray spectroscopy (EDX) completed with Scanning Electron Microscopy (SEM). The SEM micrographs confirmed a pinhole-free surface morphology of the low-pressure deposited plasma polymer films. The TEOS molecules become fragmented in the plasma by numerous collisions with energy-rich electrons and heavier particles. Recombination of fragments and condensation onto the steel substrate is responsible for the formation of organic SiO containing plasma polymer layers. Such thin layers consist of predominantly SiO x structures. Their properties are determined largely by the gap distance between the two samples used as electrodes in the plasma. The efficiency of the corrosion-protecting coating was compared with uncoated samples. The corrosion protection was determined by exposure of samples to 3.5% NaCl aqueous solutions. For this purpose, polarization and Electrochemical Impedance Spectroscopy (EIS) were used to monitor the corrosion. The optimal gap distance between the electrodes was determined for corrosion protection. The best protective efficiency reached more than 97% of the total protection as measured at room temperature.
An immobilization of graphene oxide (GO) into a matrix of polyvinyl formaldehyde (PVF) foam as an eco-friendly, low cost, superior, and easily recovered sorbent of Pb ions from an aqueous solution is described. The relationships between the structure and electrochemical properties of PVF/GO composite with implanted Pb ions are discussed for the first time. The number of alcohol groups decreased by 41% and 63% for PVF/GO and the PVF/GO/Pb composite, respectively, compared to pure PVF. This means that chemical bonds are formed between the Pb ions and the PVF/GO composite based on the OH groups. This bond formation causes an increase in the Tg values attributed to the formation of a strong surface complexation between adjacent layers of PVF/GO composite. The conductivity increases by about 2.8 orders of magnitude compared to the values of the PVF/GO/Pb composite compared to the PVF. This means the presence of Pb ions is the main factor for enhancing the conductivity where the conduction mechanism is changed from ionic for PVF to electronic conduction for PVF/GO and PVF/GO/Pb.
The electrospray ionization (ESI) method was used for deposition of thin films of poly(acrylic acid) (PAA) onto ZSM-5, Cu/ZSM-5 and Ag-Cu/ZSM-5 zeolites. This method allowed the formation of uniform polymer films of controlled thickness on conductive substrates.
The zeolites were prepared home-made. The effect of incorporation of Cu (5 wt.%) and Ag-Cu (1+4 wt.%) onto ZSM-5 on its particle size, unit cell parameters and crystallinity was investigated.
The deposited PAA layer acts as a common dispersing agent with its ionic COOH (COO-) groups. The antibacterial activity towards the bacterial strains such as Staphylococcus pneumonia (S. Pneumonia), Bacillus subtilis (B. subtilis), Escherichia coli (E. coli) and Pseudomonas aeruginosa (P. aeruginosa) as Gram positive and Gram negative bacteria, respectively, and Aspergillus fumigatus (A. fumigatus), Candida albicans (C. albicans) as Fungi was evaluated. The chemical and physical modifications of ZSM-5, Cu/ZSM-5 and Ag-Cu/ZSM-5 surfaces were characterized by X-ray photoelectron spectroscopy, Fourier-transform infrared spectroscopy, atomic force microscopy and X-ray diffraction.
The Cu/ZSM-5 and Ag-Cu/ZSM-5 nanocomposites coated with a 10 nm thick PAA layer exhibit significant antibacterial activity. The carboxyl (¬-COOH) or the corresponding carboxylate groups (¬-COO-) interact with Cu2+ and Ag+ ions by formation of ionic bonds (¬-COO-Ag+ or 2 ¬-COO->Cu2+). Moreover, short exposure to light and temperature has reduced Cu2+ and Ag+ to Cu0 and Ag0.